Standart başlıklama yöntemlerinin farklı ortamlarda kür edilmiş silindir beton örneklerin basınç dayanımı ve kırılma biçimleri üzerindeki etkilerinin karşılaştırılması

Comparison of the effects of standard capping methods on the compressive strength and fracture forms of cylinder concrete samples cured in different environments

PDF İndir

  1. Tez No: 738910
  2. Yazar: HAMZA ÇİNAR
  3. Danışmanlar: PROF. DR. REMZİ ŞAHİN
  4. Tez Türü: Yüksek Lisans
  5. Konular: İnşaat Mühendisliği, Civil Engineering
  6. Anahtar Kelimeler: beton, başlıklama yöntemi, kür koşulu, basınç dayanımı, TS EN 12390-3, kırılma biçimi, concrete, capping, curing condition, compressive strength, TS EN 12390-3, failure pattern
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: Atatürk Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 132

Özet

Amaç: TS EN 12390-3 (2019)'da önerilen dört başlıklama yöntemi ile uygulamada sıkça başvurulan iki yöntemin farklı koşullarda saklanan beton silindir örneklerin basınç dayanımları üzerindeki etkilerini mukayeseli olarak incelemektir. Yöntem: Aynı karışım hesabına sahip betonlar üretildi. Başlıklama çeşidi olarak öğütme (G), kalsiyum alüminatlı çimento harcı (CM), kükürt + silis kumu (SSM), kum kutusu (SB), kükürt (S) ve kesme (C) yöntemleri seçildi. Kür ortamları ise hava kürü, nem kürü, deney başlangıcından 24 saat önce (su kürü I) ve 10 saatten kısa (su kürü II) sürede numuneyi su kürü havuzundan çıkarma olarak belirlendi. Her bir kür koşulu için 14 adet silindir (Ø100×200 mm) ve 2 adet küp (150×150×150 mm) numune üretildi. Birim ağırlık, çökme, eksenel basınç ve ultrases geçiş hızı (UPV) deneyleri yapıldı. Başlıklama malzemelerinin dayanım gelişimleri belirlendi ve numunelerin kırılma biçimleri gözlendi. Öğütme işlemi, zımpara makinesi kullanılarak el ile (manuel öğütme) yapıldı. Bulgular: Başlıklama malzemesinin dayanımı en yüksek (35 MPa) olan SSM, başlıklama süresi en kısa (7-8 dk.) olanlar ise C, S ve SSM'dir. Havada kür edilenlere oranla nem, su kürü I ve su kürü II'de kür edilmiş betonların UPV değerleri, sırasıyla, %10,2, %12,7 ve %18,8 oranlarında artmıştır. Başlıklamadan sonra UPV değerleri genelde artmıştır. En fazla (%100) UPV artışı havada kür edilmiş örneklerin S ile başlıklanması sonucu elde edilmiştir. Başlıksız betonların dayanımına oranla tüm kür ortamlarında, manuel öğütme hariç, başlıklama işlemi örneklerin dayanımlarını arttırmıştır. En yüksek dayanım artışı nem küründe görülmüştür. SB yöntemi ile başlıklanan silindirlerin %50'sinin kırılma biçimi tatmin edici iken diğer başlıklama yöntemlerinin kırılma biçimleri genelde tatmin edici değildi. Sonuç: Manuel öğütmenin basınç dayanımlarını genelde düşürdüğü belirlendiğinden özel otomatik öğütme cihazları ile betonların aşındırılması önerildi. Numunelerin kırılma biçimi üzerinde başlık şeklinin önemli etkisinin olduğu gözlemlendi. Başlıklama performansı en yüksek SB, sonra C bulundu. Bulgular, araştırma hipotezini doğruladı.

