Characterization of micronsized poly (ethylene terephthalate) filled high density polyethylene composites
Mikron boyutta poli (etilen tereflatat) dolgulu yüksek yoğunluklu polietilen kompozitlerin karakterizasyonu
- Tez No: 76021
- Danışmanlar: PROF. DR. TEOMAN DİNÇER
- Tez Türü: Yüksek Lisans
- Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
- Anahtar Kelimeler: Geri dönüşüm, YYPE-PET Kompozitleri, Silan Bağlayıcı, Yüzey Modifikasyonu, Mekanik Özellikler. vi, Recycling, HDPE-PET Composites, Silane Coupling Agent, Surface Modification, Mechanical Properties. IV
- Yıl: 1998
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Polimer Bilim ve Teknolojisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 67
Özet
ÖZ MİKRON BOYUTTA POLİ(ETİLEN TEREFTALAT) DOLGULU YÜKSEK YOĞUNLUKLU POLİETİLEN KOMPOZİTLERİN KARAKTERİZASYONU DEMİR, Tülinay Yüksek Lisans, Polimer Bilim ve Teknolojisi Bölümü Tez Yöneticisi: Prof. Dr. Teoman Tinçer Mayıs 1998, 54 sayfa Bu çalışma atık poli(etilen tereftalat) (PET) şişelerinin, toz haline getirilerek yüksek yoğunluklu polietilende (YYPE) dolgu malzemesi olarak kullanılıp kompozit yapılması yoluyla geri dönüşümünü kapsar. YYPE ile PET arasındaki ilişkiyi arttırmak için silan bağlayıcılar kullanılmıştır. Buna ek olarak, PET tozunun yüzey modifikasyonu için, silan bağlayıcılarla birlikte, maleik anhidrit ve zincir uzatıcılar da kullanılmıştır. Atık PET şişeler kristallendirildikten sonra toz haline getirilmiştir. Daha sonra yüzeyi modifıye edilmiş veya edilmemiş PET tozu kullanılarak, değişik konsantrasyonlardaki kompozitler hazırlanmıştır. PET taneciklerinin ortalama büyüklüğü Tanecik Boyut Analizörü ile tayin edilmiştir. Hazırlanan kompozitlerde taneciklerin matriks içindeki homojen dağılımım göstermek için tomografik metod kullanılmıştır. Mekanik özellikler, elastik modül,kopma mukavemeti, kopmadaki uzama ve darbe dayanımı açısından incelenmiştir. Dinamik mekanik özellikler, Dinamik Mekanik Analizör (DMA) ile çalışılmıştır. Taramalı Elektron Mikroskobu (SEM) ile kompozitlerin kopma yüzeyleri incelenmiştir. Çalışmalarda, ince PET taneciklerinin matriks içinde düzenli dağılımı sağlanmıştır. PET taneciklerinin yüzey modifikasyonu sayesinde, matriks ve dolgu malzemesi arasındaki yapışma başarıyla gerçekleşmiştir. Bu yapışma SEM çalışmalarında da görülmüştür. Böylece, silan bağlayıcılarının, genel kullanımları dışında, organik dolgu malzemesi ve organik matriksten oluşan bu sistemlerde de kullanılabilirliği gösterilmiştir. Kompozitlerin mekanik özelliklerindeki görülür değişiklikler, dolgu malzemesinin, miktarı arttırılarak eklenmesinden ve yüzeyinin modifikasyonundan sonra ortaya çıkmıştır. Modül değerinde, dolgu malzemesinin % 40 oranında eklenmesinden sonra dikkate değer bir artış meydana gelmiştir. Gerilim kuvvetindeki en iyi değerler, yüzey modifikasyonlu % 40 PET içeren kompozitlerde görülmüştür. Diğer taraftan, artan dolgu miktarı kopmadaki uzamanın belirgin oranda azalmasına neden olmuştur. PET yüzeyinin modifikasyonu kompozitlerin darbe direncinde önemli bir iyileşme sağlamıştır. Dolgu miktarının ve yüzey modifikasyonlarının etkileri. DMA çalışmaları ile de gözlenmiştir.
