Karbon türevi ve doğal bitki ekstratı katkılı yapıştırma simanlarının antibakteriyel ve bazı fiziksel özelliklerinin incelenmesi
Investigation of antibacterial and some physical properties of luting cements with carbon derivatives and natural plant extracts
- Tez No: 716414
- Danışmanlar: PROF. DR. SERHAT SÜHA TÜRKASLAN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Süleyman Demirel Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 99
Özet
Amaç: Bu çalışmanın amacı grafen oksit ve oleuropein ilave edilmesi ile dental yapıştırma simanlarının (polikarboksilat siman, cam iyonomer siman, dual-cure siman, kompozit rezin siman) antibakteriyel özelliklerinin geliştirilmesi ve bu sırada fiziksel özelliklerindeki değişimin incelenmesidir. Malzemeler ve Yöntemler: Grafen oksit, flake yapıdaki grafitten Hummers metodu ile sentezlendi. Oleuropein ve grafen oksit, geleneksel simanların toz kısmına ve polimer içerikli simanların toplam içeriğine belirli oranda (ağırlıkça %1) ilave edildi ve mekanik olarak karıştırılarak deneysel olarak modifiye edilmiş yapıştırma simanları hazırlandı. Her bir kontrol ve deney grubu örneklerinin E. Faecalis'e karşı antibakteriyel etkisi Direkt Kontak Test yöntemi ile belirlendi. Materyaller, mikrotitre kuyucuklarına uygulandıktan hemen sonra test edildi. Hayatta kalan bakterilerin büyümesini belirlemek için 10 kat seri dilüsyonlar yapıldı ve her bir dilüsyondan 10 μl alınarak 1., 6. ve 24. saatlerde BHI agar katı besiyerlerine damlatma tekniği ile ekimler yapıldı. Sayılabilir dilüsyonlardaki bakteri sayısı dilüsyon katsayısı ile çarpılarak mililitredeki“colony forming units”(CFU/ ml) sayısı bulundu. Tüm numunelerin Vickers mikrosertliği, Vickers mikrosertlik test cihazı ile ölçülmüştür. Tüm numunelerin Taramalı Elektron Mikroskobu (SEM) ile yüzey gözenekliliği değerlendirildi. Grafen oksitin karakterizasyonu X-Işını Kırınım Yöntemi (XRD) ile yapıldı. Sonuçlar: Kontrol grubuna kıyasla deney grubu numunelerine ait besiyerlerinde daha az sayıda bakteri kolonisi tespit edildi. Oleuropein ilavesi ile polikarboksilat siman ve polimer içerikli simanların sertlik değerlerinde azalma görülürken, cam iyonomer simanda anlamlı bir fark bulunamadı. Grafen oksit ilavesi ile cam iyonomer siman ve kompozit rezin simanın sertlik değerlerinde artış görülürken, polikarboksilat siman ve dual cure simanda anlamlı bir fark bulunamadı.
Özet (Çeviri)
Aim: The aim of this study is to improve the antibacterial properties and investigate the changes in some physical properties of dental luting cements (polycarboxylate cement, glass ionomer cement, dual-cure cement, composite resin cement) by adding graphene oxide and oleuropein. Materials and Methods: Graphene oxide was synthesized from flake graphite by Hummers method. Oleuropein and graphene oxide were added to the powder part of conventional cements and to the total content of polymer-containing cements at a certain rate (1% by weight) and modified luting cements were prepared by mechanical mixing. The antibacterial effect of each control and experimental group samples against E. faecalis was determined by the Direct Contact Test method. Materials were tested immediately after application to microtiter wells. To determine the growth of surviving bacteria, 10-fold serial dilutions were made and 10 μl of each dilution was taken and cultivated on BHI agar solid media at 1, 6 and 24 hours by drip technique. The number of bacteria in countable dilutions was multiplied by the dilution coefficient to find the number of colony forming units (CFU/ml) per milliliter. The Vickers microhardness of all samples was measured with Vickers microhardness tester. Surface porosity of all samples was evaluated by Scanning Electron Microscopy (SEM). Graphene oxide was characterized by X-Ray Diffraction Method (XRD). Results: Fewer bacterial colonies were detected in the media of the experimental group compared to the control group. While the Vickers microhardness values of polycarboxylate cement and polymer-containing cements decreased with the addition of oleuropein, no meaningful difference was found in glass ionomer cement. While the Vickers microhardness values of glass ionomer cement and composite resin cement increased in with the addition of graphene oxide, no meaningful difference was found in polycarboxylate cement and dual cure cement.
Benzer Tezler
- Novel biopolymer applications as adsorbent, drug encapsulation and controlled drug release agents
Adsorban, ilaç kapsülleme ve kontrollü ilaç salımı ajanları olarak yeni biyopolimer uygulamaları
NİLAY KAHYA
Doktora
İngilizce
2023
Kimyaİstanbul Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. FATMA BEDİA BERKER
- p-hidroksibenzil tiyosteroid eter sentezi
Synthesis of p-hydroxybenzyl thiosteroid ether
AYŞE MUŞTU SİRKECİOĞLU
- Doğu Karadeniz bölgesinde yayılış gösteren bazı Betula spp. endofitlerinin betülin biyotransformasyon ve tirozinaz inhibisyon kapasitelerinin araştırılması
Investigation of betulin biotransformation and tyrosinase inhibition capabilities of some Betula spp. endophytes distributed across the Eastern Black Sea region
PELİN GÖKFİLİZ YILDIZ
- Yapay ve doğal lifli malzemeler ile güçlendirilmiş beton yapı elemanlarının incelenmesi
Investigation of concrete structural elements reinforced with artificial and natural fibrous materials
YUSUF KENAN AKÇAAT
Yüksek Lisans
Türkçe
2022
İnşaat MühendisliğiFırat Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SEDAT SAVAŞ
- Citric acid and dimer diol-based polyester membranes for food packaging applications
Gıda paketleme uygulamaları için sitrik asit ve dimer diol bazlı polyester membranlar
SARA AGHAEINEJAD AJBISHEH
Yüksek Lisans
İngilizce
2023
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. BİHTER ZEYTUNCU GÖKOĞLU
PROF. DR. EMRAH ÇAKMAKÇI