Yıkama solüsyonlarının MTA ve dentin mikrosertliği üzerine etkisinin in vitro olarak incelenmesi
In vitro investigation of the effect of irrigation solutions on MTA and dentin microhardness
- Tez No: 762651
- Danışmanlar: PROF. DR. HESNA SAZAK ÖVEÇOĞLU
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: mikrosertlik, mta, irrigasyon, retreatment, Kök kanalı irrigantları, Mineral trioksit agregat, Yeniden tedavi, microhardness, mta, irrigation, retreatment, Root canal irrigants, Mineral trioxide aggregate, Irrigation
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Endodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Yıkama solüsyonlarından, özellikle şelatif ajanların retreatment tedavisi sırasında mineral trioksit agregatın (MTA) gücünü azaltma potansiyeline sahip olduğu bilinmektedir. Aynı zamanda dentin dokusunun kompozisyonunda ve yapısında da değişikliklere neden olabilmektedir. Bu çalışmanın amacı, çeşitli kimyasalların kök kanal yıkama solüsyonu olarak kullanıldıklarında kısmen veya tamamen sertleşmiş MTA'nın çözünmesi ve dentin dokusunun mikrosertliği üzerindeki etkinliğini değerlendirmektir. Gereç ve Yöntem: Çalışmamızda EDTA, NaOCl, CHX, CA, serum fizyolojik yıkama solüsyonu olarak, NeoPUTTY ise kanal dolgu malzemesi olarak kullanıldı. Yüksekliği 6mm, kanal genişliği 1,3mm olacak şekilde diş kalıpları hazırlandı. NeoPUTTY'nin 1. Gün ve 21. Gün sertleşmeleri sonrasında hazırlanan numuneler gruplara ayrıldı. Numuneler 10dk boyunca yıkama solüsyonlarına maruz bırakılarak mikrosertlikleri Wilson®-WolpertTM Microindentation Tester 401MVD ile ölçüldü. Bulgular: Kontrol grubu için kullanılan serum fizyolojik dahil olmak üzere tercih edilen tüm solüsyonlar 1. gün ve 21. gün sonunda NeoPUTTY ve dentin dokusunun mikrosertliklerini istatistiksel olarak anlamlı derecede düşürmüşlerdir(p<0,05). 21. gün NeoPUTTY mikrosertlik değerleri, 1. günün NeoPUTTY mikrosertlik değerlerine göre daha yüksektir(p<0,05). Sonuçlar: Solüsyonlar içinde en düşük pH'a sahip Sitrik asit grubu NeoPUTTY ve dentin doku sertliğini diğer solüsyonlara göre anlamlı derecede daha fazla düşürmüştür(p<0,05). Sitrik asit grubu ile EDTA grubu arasında ise anlamlı bir fark bulunamamıştır(p=1,000).
Özet (Çeviri)
Aim: Endodontic solutions, especially chelating agents, have the potential to reduce the strength of mineral trioxide aggregate (MTA) during retreatment. It can cause changes in the composition and structure of dentin. The aim of this study was to evaluate the effectiveness of various chemicals on the dissolution of partially or completely hardened MTA and their effectiveness on the microhardness of dentin when used as endodontic solution. Materials and Methods: In our study, EDTA, NaOCl, CHX, CA, normal saline were used as endodontic solution and NeoPUTTY was used as canal filling material. Tooth molds were prepared with a height of 6 mm and a channel width of 1.3 mm. The samples prepared after the 1st and 21st days of NeoPUTTY hardening were divided into groups. The samples were exposed to endodontic solutions for 10 minutes. The microhardness of the samples was measured with the Wilson®-WolpertTM Microindentation Tester 401MVD. Results: Except for the normal saline used for the control group, all preferred solutions significantly reduced NeoPUTTY and dentin microhardness at the end of day 1 and day 21(p<0,05). Day 21 NeoPUTTY microhardness is higher than Day 1 NeoPUTTY microhardness(p<0,05). Conclusions: Among the solutions, the citric acid group with the lowest pH significantly reduced NeoPUTTY and dentin hardness compared to other solutions(p<0,05). No significant difference was found between the citric acid group and the EDTA group(p=1,000).
Benzer Tezler
- Farklı güncel kalsiyum silikat esaslı simanların kısa ve uzun dönemdeki dentine bağlanma dayanımlarının karşılaştırılması
Comparison of the short- and long-term bond strengths of different contemporary calcium silicate-based cements to dentin
MERVE YÜNÜK
- Smear tabakası"'nın varlığında ve yokluğunda doldurulan kök kanallarında apikal sızıntının incelenmesi
Başlık çevirisi yok
IŞIL KARAGÖZ KÜÇÜKAY
Doktora
Türkçe
1990
Diş Hekimliğiİstanbul ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF.DR. GÜNDÜZ BAYIRLI
- Kitosan-bazlı son yıkama solüsyonlarının Mineral Trioksit Agregat'ın mikrosertliği üzerine etkisi
The effects of chitosan-based final irrigation solutions on the microhardness of Mineral Trioxide Aggregate
HARUN BAĞCI
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiGazi ÜniversitesiEndodonti Ana Bilim Dalı
PROF. DR. BAĞDAGÜL HELVACIOĞLU KIVANÇ
- Epoksi rezin ve biyoseramik esaslı kanal dolgu patlarının kök kanal duvarlarından uzaklaştırılmasında etanol ve EDTA solüsyonlarının etkinliğinin değerlendirilmesi
Efficacy of ethanol and EDTA solution for the removalof epoxy resin and bioceramic based sealers from theroot canal walls
ÇAĞRI CEYLİ
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiBezm-İ Alem Vakıf ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. MEHMET BURAK GÜNEŞER
- Farklı kök kanal yıkama solüsyonları ve kanal dolgu patlarının biyouyumluluklarının hücre kültüründe araştırılması
Investigation of the biocompability of different root canal irrigation solutions and root canal sealers in cell culture
CANDAN GÜRBÜZ SARIGÖL