Özet (Çeviri)
ABSTRACT CHARACTERIZATION OF MICRONSIZED POLY(ETHYLENE TEREPHTHALATE) FILLED HIGH DENSITY POLYETHYLENE COMPOSITES DEMIR,Tülinay M.S., Department of Polymer Science and Technology Supervisor: Prof. Dr. Teoman Tinçer May 1998, 54 pages This study covers the recycling of waste poly(ethylene terephthalate) (PET) bottles, via powdering and using as filler in high density polyethylene (HDPE) to make composites of it. Silane Coupling Agents (SCA) were utilised to enhance the compatibility of the filler PET and the matrix HDPE. Maleic anhydride and chain extenders were also used in addition to SCA, to improve the surface properties of PET powder particles. Waste PET bottles were powdered after crystallisation. Then, PET powder, with or without surface treatment, was used to prepare composites at different concentrations by melt mixing. The average size and size distribution of PET particles were determined by Particle Size Analyser instrument. For the prepared composites, tomographic method was applied to examine the homogeneity of dispersion PET of particles through the matrix. Mechanical properties were studied in terms of elastic modulus, tensile iiistrength, strain at break and impact strength. Dynamic mechanical properties were investigated by Dynamic Mechanical Analysis, DMA. The fractured surfaces of composites were examined by Scanning Electron Microscope, SEM. Throughout the studies, the good dispersion of fine PET particles in HDPE matrix was provided. By the surface modification of PET particles, the well adhesion between filler and matrix was successfully achieved. The adhesion was also seen in SEM studies. The ability of utilisation of SCAs for such systems, besides the common use of SCAs, those include both organic filler and an organic matrix was proved to be successful. The observable changes in mechanical properties of composites occurred with the amount of filler and also by the surface treatment. A noticeable increase in modulus took place after addition of 40 % filler. The most improved values in tensile strength appeared in composites contain 40 % surface modified PET. On the other hand, increasing filler content caused a sharp decline in elongation at break. Surface modifications of PET brought about significant developments in impact resistance of composites. The effect of filler content and surface modifications was also observed in DMA studies.
Benzer Tezler
- Investigation of graphene growth on different natural substrates from aromatic plastic wastes and its systematic life cycle assessment
Aromatik plastik atıklardan farklı doğal substratlar üzerinde grafen büyümesinin araştırılması ve sistematik yaşam döngüsü değerlendirmesi
ESRA YALÇINKAYA
Yüksek Lisans
İngilizce
2022
KimyaSabancı ÜniversitesiMalzeme Bilimi ve Nanomühendislik Ana Bilim Dalı
DOÇ. DR. BURCU SANER OKAN
- Synthesis and characterization of nano zinc borate and its usage as a flame retardant for polymers
Nano çinko boratın sentezi,karakterizasyonu ve polimerlerde alev geciktirici olarak kullanılması
BERK BALTACI
Yüksek Lisans
İngilizce
2010
Polimer Bilim ve TeknolojisiOrta Doğu Teknik ÜniversitesiKimya Mühendisliği Bölümü
PROF. DR. GÖKNUR BAYRAM
- Production and characterization of zinc borate-polymer nano composites
Çinko borat-polimer nano kompozitlerin üretilmesi ve karakterizasyonu
HÜLYA BÖLEK
Yüksek Lisans
İngilizce
2011
Metalurji MühendisliğiMarmara ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. AYHAN MERGEN
- Mikro ve nano boyutlu polimer esaslı floresans kemosensörlerin dizaynı
Designing of micro and nano sized polymer based fluorescence chemosensors
ECE AKKOÇ
- Synthesis and characterization of polyurea formaldehydemicrocapsules filled with tung oil for preparation ofcomposite polylactic acid film for self healing applications
Kendini onarabilen polilaktik asit kompozit filmerindekullanılmak üzere tung yağı katklı poliüre formaldehitmikrokapsüllerinin sentezlenmesi ve karakterize edilmesi
GİZEM SEMRA ARITÜRK
Yüksek Lisans
İngilizce
2020
Kimyaİstanbul Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. OZAN SANLI ŞENTÜRK