Magnezyum alaşımlara hidrofobik özellik kazandırılarak korozyon direncinin zamana bağlı incelenmesi
Time-dependent examination of corrosion resistance by featuring magnesium alloys with hydrophobic properties
- Tez No: 687170
- Danışmanlar: DR. HASAN KÖTEN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Mühendislik Bilimleri, Polimer Bilim ve Teknolojisi, Metallurgical Engineering, Engineering Sciences, Polymer Science and Technology
- Anahtar Kelimeler: AZ31B, Korozyon Direnci, Elektroforetik Kaplama, Stearik asit, Biyo implant, AZ31B, Corrosion Resistance, Electrophoretic Coating, Stearic acid, Bio implant
- Yıl: 2021
- Dil: Türkçe
- Üniversite: İstanbul Medeniyet Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Nanobilim ve Nanomühendislik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 192
Özet
Bu tez çalışmasında, AZ31B magnezyum alaşımının korozyona olan direncinin zamana karşı değerlendirilmesi yapılmıştır. AZ31B, magnezyum alaşımı korozyona olan hassasiyetinden ötürü eleforetik kaplama yöntemiyle kaplanması uygun görülmüştür. Elektroforetik kaplama yöntemiyle tek adımda, biyo uyumlu malzemelerle alaşım yüzeylerinin pratik olarak kaplanması yapılabilmektedir. Magnezyumun korozyona olan hassasiyetinin giderilmesi amacıyla, alaşım yüzeylerinin karakterizasyonu değiştirilmiştir. Alaşımların kaplanmasıyla yüzey karakterizasyonu süperhidrofobik ve hidrofobik hale getirilmiştir. Stearik asit ve magnezyum nitrat içerikli kaplama malzemeleri alaşımların, yüzey enerjisinin düşürülmesi hedeflenmiştir. Yüzey kaplaması yapılmış alaşımların, korozyona olan dirençlerinin kaplanmamış alaşım örneklerine göre yüksek olduğu gösterilmiştir. Tez çalışmasının özgün değerlerini tartışmak gerekirse, AZ31B alaşımıları ilk defa uzun süre limitinde korozif sıvılarda bekletilip kaplama sayesinde hidrofobik özelliğini koruduğu görülmüştür. Yine AZ31B alaşımı biyo implant ham malzemesi olarak kullanıldığından yine ilk defa vücut koşullarını simüle eden ortamda korozyona uğraması değerlendirilmiştir. Kaplanmış AZ31B numunelerinin yaklaşık bir ay kadar DMEM içinde stabilizasyonlarını korudukları gösterilmiştir. Kaplama örnekleri olarak alınan K.10AZ31B, K.12AZ31B alaşımlarının, süperhidrofobik yüzey karakterizasyonunda olduğu, K.8AZ31B ve K.D.10AZ31B örneklerinin hidrofobik olarak kaplandığı gösterilmiştir. Yine ilk defa bu konsantrasyonlarda AZ31B örnekleri kaplaması yapılmıştır. Kaplama örneklerinin başarıyla yapıldığı ve uzun bir müddet hem %3.5 NaCl ortamında hem de içinde antibiyotik barındıran DMEM içinde kaplamaların varlığının devam ettiği gösterilmiştir.
Özet (Çeviri)
In this thesis, the corrosion resistance of AZ31B magnesium alloy was evaluated against time. Because of its sensitivity to corrosion, AZ31B magnesium alloy was chosen to be coated with elephoretic coating method. With the electrophoretic coating method, it is possible to coat the alloy surfaces practically with biocompatible materials in one step. The characterization of the alloy surfaces has been changed in order to eliminate the susceptibility of magnesium to corrosion. Surface characterization has been made superhydrophobic and hydrophobic by coating the alloys. Stearic acid and magnesium nitart-containing coating materials are aimed to reduce the surface energy of alloys. It has been shown that the corrosion resistance of the surface coated alloys is higher than the uncoated alloy samples. To discuss the authenticity of the thesis, it was observed for the first time that AZ31B alloys were kept in corrosive liquids for a long time and preserved their hydrophobic properties thanks to the coating. Since AZ31B alloy is used as a bio implant raw material, corrosion has been evaluated for the first time in an environment simulating body conditions. Coated AZ31B samples have been shown to retain their stabilization in DMEM for approximately one month. It has been shown that K.10AZ31B, K.12AZ31B alloys taken as coating samples have superhydrophobic surface characterization, and K.8AZ31B and K.D.10AZ31B samples are hydrophobic coated. For the first time, AZ31B samples were coated at these concentrations. It has been shown that the coating samples were made successfully and the coatings continued for a long time both in 3.5% NaCl environment and in DMEM containing antibiotics.
Benzer Tezler
- Çinko esaslı antibakteriyel biyobozunur malzemelerin üretimi ve yüzey özelliklerinin mikro ark oksidasyon yöntemiyle geliştirilmesi
Production of zinc based antibacterial biodegradable materials and improvement of surface properties by the micro arc oxidation process
AYBÜKE AYDOĞAN
Yüksek Lisans
Türkçe
2020
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MURAT BAYDOĞAN
DR. ÖĞR. ÜYESİ HAKAN YILMAZER
- Synthesis of next-generation silicon/graphite anode materials via molten salt-assisted magnesiothermic reduction for lithium-ion batteries
Lityum iyon piller için erimiş tuz yardımlı magnezyotermik indirgeme yoluyla yeni nesil silisyum- grafit anot malzemelerinin sentezi
BURAK FEDAKAR
Yüksek Lisans
İngilizce
2023
Enerjiİstanbul Teknik ÜniversitesiEnerji Bilim ve Teknoloji Ana Bilim Dalı
PROF. DR. NİLGÜN YAVUZ
- AZ31 magnezyum alaşımlarına ilave edilen farklı alaşım elementlerinin korozyon özelliklerine etkisinin incelenmesi
Investigation of the effect of different alloying elements added to AZ31 magnesium alloys on corrosion properties
DİDEM KAZAN
Yüksek Lisans
Türkçe
2019
Metalurji MühendisliğiKarabük ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. YUNUS TÜREN
- Magnezyum ZWX ekstrüzyon alaşımlarının havacılık uygulamaları için geliştirilmesi
Development of magnesium ZWX extrusion alloys for aircraft applications
ÖNDER TUNA
Yüksek Lisans
Türkçe
2021
Metalurji MühendisliğiGebze Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. METİN USTA
DR. DENİZ SULTAN AYDIN
- AM60 ve AZ61 magnezyum alaşımlarının soğuma hızına bağlı mekanik ve mikroyapı özelliklerinin incelenmesi
Investigation of mechanical and microstuructural properties of AM60 and AZ61 magnesium alloys depending on cooling rate
ÖZCAN BÜYÜKGENÇ
Yüksek Lisans
Türkçe
2011
Metalurji MühendisliğiKarabük ÜniversitesiMetal Eğitimi Ana Bilim Dalı
YRD. DOÇ. DR. MEHMET ÜNAL