Karbon lif ve karbon aerojel katkılı çimento kompozitlerinin elektriksel özelliklerinin incelenmesi

Investigation of the electrical properties of carbon fiber and carbon aerogel additives cement composites

  1. Tez No: 772475
  2. Yazar: ABDULKERİM BUĞRA KOÇAN
  3. Danışmanlar: DOÇ. DR. MERAL OLTULU
  4. Tez Türü: Yüksek Lisans
  5. Konular: İnşaat Mühendisliği, Civil Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: Atatürk Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 100

Özet

Çimento esaslı kompozitler, üstün dayanıklılıkları ve mekanik özellikleri nedeniyle, inşaat mühendisliği alanında kullanımı en önde gelen malzemelerdir. Elektriksel iletkenlik özelliklerinin iyileştirilmesine bağlı olarak, yapısal sağlık izleme, akıllı trafik izleme ve kar eritme vb. çeşitli uygulama alanlarında da kullanımı artmaktadır. Bu çalışmada, çimento esaslı kompozitlerin karbon lif ve karbon aerojel iletkenlerinin katkısıyla elektriksel iletkenlik özelliklerinin artırılması amaçlanmıştır. Çalışmanın birinci aşamasında çimentonun ağırlıkça %0,50, %0,75, %1 ve %1,5'i oranlarında karbon lif katkılı çimentolu kompozitler üretilerek basınç dayanımı, eğilme dayanımı ve elektriksel iletkenlik yönünden optimum kullanılma oranı bulunmuştur. Çalışmanın ikinci aşamasında ise belirlenen optimum karbon lif oranı sabit tutularak; çimento ağırlığının %0,25, %0,50, %0,75, %1, %1,25, %1,5, %1,75 ve %2'si oranlarında karbon aerojel katkısının çimento esaslı kompozitin basınç, eğilme dayanımı ile elektriksel iletkenlik özellikleri üzerindeki etkileri incelenmiştir. Karbon lif ve karbon aerojel katkılı kompozitlerin iç yapılarının incelenmesi için SEM ve XRD analizleri yapılmıştır. Çimentolu kompozitlere hem mekanik hem de elektriksel iletkenlik özellikleri açısından %1 karbon lif eklenmesinin uygun olacağı tespit edilmiştir. Bu oran sabit tutularak kompozite farklı oranlarda eklenen karbon aerojelin de optimum oranının %1 olduğu belirlenmiştir. Optimum oranda karbon aerojel ve karbon lifli çimentolu kompozitlerin elektriksel dirençlerindeki azalışın %80 olduğu belirlenmiştir. Karbon aerojel katkısı çimentolu kompozitlerin basınç ve eğilme dayanımlarında %10-%30'luk bir azalış meydana getirmiştir. Elektriksel iletkenlik açısından karbon aerojel ve karbon lif malzemelerinin birlikte kullanımının daha iyi olduğu belirlenmiştir. Katkılı kompozitlerin, elektriksel iletkenlikleri ilerleyen yaşlarda giderek azalmaktadır. Karbon aerojel katkısı çimentolu kompozitlerin basınç dayanımlarında olumsuz bir etkiye sebep olmuştur.

Özet (Çeviri)

Cement composites are the most prominent materials for use in the field of civil engineering due to their superior durability and mechanical properties. Depending on the improvement of its electrical conductivity properties, its use is increasing in various application areas such as structural health monitoring, smart traffic monitoring, and snow melting. This study, it was aimed to increase the electrical conductivity properties of cement-based composites with the addition of carbon fiber and carbon aerogel conductors. In the first stage of the study, cement composites with carbon fiber additives at 0.50%, 0.75%, 1%, and 1.5% by weight of cement were produced and the optimum ratio was found in terms of compressive strength, flexural strength, and electrical conductivity. In the second stage of the study, by keeping the determined optimum carbon fiber ratio constant; the effect of carbon aerogel added at the ratios of 0.25%, 0.50%, 0.75%, 1%, 1.25%, 1.5%, 1.75%, and 2% by weight of cement on the compressive strength, flexural strength and electrical conductivity properties of cement-based composites was investigated. SEM and XRD analyzes were performed to examine the internal structures of carbon fiber and carbon aerogel-added cementitious composites.It has been determined that 1% carbon fiber should be added to cementitious composites in terms of both mechanical and electrical conductivity properties. It was determined that the optimum ratio of carbon aerogel added to the cemented composite at different rates by keeping the 1% carbon fiber ratio constant was 1%. The decrease in electrical resistance of cementitious composites with 1% carbon aerogel and carbon fiber was 80%. Carbon aerogel additive caused a 10%-30% decrease in the compressive and flexural strengths of cementitious composites.It was determined that the combined use of carbon aerogel and carbon fiber materials is better in terms of electrical conductivity. The electrical conductivity of composites gradually decreases with proceeded age. The carbon aerogel additive caused a negative effect on the compressive strength of the cementitious composites.

Benzer Tezler

  1. Conductive polyamide/carbon black, carbon fiber and carbon nanotubes composites for electrostatic painting

    Elektrostatik boyamaya uygun iletken poliamid/ karbon siyahı, karbon lif ve karbon nano tüp kompozitleri

    AMIRHOSSENI NASRI

    Yüksek Lisans

    İngilizce

    İngilizce

    2015

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    Prof. Dr. ESMA SEZER

  2. Development and characterization of thermal and structural properties of textile fibers

    Tekstil elyafın termal ve yapısal özelliklerinin geliştirilmesi ve karakterize edilmesi

    MD MAHBUBOR RAHMAN

    Doktora

    İngilizce

    İngilizce

    2021

    Tekstil ve Tekstil MühendisliğiErciyes Üniversitesi

    Tekstil Mühendisliği Ana Bilim Dalı

    PROF. DR. İSMAİL KARACAN

  3. Aktif-karbonizasyon öncesi selüloz esaslı tekstil malzemelerinin termal kararlılığının sağlanması ve yapısal özelliklerinin araştırılması

    Investigation of the structural properties of thermally stabilized cellulose based textile materials prior to carbonization and activation

    TANER SOY

    Yüksek Lisans

    Türkçe

    Türkçe

    2012

    KimyaErciyes Üniversitesi

    Tekstil Mühendisliği Ana Bilim Dalı

    DOÇ. DR. İSMAİL KARACAN

  4. Hızlandırılmış oksidasyon aşamasının poliakrilonitril (PAN) esaslı karbon lif üretimi sırasında değerlendirilmesi ve etkilerinin araştırılması

    The assessment and the investigation of the effects of accelerated oxidation stage during the production of PAN-based carbon fibers

    AHMET KILIÇ

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    Tekstil ve Tekstil MühendisliğiErciyes Üniversitesi

    Tekstil Mühendisliği Ana Bilim Dalı

    PROF. DR. İSMAİL KARACAN

  5. Experimental investigation and finite element modeling of rehabilitated and steel fiber rc members

    Rehabilite edilmiş çelik lif katkılı betonarme elemanların deneysel araştırması ve sonlu elemanlar modellemesi

    MOHAMMED SHAKIB MOHAMMED AL JAWAHERY

    Doktora

    İngilizce

    İngilizce

    2018

    İnşaat MühendisliğiGaziantep Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    Prof. Dr. ABDULKADİR ÇEVİK

    Assist. Prof. Dr. MEHMET EREN GÜLŞAN