Özet (Çeviri)

Purpose: The aim is to compare the effects of the four capping methods recommended in TS EN 12390-3 (2019) and the two methods frequently used in construction practice on the compressive strength of concrete cylinder samples stored in different curing conditions. Method: Concretes with the same mix design were produced. Grinding (G), calcium aluminate cement mortar (CM), sulfur + silica sand (SSM), sandbox (SB), sulfur (S) and cutting (C) methods were selected as the capping. Curing conditions were determined as air curing, moisture curing, removing the sample from the water curing 24 hours before the start of the experiment (water cure I) and less than 10 hours (water cure II). For each curing condition, 14 cylinders (Ø100×200 mm) and 2 cubes (150×150×150 mm) samples were produced. Unit weight, slump, axial compression and ultrasound pulse velocity (UPV) tests were performed. The strength developments of the capping materials were determined and the failures patterns of the samples were observed. G was done manually (manual grinding) using a sanding machine. Findings: The capping material of SSM had the highest compressive strength (35 MPa). Those with the shortest capping time (7-8 min.) were C, S and SSM. Compared to those cured in air, the UPV values of concretes cured to moisture, water cure I and water cure II increased by 10.2%, 12.7% and 18.8%, respectively. UPV values generally increased after capping. The maximum (100%) UPV increase was obtained by capping the air-cured samples with S. Compared to the strength of uncapped concrete, capping increased the strength of the samples in all curing conditions, except for manual grinding. The highest increase in strength was observed in the moisture cure. While 50% of the cylinders capped with the SB were satisfactory, the failure patterns of the samples with other capping methods were generally unsatisfactory. Results: Since it was determined that manual grinding generally reduces the compressive strength, it was recommended to grind the concrete with automatic grinding devices. It was observed that the type of the capping had a significant effect on the failure pattern of the samples. The capping performance was the highest SB, then C. The findings confirmed the research hypothesis.

Benzer Tezler

  1. Tez No

    511343

    Invitational leadership practices at a school of foreign languages from a gendered perspective: A case study

    Bir yabancı diller yüksek okulundaki katılımcı liderlik uygulamalarının toplumsal cinsiyet çerçevesinde incelenmesi: Bir durum çalışması

    ZÜBEYDE DURNA

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Eğitim ve ÖğretimOrta Doğu Teknik Üniversitesi

    Kadın Çalışmaları Ana Bilim Dalı

    PROF. DR. GÖLGE SEFEROĞLU

  2. Tez No

    467085

    Virtual and augmented reality based interfaces for choreography generation

    Koregrafi üretimi için sanal ve artırılmış gerçeklik tabanlı arayüzler

    TAFADZWA JOSEPH DUBE

    Yüksek Lisans

    İngilizce

    İngilizce

    2017

    Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve Kontrolİstanbul Teknik Üniversitesi

    Bilgisayar ve Bilişim Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. GÖKHAN İNCE

  3. Tez No

    848274

    MODELLING AND ESTIMATION OF SHIP MOTIONS

    GEMİ HAREKETLERİNİN MODELLENMESİ VE TAHMİNİ

    ALPER ZİHNİOĞLU

    Doktora

    İngilizce

    İngilizce

    2023

    Gemi Mühendisliğiİstanbul Teknik Üniversitesi

    Gemi İnşaatı ve Gemi Makineleri Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ MELEK ERTOGAN

  4. Tez No

    556205

    Ağrı kesici yüklü pektin temelli transdermal yama tasarımı

    Transdermal painkiller delivery with pectin based patches

    AYBÜKE TAVASLI

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Mühendislik Bilimleriİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. FATMA SENİHA GÜNER

  5. Tez No

    183999

    Çok doymamış yağ asitleri bakımından zengin alg ilave edilen yemlerin levrek (Dicentrarchus albrax L., 1758)'de büyüme performansı ve vücut komposizyonuna etkisi

    Effects of pufa (Polyunsaturated fatty acids) enriched algae added diets on growth and body composition of sea bass (Dicentrarchus labrax L., 1758)

    KAMİL MERT ERYALÇIN

    Yüksek Lisans

    Türkçe

    Türkçe

    2006

    Su Ürünleriİstanbul Üniversitesi

    Su Ürünleri Yetiştiriciliği Ana Bilim Dalı

    PROF. DR. ERDAL ŞENER

Geri Dön