Improving joining performance of composites by electro-spinning of nano fibers

Nano elyafların elektro-eğirilmesi ile kompozitlerin birleşme performansının iyileştirilmesi

  1. Tez No: 705890
  2. Yazar: GÖZDE ESENOĞLU
  3. Danışmanlar: PROF. DR. METİN TANOĞLU
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2021
  8. Dil: İngilizce
  9. Üniversite: İzmir Yüksek Teknoloji Enstitüsü
  10. Enstitü: Mühendislik ve Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 79

Özet

Kompozit malzemelerde (vidalar, perçinler vb.) geleneksel olarak kullanılan mekanik mafsallar sadece ağırlığı artırmakla kalmaz, aynı zamanda stres toplayıcı olarak da hareket ederek ciddi delaminasyon sorunlarına neden olur. Aynı zamanda korozyona karşı hassaslığı, elektromanyetik özellikleri/radar absorpsiyon özellikleri, işçilik maliyetini ve imalat sürecini olumsuz etkilemesi nedeniyle alternatif birleştirme tekniklerinin geliştirilmesi kompozit sektöründe önemli bir konu haline gelmiştir. Bu yüksek lisans tezinde, poliamid 66 (PA 66) nanolifler ile kaplanmış iki farklı prepreg kompozitin (UD ve dokuma prepreg kumaşlar) birleşme bölgesi mekanik özellikleri üzerindeki etkileri araştırıldı. Ayrıca üretilen PA66 nanoliflerin lif yapıları araştırılmıştır. Üretilen nanolifler doğrudan karbon prepreglerin birleşme bölgesi katmanı (üst yüzey) üzerine kaplandı. Referans ve nanofiber katkılı prepregler sıcak pres yöntemiyle kürlendi ve ardından sıcak preste FM300K film yapıştırıcı kullanılarak ikincil bağlama yöntemiyle birleştirildi. Üretilen numuneler üzerinde çekme, basma, eğilme, kesme, charpy-darbe ve çift konsol kiriş testleri (DCB) testleri yapıldı. PA66 nanoliflerinin homojenliğinin ve alan yoğunluğunun mekanik performansa etkisi araştırıldı. Nanoliflerin morfolojisi ve test sonrası deformasyonları taramalı elektron mikroskobu (SEM) ile incelendi. PA66 nanoliflerinin termal özellikleri Diferansiyel Taramalı Kalorimetri (DSC) yöntemi ile araştırıldı. SEM görüntüleri ve bindirme kesme testi sonuçları karşılaştırılarak kompozitlerin mekanik performansı için en verimli parametreler belirlendi. Sonuçlar, ağırlıkça %10 çözelti oranı ve 10 dakikalık kaplama süresi ile üretilen PA66 nanoliflerinin kompozitler üzerinde en verimli olduğunu gösterdi. Elektro-eğirme tekniği ile bağlantı bölgesine PA66 nanofiberlerin eklenmesinin malzemelerin bağlantı bölgesi performansını arttırdığı ispatlandı ve çıktılar elde edildi.

Özet (Çeviri)

Mechanical joints traditionally used in composite materials (screws, rivets, etc.) not only increase weight but also act as a stress collector, causing serious delamination problems. At the same time, the development of alternative joining techniques has become an important issue in the composite industry due to its sensitivity to corrosion, electromagnetic properties/radar absorption properties, labor cost and adverse effects on the manufacturing process. In this master's thesis, the effects on the mechanical properties of two different prepreg composites (UD and woven) coated with polyamide 66 (PA 66) nanofibers in the joint region were investigated. In addition, the fiber structures of the produced PA66 nanofibers were investigated. The produced nanofibers were directly coated on the bond zone layer (top surface) of the carbon prepregs. The reference and nanofiber doped prepregs were cured by the hot press method, and then they were combined with the secondary bonding method using FM300K film adhesive in the hot press. Tensile, compression, bending, shear, Charpy-impact and double cantilever beam (DCB) tests were performed on the produced samples. The effect of homogeneity and areal weight density (AWD) of PA66 nanofibers on mechanical performance was investigated. The morphology and post-test deformations of the nanofibers were investigated by scanning electron microscopy (SEM). The thermal properties of PA66 nanofibers were investigated by the differential scanning calorimetry (DSC) method. By comparing the SEM images and the lap shear test results, the most efficient parameters for the mechanical performance of the composites were determined. The results showed that PA66 nanofibers produced with a 10% wt solution ratio and 10 min coating time were the most efficient on composites. The addition of PA66 nanofibers to the junction region with the electro-spinning technique has been proven to increase the junction region performance of the materials and outputs have been obtained.

Benzer Tezler

  1. Improving the joining performance of carbon fiber/PEEK based thermoplastic composites with laser surface treatment

    Karbon fiber/ PEEK esaslı termoplastik kompozitlerin birleşim performansının lazer yüzey işlem ile artırılması

    CEREN TÜRKDOĞAN DAMAR

    Doktora

    İngilizce

    İngilizce

    2024

    Makine Mühendisliğiİzmir Yüksek Teknoloji Enstitüsü

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. METİN TANOĞLU

  2. Manufacturing, mechanical behavior and failure analysis of ultrasonic welded carbon fiber reinforced thermoplastic composites

    Başlık çevirisi yok

    UMUT ÖZKAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2020

    Makine MühendisliğiÖzyeğin Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. GÜNEY GÜVEN YAPICI

  3. Karbon kompozit ile alüminyum alaşımını yapıştırmada mekanik kilitleme sağlamak için lazerle yüzey işleme prosesi optimizasyonu

    Optimization of laser surface treatment process to provide mechanical locking in aluminum alloy adhesive bonding with carbon composite

    SEDA AYBALIK

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Havacılık MühendisliğiKocaeli Üniversitesi

    Havacılık Bilimi ve Teknolojileri Ana Bilim Dalı

    DOÇ. DR. ONUR ÇOBAN

  4. Metal yüzey bağlantılarında kullanılan yapıştırıcıların performansına fenolik reçinenin etkisinin incelenmesi

    Investigation of the effect of phenolic resin on the performance of adhesives used in metal-metal bonding

    SALİHA SÖKEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Metalurji MühendisliğiNecmettin Erbakan Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. YASİN RAMAZAN EKER

    DR. ÖĞR. ÜYESİ HAKAN BURAK KARADAĞ

  5. Fastening solutions for composite structures

    Kompozit yapılar için bağlantı çözümleri

    EMRE ERBİL

    Doktora

    İngilizce

    İngilizce

    2023

    Makine MühendisliğiDokuz Eylül Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. RAMAZAN KARAKUZU