Geri Dön

Farklı yapıdaki kor materyallerinin tamir bağlanma dayanımlarının değerlendirilmesi

Evaluation of the repair bond strength of core materials with different structure

  1. Tez No: 764055
  2. Yazar: ZUHAL ATA
  3. Danışmanlar: DR. ÖĞR. ÜYESİ TUĞBA SERİN KALAY
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Dental bonding, Dental materyaller, Dental restorasyon, Dental stres analizi, Dental çimentolar, Yapay yaşlandırma, Yüzey işleme tekniği, Dental bonding, Dental materials, Dental restoration, Dental stress analysis, Dental cements, Artificial aging, Surface handling technique
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: Karadeniz Teknik Üniversitesi
  10. Enstitü: Diş Hekimliği Fakültesi
  11. Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Farklı yapıdaki 3 akışkan bulk fill kor materyalinin tamir mikrogerilim bağlanma dayanımlarının (μGBD), yaşlandırmanın ve uygulanan ön yüzey işlemlerinin, tamir μGBD'sine etkisinin değerlendirilmesi amaçlanmıştır. Bu çalışmada bulk fill kor materyallerinden (Clearfill DC Core plus, EverX Flow, SDR Flow+) 6x6x4 mm lik örnekler hazırlandı. Örnekler bir LED ışık cihazıyla (Elipar, 3M ESPE, Almanya) polimerize edildi. Hazırlanan örneklere termal yaşlandırma işlemi uygulandı. Ön yüzey işlemlerine göre, 7 gruba ayrıldı; Kontrol, bu gruba her gruba uygulanan zımpara uygulandı, FA; fosforik asit, HFA; hidroflorik asit, K; kumlama, FA+S; fosforik asit+silan, HFA+S; hidroflorik asit +silan, K+S; kumlama+silan. Ayrıca her kor materyalinden başlangıç bağlama dayanımını belirlemek için ön yüzey işlemi veya yaşlandırma işlemi uygulanmadan tamir kompoziti (P60, 3M ESPE, Almanya) uygulandı. Yaşlandırılan ve ön yüzey işlemleri uygulanan örneklere 4 mm yüksekliğinde tamir kompoziti uygulandı. Örnekler 24 saat 37 °C nemli ortamda bekletildikten sonra düşük hızlı kesme cihazı (Micracut 125, Metkon, Bursa,Türkiye) kullanılarak yaklaşık 1 mm²'lik kesitler elde edildi (n=15). Örneklerin mikrogerilim bağlanma dayanımı (μGBD) testi (Microtensile Tester, Bisco, IL, ABD) 1 mm/dk bir hızda gerçekleştirildi ve veriler MPa cinsinden kaydedildi. Veriler 2 yönlü ANOVA ve Tukey HSD testi ile analiz edildi. μGBD ana faktörlerden (kor materyali yapısı, ön yüzey işlemi) istatistiksel olarak anlamlı şekilde etkilendi (p=0.00). Ön yüzey işlemleri arasında K+S tüm gruplara göre istatistiksel olarak daha yüksek μGBD gösterdi (p<0.05) ve kor materyalleri arasında grup K+S de anlamlı bir farklılık gözlenmedi. Kor materyalleri karşılaştırdığında EverX Flow grubunun μGBD değeri genel olarak daha yüksektir (p<0.05). Başlangıç grubuna göre yaşlandırma sonrası bütün gruplarda μGBD değerinde istatistiksel olarak anlamlı düşüş gözlendi (p<0.05). Ön yüzey işlemi grupları arasında en yüksek tamir bağlanma dayanımı değerini kumlama ve silan uygulaması, kor materyalleri arasında da EverX Flow (kısa fiberle güçlendirilmiş kompozit) grubu gösterdi.

