AISI 4140 çeliklerinden üretilen hafif silah kapak bileşenlerinin yüzey özelliklerinin nitrokarbürizasyon yöntemi ile geliştirilmesi
Development of surface characteristics of light weapon slide components to be made of AISI 4140 steels with nitrocarburization
- Tez No: 768394
- Danışmanlar: PROF. DR. GENÇAĞA PÜRÇEK
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Metalurji Mühendisliği, Mechanical Engineering, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Malzeme Bilim Dalı
- Sayfa Sayısı: 119
Özet
Bu çalışmada, hafif silahlarda ateşleme esnasında ve sonrasında meydana gelen sürtünme, aşınma, yorulma, aşırı ısınma ve korozyon gibi olumsuz etkilerin nitrokarbürizasyon işlemi ile miminize edilmesi amaçlanmıştır. Bu kapsamda temel tabanca parçalarından biri olan AISI 4140 kapak parçası yüzey hazırlık işlemleri optimize edilerek nitrokarbürizasyon prosesi öncesi en iyi yüzey durumuna getirilmiştir. Deney numunelerine farklı sıcaklık ve süre parametrelerinden oluşan on iki farklı nitrokarbürizasyon işlemi uygulanmıştır. Sonrasında ise tüm deney numunelerinin korozyon dayanımı artırmak ve estetik bir görünüm kazandırmak için numunelere oksidasyon ve kumlama işlemleri uygulanmıştır. Numunelere uygulanan her yüzey işlem sonrasında yüzey pürüzlülüğü ölçümleri yapılmıştır. Nitrokarbürizasyon sonrası yüzey işlemleri de uygulandıktan sonra sertlik değeri ölçümü, metalografik incelemeler, aşınma testi, yüzey topografyası incelemeleri gerçekleştirilmiştir. Elde edilen sonuçlara göre, kumlama en iyilemesi sonrası en kararlı ve homojen yüzey S70 çelik bilye ile kumlanan numunelerde elde edilmiştir. Bileşik tabaka kalınlığının sıcaklık ve süre ile birlikte arttığı, aşınma miktarının ise bileşik tabaka değeri arttıkça azaldığı görülmüştür. Difüzyon tabakasındaki artışın süre ve sıcaklık artışı ile doğru orantılı arttığı, fakat işlem süresi arttıkça kalınlık artış hızında düşüş meydana geldiği tespit edilmiştir. Difüzyon tabakasının belirli kalınlığa ulaştıktan sonra yavaş ilerlediği; sertliğin ise difüzyona bağlı olmaksızın arttığı görülmüştür.
Özet (Çeviri)
In this study, it is aimed to minimize the negative effects such as friction, wear, fatigue, overheating and corrosion that occur in weapons during and after firing by nitrocarburization process. In this context, the AISI 4140 slide piece, which is one of the basic gun parts, has been brought to the best surface condition before the nitrocarburization process by optimizing the surface preparation processes. Twelve different nitrocarburization processes consisting of different temperature and time parameters were applied to the test samples. Afterwards, oxidation and sandblasting processes were applied to all test samples to increase corrosion resistance and to give them an aesthetic appearance. Surface roughness measurements were made after each surface treatment applied to the samples. After applying the surface treatments after nitrocarburization, hardness value measurement, metallographic examinations, wear tests, surface topography examinations were carried out. According to the results obtained, the most stable and homogeneous surface after sandblasting optimization was obtained in the samples blasted with S70 steel shot. It was observed that the composite layer thickness increased with temperature and time, while the rate of wear decreased as the composite layer value increased. It was determined that increasing in the diffusion layer also increased in direct proportion with the increase in time and temperature, but as the treatment time increased, the thickness increment rate decreased. After reaching a certain thickness, the increment rate in the diffusion layer decreased slowly; It was also observed that the hardness increased regardless of the diffusion.
Benzer Tezler
- İnşaat asansörleri istikamet makaralarında kullanılan farklı çelik malzemelerin aşınmalarının incelenmesi
Examination of the wear of different steel materials used in construction hoists direction rollers
ÜNAL KILINÇ
Yüksek Lisans
Türkçe
2020
Makine MühendisliğiSüleyman Demirel ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ŞEVKİ YILMAZ GÜVEN
- ZnCrCo alaşım filmlerinin elektrokimyasal depolama yöntemi ile üretimi, karakterizasyonu ve korozyon özelliklerinin incelenmesi
Production of ZnCrCo alloy films by electrochemical deposition technique, characterization and investigation of corrosion properties
ÜNZİLE ULUTAŞ
Yüksek Lisans
Türkçe
2009
Fizik ve Fizik MühendisliğiMustafa Kemal ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. HÜSNÜ SALİH GÜDER
- Toz metalürjisi ile üretilen çeliklerde presleme tekniğinin mikroyapı mekanik özelliklere etkisinin araştırılması
Investigation of the effect of pressing technique on microstructure mechanical properties in steel produced by powder methods
BURAK AYVACI
Yüksek Lisans
Türkçe
2019
Makine MühendisliğiKarabük Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
DOÇ. DR. MEHMET AKİF ERDEN
- AISI 1350 çeliğinden imal edilmiş buraj makinesi kazmalarının yerine, AISI 1040 ve AISI 4140 çeliklerinin kullanabilirliğinin araştırılması
An investigation about availability of AISI 1040 and AISI 4140 steels instead of AISI 1350 steel at production of tamping machine?s diggers
BİLGEHAN DOĞAN
Yüksek Lisans
Türkçe
2011
Makine MühendisliğiCumhuriyet ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. BURHAN SELÇUK
- Üç farklı çeliğe katı borlama işlemi yapılmasının içyapı ve sertlik üzerine etkisinin incelenmesi
The investigation of effect of solid boronizing process on microstructure and hardness in three different steels
MEHMET ÖZER
Yüksek Lisans
Türkçe
2011
Makine MühendisliğiBalıkesir ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. İRFAN AY