Determination of the hydrogen content in the weld metal after welding with a basic covered electrode

Bazik bir elektrotla yapılan kaynak sonucunda kaynak metaline yayınabilir hidrojen miktarının tayini

  1. Tez No: 75954
  2. Yazar: AYKUT KIRBAŞ
  3. Danışmanlar: PROF. DR. ALPAY ANKARA
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Yayınabilir Hidrojen Miktarı, Kaynak, Bazik Örtülü Elektrod vı, Diffusible hydrogen content, Welding, Basic covered electrode IV
  7. Yıl: 1998
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 119

Özet

öz BAZİK BİR ELEKTRODLA YAPILAN KAYNAK SONUCUNDA KAYNAK METALİNE YAYINABİLİR HİDROJEN MİKTARININ TAYİNİ KIRBAŞ, Aykut Yüksek Lisans, Metalürji ve Malzeme Mühendisliği Bölümü Tez Yöneticisi: Prof Dr.Alpay ANKARA Eylül 1998, 105 sayfa Bu tez ASB 255 (TS 563 E 51 55 B 10 120 H) bazik örtülü elektrodla yapılan kaynak sonucunda kaynak metaline yayınabilir hidrojen miktarının civa yer değiştirme metodu ile hesaplanması üzerinedir. Bazik elektrodlarlarla yapılan kaynak sonucunda kaynak metaline yayınabilir hidrojen miktarının bilinmesi önem taşır. Bu araştırmada AS KAYNAK firmasının ürettiği AS B 255 (TS 563 E 51 55 BIO 120H) bazik elektrodla çalışılmaktadır. İlk önce elektrodlar 40°C ve 90% nem ihtiva eden birodada nemlendirilir. Daha sonra 150°C'den 400°C'ye kadar sıcaklığı 50°C artırarak, sırasıyla ilk önce bir saat daha sonra ise iki saat kurutulur. Kurutulan elektrodla 10 cm'lik bir kaynak yapılır. Kaynaklanan numune ilk önce buzlu suya, sonrada sıvı azotun içine atılarak soğutulur. Soğutulan numune temizlendikten sonra hidrojen tayin cihazının içine konur ve burada 72 saat bekletilir. 72 saat sonunda cihazdan okunan değer kaynak metaline yayınabilir hidrojen miktarına eşittir. Bu değer standard sıcaklık ve basınçta 100 g kaynak metaline yayınabilir hidrojen miktarına dönüştürülür. Bu prosedür tekrarlanarak 150°C'den 400°C'ye kadar okunan değerler bir grafiğe taşınır. (Yayınabilir hidrojen miktarı - Kurutma sıcaklığı) Bu grafik sayesinde elektrod kullanıcısı elektrodu hangi sıcaklıkta ve ne kadar ısıtacağına karar vererek, kaynak metaline yayınabilir hidrojen miktarına karar verebilir.

Özet (Çeviri)

ABSTRACT DETERMINATION OF THE HYDROGEN CONTENT IN THE WELD METAL AFTER WELDING WITH A BASIC COVERED ELECTRODE KIRBAŞ, Aykut M. S., Department of Metallurgical and Materials Engineering Supervisor: Prof.Dr. Alpay ANKARA September 1998, 105 pages This thesis is on the determination of the diffusible hydrogen content in the weld metal after welding with a basic covered electrode AS B 255 (TS 563 E 51 55 B 10 120 H) by the mercury displacement method. It is important to know the amount of diffusible hydrogen content in the weld metal after welding with basic covered electrodes.The present work is concerned with AS B 255 basic covered electrode produced by AS KAYNAK. First of all the electrodes are humidified in a climatic chamber of 40°C and 90% mhumidity. Then the electrodes are dried at 150°C for one hour and after for two hours. The procedure is repeated by increasing the temperature up to 400°C by an increase of 50°C in each step. After the drying operation a weld of 10 cm. is done. The welded sample is quenched first in iced water then in liquid nitrogen. Then the quenched specimen is cleaned, degassed in the measuring apparatus and held there for 72 hours. At the end of the test period the value readed from the measuring apparatus is the content of the hydrogen in the weld metal. This value is transferred to the amount of hydrogen that can diffuse into lOOg of weld metal at standard temperature and pressure. This procedure is repeated from 150°C to 400°C and the values measured were tabulated to a graph. (Diffusible hydrogen content - Drying temperature) By the help of this graph the electrode user can decide on the drying temperature and time for a desired diffusible hydrogen content in the weld metal after welding with a basic covered electrode AS B 255.

Benzer Tezler

  1. Teras çatılarda kullanılan pestil ve sıvı şeklindekisu yalıtım malzemeleri ve uygulamaları

    Watertight insulating materials for flat roofs in the form of membranes and liquıds and their applications

    SİBEL MÜTEVELLİOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    1994

    Mimarlıkİstanbul Teknik Üniversitesi

    PROF. DR. EROL GÜRDAL

  2. Yağ ve petrol ürünlerinin düşük manyetik alanda zaman boyutlu NMR araştırmaları

    Low magnetic field time domain NMR studies of oils and petroleum products

    İLKNUR GÜNDÜZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2013

    Fizik ve Fizik MühendisliğiKocaeli Üniversitesi

    Fizik Ana Bilim Dalı

    DOÇ. DR. SEDA GÜNEŞDOĞDU SAĞDINÇ

  3. Determination of effect of hydrogen on aluminium and its alloys by experimental studies and molecular dynamic simulations

    Hidrojenin alüminyum ve alaşımları üzerindeki etkisinin deneysel çalışmalar ve moleküler dinamik simülasyonlar ile belirlenmesi

    AHMET TIĞLI

    Doktora

    İngilizce

    İngilizce

    2024

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. DERYA DIŞPINAR

  4. Bakır/gümüş/çinko oksit (CuAg/ZnO) partiküllerinin ultrasonik sprey piroliz yöntemiyle üretimi

    Production of CuAg/ZnO nanocomposite particles by ultrasonic sprey pyrolysis

    TOLGA ÇAKMAK

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. SEBAHATTİN GÜRMEN

  5. Mechanical milling of magnesium powders and measurement of their hydrogen sorption characteristics

    Magnezyum tozlarının mekanik olarak öğütülmesi ve hidrojen alma/ verme özelliklerinin ölçümü

    ELİF BAYBÖRÜ

    Yüksek Lisans

    İngilizce

    İngilizce

    2001

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    PROF. DR. TAYFUR ÖZTÜRK