Yüksek kromlu beyaz dökme demire bor elementi ilavesinin aşınma davranışı üzerine etkisinin incelenmesi
Investigation of the effect of boron element addition to high chromium white cast iron on wear behavior
- Tez No: 767497
- Danışmanlar: PROF. DR. ERDEM ATAR
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Gebze Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 87
Özet
Yüksek kromlu beyaz dökme demirler genel olarak iyi aşınma direncine ve tokluk özelliğine sahip oldukları için özellikle yüksek aşınma direnci gerektiren yerlerde geniş kullanım alanına sahiptirler. Bu nedenle cevher kırıcıları, öğütücü değirmen bilyeleri, pompalar, diskler, tarım alet ve makinaları, çeşitli astarlar, madencilik ve metal sanayi sektöründe yaygın olarak kullanılmaktadır. Bu çalışmada, yüksek kromlu beyaz dökme demire farklı oranda bor elementi ilavesi yapılarak mikroyapı, aşınma ve mekanik özellikler üzerine etkileri incelenmiştir. Deneylerde numuneler 100 kg kapasiteli indüksiyon ocağında 4 farklı döküm analizi ile ergitilerek ve kum kalıba dökülerek elde edilmiştir. İlk döküm borsuz, diğer 3 döküm şarja sırasıyla % 0.006, %0.008 ve %0.010 bor içeriğine sahip olacak şekilde bor ilavesi yapılarak alaşımlandırma yapılmıştır. Her bir grup numuneye 1010℃ 'de 6 saat süreyle östenitleme, daha sonra fan ile soğutma ve 200 ℃ 'de 6 saat süreyle temperleme ısıl işlemi uygulanmıştır. Farklı oranlarda yapılan bor elementi ilavesinin tribolojik ve mekanik özelliklere etkilerini incelemek üzere pin-on-disk aşınma testi, darbe testi, üç nokta eğme testi yapılmıştır, aşınma izlerinin ölçümleri iki boyutlu kontak profilometresi ile yapılmıştır, elde edilen her bir numunenin mikroyapısal karakterizasyonu için metalografi numuneleri hazırlanmıştır ve bu numunelerin Optik Mikroskop (OM) ve Taramalı Elektron Mikroskobu (SEM) kullanılarak mikroyapı incelemeleri yapılmıştır. Numuneler üzerinde aynı zamanda XRD analizi gerçekleştirilmiştir. Her bir numunenin sertlik ölçümleri yapılmıştır. Elde edilen sonuçlara göre % 0.010 bor içeriğine sahip numunenin en yüksek eğme mukavemetine, darbe dayanımına ve aşınma direncine sahip olduğu görülmüştür. Artan bor içeriğinin mekanik özellikler ve aşınma direncine pozitif yönde bir etki yaptığı sonucuna varılmıştır.
Özet (Çeviri)
High chromium white cast irons are widely used especially in places where high wear resistance is required, as they have good wear resistance and toughness in general. For this reason, it is widely used in ore crushers, grinding mill balls, pumps, discs, agricultural tools and machinery, various linings, mining and metal industry sectors. In this study, the effects on microstructure, wear and mechanical properties were investigated by adding different ratios of boron element to high chromium white cast iron. In the experiments, the samples were obtained by melting and pouring sand molds with 4 different casting analyzes in an induction furnace with a capacity of 100 kg. Alloying was done by adding boron to the first casting without boron, the other 3 castings with boron content of 0.006%, 0.008% and 0.010%, respectively. Austenitizing at 1010°C for 6 hours, then fan cooling and tempering at 200°C for 6 hours were applied to each group of samples. Pin-on-disc wear test, impact test, three-point bending test were performed to examine the effects of boron addition at different rates on tribological and mechanical properties were prepared and microstructure examinations of these samples were made using Optical Microscope (OM) and Scanning Electron Microscope (SEM). XRD analysis was also performed on the samples. Hardness measurements of each sample were made. According to the results obtained, it was seen that the sample with 0.010% boron content had the highest bending strength, impact resistance and abrasion resistance. It was concluded that increasing boron content had a positive effect on mechanical properties and wear resistance.
Benzer Tezler
- Maden kırıcılarda kullanılan beyaz dökme demirlerde bor katkısının ve ısıl işlemin mekanik özelliklere etkisi
Effect of heat treatment and bor addition to mechanical properties of white cast irons used for the mining applications
GÜRKAN KAZDAL
Yüksek Lisans
Türkçe
2011
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. HAVVA KAZDAL ZEYTİN
PROF. DR. HÜSEYİN ÇİMENOĞLU
- Gri dökme demirin dubleks dökümünde karbür yapıcı elementlerin mekanik ve mikroyapı özelliklerine etkilerinin incelenmesi
Investigation of effects from the point of mechanic and microstructure properties of elements formed carbide on doblex cast of grey cast iron
YAHYA TAŞGIN
Doktora
Türkçe
2007
Metalurji MühendisliğiFırat ÜniversitesiMetalurji Eğitimi Ana Bilim Dalı
YRD. DOÇ. MEHMET KAPLAN
- Ötektiküstü yüksek kromlu beyaz dökme demirlerde Ce ve B elementlerinin mikroyapı üzerindeki etkileri
The effects of Ce and B elements on the microstructure ofhypereutectic high chromium white cast iron
HASAN KAYA
Yüksek Lisans
Türkçe
2022
Makine MühendisliğiTekirdağ Namık Kemal ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. İBRAHİM SAVAŞ DALMIŞ
PROF. DR. SERDAR OSMAN YILMAZ
- Ötektik altı yüksek kromlu beyaz dökme demire mo-w-ti ilavesiyle aşınma direncinin iyileştirilmesi
Abrasion resistance improvement of hypo eutectic high chromium white cast iron by mo-w-ti addition
BURAK KÜRŞAD BAŞARAN
Yüksek Lisans
Türkçe
2019
Makine MühendisliğiTekirdağ Namık Kemal ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. SERDAR OSMAN YILMAZ
- Yüksek kromlu beyaz dökme demirlerde nb, ti, v, mg elementlerinin mikroyapı, aşınma ve darbe direncine etkisinin incelenmesi
Investigation of the effect of ti, nb, v and mg elements on microstructure, wear and impact resistance of high chromium white cast iron
ŞÜKRAN MUTLU
Doktora
Türkçe
2012
Metalurji MühendisliğiGazi ÜniversitesiMetal Eğitimi Ana Bilim Dalı
PROF. DR. KADİR KOCATEPE