Özet (Çeviri)

It was aimed to evaluate the effect of repair microtensile bond strength (μTBS), aging and applied surface pretreatments on repair μTBS of 3 flowable bulk fill core materials with different structures. In this study, 6x6x4 mm samples were prepared from bulk fill core materials (Clearfill DC Core plus, EverX Flow, SDR Flow). The samples were polymerized with LED light device (Elipar, 3M ESPE, Germany). Thermal aging process was applied to the prepared samples. According to the surface pretreatments, they were divided into 7 groups; Control, sandpaper applied to each group was applied to this group, FA; phosphoric acid, HFA; hydrofluoric acid, K; sandblasting, FA+S; phosphoric acid+silane, HFA+S; hydrofluoric acid +silane, K+S; sandblasting+silane. In addition, repair composite (3M P60) was applied without surface pretreatment or aging to determine the initial bond strength from each core material. A 4 mm high repair composite was applied to the aged and surface pretreated specimens. After the samples were kept in a humid environment at 37 °C for 24 hours, sections of approximately 1 mm² were obtained using a low speed cutting device (Micracut 125, Metkon, Bursa, Turkey) (n=15). Microtensile bond strength testing of the samples (Microtensile Tester, Bisco, IL, USA) was performed at a rate of 1 mm/min and data were recorded in MPa. Data were analyzed by 2-way ANOVA and Tukey HSD test. μGBD was statistically significantly affected by the main factors; core material structure, pre-surface treatment (p=0.00). Between surface pretreatments, K+S showed statistically higher μGBD than all groups (p<0.05), and no significant difference was observed between core materials in group K+S. The μGBD value of the EverX Flow group was generally higher when comparing the core materials (p<0.05). A statistically significant decrease in μGBD value was observed in all groups after aging compared to the initial group. Sandblasting and silane application showed the highest repair bond strength value among the surface pretreatment groups, and the EverX Flow (short fiber reinforced composite) group among the core materials.

Benzer Tezler

  1. Yeni sürmüş çürüksüz daimi birinci molar dişlerde farklı içerikli fissür örtüleme materyallerinin klinik etkinliklerinin değerlendirilmesi

    Clinical efficacy of different fissur sealant materials in the newly erupted non-carious first permanent molars

    DERYA NAZLI SHAKIR

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2021

    Diş Hekimliğiİzmir Katip Çelebi Üniversitesi

    Pedodonti Ana Bilim Dalı

    DOÇ. DR. MERVE AKÇAY

  2. Farklı miktarda kök dentin desteğine sahip dişlerin restorasyonu: Sonlu elemanlar yöntemi ile stres analizi ve yorulma deneyi gerçekleştirilmesi

    The restoration of teeth having different amounts of root dentin loss:stress analysis and fatigue analysis using the finite element method

    ALİ KARAHANOĞLU

    Doktora

    Türkçe

    Türkçe

    2010

    Diş HekimliğiBaşkent Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. SELİM ERKUT

  3. Electric and magneto-transport properties of magnetic and superconductive iron pnictide and skutterudite compounds

    Magnetik ve süperiletken demir pniktid ve skutterudit bileşiklerinin elektrik ve magneto-transport özellikleri

    MURAT SERTKOL

    Doktora

    İngilizce

    İngilizce

    2016

    Fizik ve Fizik Mühendisliğiİstanbul Teknik Üniversitesi

    Fizik Mühendisliği Ana Bilim Dalı

    PROF. DR. YILDIRHAN ÖNER

  4. Oral sıcaklık degisikliklerinin farklı yapıdaki restoratif post ve kor materyaller üzerindeki termal stres etkisinin üç boyutlu sonlu elemanlar termal analiz yöntemi ile karsılastırılması

    Comparison of the effect of thermal change on various restorative dowel and core materials using three dimensional finite element thermal stress analysis

    UMUT KAÇAN

    Doktora

    Türkçe

    Türkçe

    2006

    Diş HekimliğiHacettepe Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF.DR. GÜLBİN SAYGILI

  5. Çocuklarda venöz kan alma işlemi sırasında elde kullanılan topun ağrı ve korku düzeyine etkisi

    The effect of ball used on venous blood collection in children on pain and FEAR level

    ZEYNEP YURDAKUL

    Doktora

    Türkçe

    Türkçe

    2022

    HemşirelikAnkara Üniversitesi

    Hemşirelik Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ FİGEN IŞIK ESENAY