Farklı yaşlandırma sürelerinin zirkonya seramiklerin eğilme dayanımına etkisi
Evaluation of different aging times on flexural strength of zirconia ceramics
- Tez No: 728728
- Danışmanlar: DR. ÖĞR. ÜYESİ ESRA TALAY ÇEVLİK, DOÇ. DR. DUYGU KÜRKLÜ ARPAÇAY
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental porselen, Dental stres analizi, Yapay yaşlandırma, Yaşlandırma, Zirkonyum, Zirkonyum oksit, Dental porcelain, Dental stress analysis, Artificial aging, Ageing, Zirconium, Zirconium oxide
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Aydın Adnan Menderes Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, farklı miktarda yttria içeriğine sahip Y-TZP seramiklerin farklı kalınlıklara sahip alt gruplarının 1 saat ve 5 saat yapay yaşlandırma sürecinin eğilme dayanımına etkisinin incelenmesidir. Gereç ve Yöntem: Toplamda 300 adet disk şeklindeki örnek final boyutları 12 mm çap, 0.8 mm ve 1.5 mm kalınlık olmak üzere, DD Bio ZX2 Color, DD Cube One ML, DD Cube X2 ML, IPS e. max ZirCAD Prime ve IPS e. max ZirCAD MT Multi materyallerinden üretildi. Kontrol grupları işleme tabi tutulmazken, deney grupları ISO 13356 standardına göre otoklavda 134 °C, 2 bar basınçta, 1 saat ve 5 saat yaşlandırıldı. Yaşlandırma sonrası SEM ve XRD analizi yapıldı. Biaksiyal eğme testi ile örneklerin eğilme dayanımları incelendi. Çalışmadan elde edilen veriler, Shapiro-Wilk, Levene testi, Varyans Analizi ve Bonferroni testi kullanılarak istatiksel olarak değerlendirildi. Bulgular: Materyallerin ortalama eğilme dayanımı değerleri sırasıyla; DD Bio ZX2 Color, IPS e. max ZirCAD Prime ve DD Cube One ML, IPS e. max ZirCAD MT Multi ve DD Cube X2 ML' dir. IPS e. max ZirCAD Prime ve IPS e. max ZirCAD MT Multi materyallerinde kalınlık artışıyla eğilme dayanımlarında artış gözlendi. Yaşlandırma süresinin artmasıyla DD Bio ZX2 Color materyalinin eğilme dayanımında artış gözlenirken, diğer materyallerin ED değerlerinde anlamlı fark görülmedi. Yaşlanmayla beraber SEM analizinde yüzey bozunmalarında artış izlendi. Sonuçlar: Farklı miktarda yttria içeriğine sahip materyallerin eğilme dayanımlarında istatistiksel fark vardır. Yaşlandırma sürelerinin ve materyal kalınlıklarının Y-TZP seramiklerin eğilme dayanımına etkisi bulunmaktadır.
Özet (Çeviri)
Objective: The purpose of this study was to investigate the effect of 1 hour and 5 hours artificial aging process on flexural strength of Y-TZP ceramics with different thickness and different amount of yttria content. Materials and Methods: A total of 300 disc-shaped specimens; DD Bio ZX2 Color, DD Cube One ML, DD Cube X2 ML, IPS e. max ZirCAD Prime and IPS e. max ZirCAD MT Multi were produced as final dimentions 12 mm diameter, 0.8 and 1.5 mm thickness. According to ISO 13356 standards, experimental groups were artificially aged at 134 °C, under 2 bar pressure, for 1 hour and 5 hours at autoclave. Control groups were not subjected to any treatment. SEM and XRD analysis were performed. The effect of aging on flexural strength was investigated by biaxial bending test. Datas were analyzed using the Shapiro-Wilk, Levene test, Analysis of Variance and Bonferroni test. Results: The mean flexural strength (FS) values of the materials are DD Bio ZX2 Color, IPS e. max ZirCAD Prime and DD Cube One ML, IPS e. max ZirCAD MT Multi and DD Cube X2 ML respectively. The flexural strengths of IPS e. max ZirCAD Prime and IPS e. max ZirCAD MT Multi materials increased with a increase in the thickness. Flexural strength of DD Bio ZX2 Color was increased with aging time, no significant difference was observed in the FS values of other materials. SEM investigation revealed that with increasing aging time, the surface degradation increased. Conclusions: Significant differences were observed in the flexural strengths of materials with different amounts of yttria content. Aging times and material thickness have an effect on the flexural strength of Y-TZP ceramics.
Benzer Tezler
- Farklı yapay yaşlandırma sürelerinin 6XXX serisi alüminyum alaşımlarının mekanik özelliklerine etkisi
The effect of different artificial aging times on the mechanical properties of 6XXX series aluminum alloys
ÇAĞATAY KIRSAVAŞ
Yüksek Lisans
Türkçe
2021
Makine MühendisliğiTekirdağ Namık Kemal ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ İBRAHİM SAVAŞ DALMIŞ
- Kompozit tamirinde farklı yüzey hazırlama yöntemlerinin ve yaşlandırma sürelerinin bağlanma dayanıklılığına etkisi
The effect of different surface preparation methods and various aging periods on bond strength for composite repair
MELTEM NERMİN DURSUN
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiHacettepe ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ESRA ERGİN
- Kompozit restorasyonların tamirinde farklı yüzey hazırlama yöntemlerinin ve yaşlandırma sürelerinin mikro makaslama bağlanma dayanımına etkisi
The effect of different surface pretreatment methods and thermal aging durations on repair micro-shear bond strength of composite resin restorations
AYŞENUR ALTUĞ YILDIRIM
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiGazi ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. MİNE BETÜL ÜÇTAŞLI
- Üç boyutlu yazıcı ile üretilen kalıcı kuron restorasyonların tamirinde farklı yaşlandırma sürelerinin bağlanma dayanımına etkisi
The effect of different aging periods on bond strength in the repair of permanent crown restorations fabricated by three-dimensional printing
MERVE YILMAZ
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiOndokuz Mayıs ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. NİHAN GÖNÜLOL
- Farklı yaşlandırma sürelerine maruz bırakılan rezin kompozit yüzeylerine farklı tedavi protokollerinin uygulanmasının bağlanma dayanımına etkisi
The effect of applying different treatment protocols on resin composite surfaces exposed to different aging times on bond strength
ZUHAL ÇALIŞKAN
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiGazi ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. OYA BALA