Karbon türevi nano katkıların poliüretan üzerindeki etkilerinin incelenmesi
Investigation of the effects of carbon derivative nano additives on polyurethane
- Tez No: 755217
- Danışmanlar: PROF. DR. METİN USTA
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Mühendislik Bilimleri, Polimer Bilim ve Teknolojisi, Chemistry, Engineering Sciences, Polymer Science and Technology
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Gebze Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 107
Özet
Bu çalışmada elastomerik özellikler gösteren termoset poliüretan polimer matriks malzemesine son dönem trendi olan karbon türevi nano katkılar eklenmiştir. Bu katkılar çok çeşitli olmasına karşılık yaptığımız çalışmada grafen, karbon nanotüp ve kırpılmış karbon fiberler seçilmiştir. Bu katkıların yüksek oranlarda takviye edildiği polimerlerde elektriksel özelliklerde artış gözlendiği bilinmektedir fakat çalışmamızda karbon katkıların oranlarını olabildiğince düşük tutarak karışımlar hazırlanmıştır. Farklı tip karıştırıcılarda yapılan bu denemelerin sonucunda en verimli karıştırma sisteminin ultrasonik karıştırıcı olduğu fakat yüksek kayma kuvvetli karıştırıcılar ile de gayet yüksek performans elde edildiği saptanmıştır. Bu teknikler kullanılarak numuneler üretilmiştir. Üretilen numunelere çeşitli termal ve mekanik deneyler yapılarak sonuçlar incelenmiştir. Böylece düşük miktarda nano karbon eklenerek termal ve mekanik özellikleri iyileştirilmiş elastomerik termoset poliüretan malzeme geliştirilmiştir. Mekanik özelliklerde en dayanıklı ürünler çok duvarlı karbon nano tüp takviyesinde özellikle yırtılma deneyinde %0,025 MWCNT katkısında elde edilmiş, camsı geçiş sıcaklığının geliştirilmesinde yüksek kayma kuvvetli karıştırıcı ile birlikte %0,05 grafen katkısı sağlamıştır, akustik performans deneyleri incelendiğinde %0,025 CNT ve grafen katkısının özellikle yalıtım teknolojisinde iyi sonuçlar verebileceği, aşınma olan alanlarda ise %0,05 karbon fiber katkısının saf poliüretana nazaran açık ara çok daha dayanıklı olduğu bu tez kapsamında yapılan çalışmalarla gösterilmiştir.
Özet (Çeviri)
In this study, carbon-derived nano additives, which is a recent trend, were added to the thermoset polyurethane polymer matrix material with elastomeric properties. Although these additives are very diverse, graphene, carbon nanotube and chopped carbon fibers were selected in our study. It is known that an increase in electrical properties is observed in polymers in which these additives are reinforced at high rates, but in our study, mixtures were prepared by keeping the proportions of carbon additives as low as possible. As a result of these trials with different types of mixers, it was determined that the most efficient mixing system was the ultrasonic mixer, but very high performance was obtained with mixers with high shear force. Samples were produced using these techniques. Various thermal and mechanical experiments were performed on the produced samples and the results were examined. Thus, an elastomeric thermoset polyurethane material with improved thermal and mechanical properties by adding a low amount of nano carbon was developed. The most durable products in mechanical properties were obtained with the addition of 0.025% MWCNT in the multi-walled carbon nano tube reinforcement, especially in the tear test, and the contribution of 0.05% graphene together with the high shear strength mixer in the development of the glass transition temperature. It has been shown by the studies carried out within the scope of this thesis that it can give good results in insulation technology, and that the 0.05% carbon fiber additive in areas with abrasion is much more durable than pure polyurethane.
Benzer Tezler
- Karbon katkılı iletken polimer kompozitlerin üretimi, karakterizasyonu ve elektromanyetik dalga kalkanlamada kullanımlarının değerlendirilmesi
Production, characterization and evaluation of their usage in electromagnetic interference shielding of carbon reinforced conductive polymer composites
BEDRİYE ÜÇPINAR DURMAZ
Doktora
Türkçe
2023
Kimya MühendisliğiKocaeli ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. AYŞE AYTAÇ
- Synthesis of poly (Methyl methacrylate) reinforced by multi-walled carbon nanotubes and magnetite nanofillers
Mwcnt ve magnetit nanodolgular ile güçlendirilmiş poli (Metil metakrilat) sentezi
ECEM ERMAN
Yüksek Lisans
İngilizce
2022
Mühendislik Bilimleriİstanbul Teknik ÜniversitesiNanobilim ve Nanomühendislik Ana Bilim Dalı
PROF. DR. NİLGÜN BAYDOĞAN
- Effect of polylactide molecular weight on cellulose nanocrystal dispersion quality
Polilaktitin molekül ağırlığının selüloz nanokristal dağılım kalitesine etkisi
ANIL DÜNDAR
Yüksek Lisans
İngilizce
2022
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
DOÇ. DR. MOHAMMADREZA NOFAR
- Preparation and characterization of nanofibers for energy applications
Enerji uygulamaları için nanofiberlerin hazırlanması ve karakterizasyonu
GÖKTUĞ CİHANBEYOĞLU
Yüksek Lisans
İngilizce
2023
Enerjiİstanbul Teknik ÜniversitesiNanobilim ve Nanomühendislik Ana Bilim Dalı
DOÇ. DR. MELTEM YANILMAZ
- Elektrot malzemesi olarak balık pulundan karbon sentezi ve karakterizasyonu
Carbon synthesis and characterization from fish scale as electrode material
CANSU BODUR
Yüksek Lisans
Türkçe
2022
Kimya MühendisliğiOndokuz Mayıs ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. BERKER FIÇICILAR