Yüksek sıcaklık endüstriyel tekerlek uygulamaları için polimer esaslı kompozit malzeme geliştirilmesi ve özelliklerinin incelenmesi

Investigation and development of polymer-based composite material properties for high temperature industrial wheel applications

PDF İndir

  1. Tez No: 745340
  2. Yazar: MÜCAHİT KOCAMAN
  3. Danışmanlar: PROF. DR. HAMDULLAH ÇUVALCI
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: Karadeniz Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Malzeme Bilim Dalı
  13. Sayfa Sayısı: 110

Özet

Bu çalışmada cam elyaf ve grafit katkı oranlarının novalak esaslı fenolik reçine ile birlikte olan etkileri incelendi. Üretilen malzemelerin termal bozunma ve yanma dirençlerinin yanısıra fiziksel ve mekanik özellikleri de incelemeye alınmıştır. Ayrıca novalak matriste cam elyaf ve grafit partiküllerinin beraberce olan etkisi incelendi. Üretilen kompozit numunelerin karakterizasyonu sürecinde; fiziksel özelliklerin belirlenmesi için porozite ve yoğunluk (Arşimet yöntemi), mekanik özelliklerinin belirlenmesi için sertlik, çekme ve üç nokta eğilme testleri, termal özelliklerin belirlenmesi için termogravimetrik analiz (TGA), matris ve katkı parçacıklarının morfolojisi, hibrit kompozit tozların mikro yapısı ve kırılma yüzeylerinin karakterizasyonunda taramalı elektron mikroskobu (SEM-EDS), alev geciktiricilik özelliklerinin belirlenmesi için ise limit oksijen indisi (LOI) testleri uygulandı. Elde edilen termogravimetrik verilere göre novalak reçineye ilave edilen cam elyaf ve grafit partikülleri sayesinde bozunan kütle miktarı azalırken bozunma sıcaklıklarının arttığı gözlendi. Saf novalak malzemesinin sertlik, maksimum çekme ve eğilme mukavemeti sırasıyla 32 HRM, 12 MPa ve 20.3 MPa iken, optimum kompozit numunede(%30 cam elyaf, %40 grafit) 98 HRM, 33.8 MPa ve 77.4 MPa olarak tespit edildi. Saf novalak malzemesinin LOI değeri ise %37 iken, üretilen kompozit malzemeler arasında >%50'ye kadar bir artış ile yüksek alev geciktiricilik tespit edilmiştir.

Özet (Çeviri)

In this study, the effects of glass fiber and graphite additive rates on novalac based phenolic resin were investigated. The physical and mechanical properties of the produced materials, as well as their thermal decomposition and combustion resistance, were also examined. In addition, the effect of the combined effect of glass fiber and graphite particles in the novolac matrix was investigated. Samples containing glass fiber and graphite in different rates will be prepared. In the characterization process of the produced composite samples; porosity and density(Archimedes' method) to determine of physical properties, hardness, tensile and flexural tests to determine of mechanical properties, thermogravimetric analysis (TGA) to determine thermal properties, scanning electron microscopy (SEM-EDS) for morphology of matrix and additive particles, microstructure of hybrid composite powders characterization of fracture surfaces, and limit oxygen index (LOI) tests to determine flame retardance properties were applied. According to the obtained thermogravimetric datas, it was observed that the decomposition temperature increased while the amount of decomposed mass decreased thanks to the glass fiber and graphite particles added to the novolac resin. While the hardness, maximum tensile and flexural strengths of pure novalac material were 32 HRM, 12 Mpa and 20.3 Mpa, respectively, the optimum composite sample (30% glass fiber, 40% graphite) was determined as 98 HRM, 33.8 Mpa and 77.4 Mpa. While the LOI value of the pure novalak material was 37%, high flame retardancy was determined with an increase of up to >50% among the composite materials produced.

Benzer Tezler

  1. Tez No

    455424

    Slip-slide control system for railway vehicles

    Demiryolu araçları için kayma-kızaklama kontrol sistemi

    ÖNCÜ ARARAT

    Doktora

    İngilizce

    İngilizce

    2017

    Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve Kontrolİstanbul Teknik Üniversitesi

    Kontrol ve Otomasyon Mühendisliği Ana Bilim Dalı

    PROF. DR. MEHMET TURAN SÖYLEMEZ

  2. Tez No

    788466

    Evaluation of the effect of crumb rubber asphalt modification variables on the asphalt binder performance

    Kauçuk modifiye asfalt modifikasyon değişkenlerinin asfalt performansı üzerindeki etkisinin belirlenmesi

    MEHMET ÖZÇİLOĞLU

    Yüksek Lisans

    İngilizce

    İngilizce

    2023

    İnşaat MühendisliğiOrta Doğu Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. HANDE IŞIK ÖZTÜRK

  3. Tez No

    467228

    A numerical analysis of friction-induced noise in stick-slip friction

    Tutma-bırakma sürtünmesi kaynaklı gürültünün sayısal olarak incelenmesi

    SHAHRAD SAMANKAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2017

    Makine Mühendisliğiİstanbul Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. ATAKAN ALTINKAYNAK

  4. Tez No

    439497

    Design and production of benchtop x-ray imaging system

    Masaüstü x-ışını görüntüleme sisteminin dizaynı ve üretimi

    MEHMET ERHAN EMİRHAN

    Doktora

    İngilizce

    İngilizce

    2016

    Fizik ve Fizik Mühendisliğiİstanbul Teknik Üniversitesi

    Fizik Mühendisliği Ana Bilim Dalı

    PROF. DR. CENAP ŞAHABETTİN ÖZBEN

  5. Tez No

    510832

    Effects of particle granulation optimisation and new binder development on properties of alumina based castable refractories

    Tane boyut dağılımı optimizasyonunun ve yeni bağlayıcı geliştirilmesinin alümina esaslı dökülebilir refrakterlerin özelliklerine etkileri

    MELİS OKTAY

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ÖMER SERDAR ÖZGEN

Geri Dön