Santrifüj pompaların çark malzemesine yapılan yüzey işlemi sonrasında performans değerlendirmesi

Performance evaluation of centrifugal pumps after surface treatment on impeller material

  1. Tez No: 781042
  2. Yazar: FURKAN ENES GÜNDOĞDU
  3. Danışmanlar: DOÇ. DR. LÜTFÜ NAMLI
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Hidrofobik yüzey, Santrifüj pompa, Pompa çarkı, SiO2 kaplama, Pompa verimi, PETG, Hydrophobic surface, Centrifugal pump, Pump impeller, SiO2 coating, Pump efficiency, PETG
  7. Yıl: 2023
  8. Dil: Türkçe
  9. Üniversite: Ondokuz Mayıs Üniversitesi
  10. Enstitü: Lisansüstü Eğitim Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 78

Özet

Bu çalışmada, muadillerine kıyasla daha uygun üretim maliyetine sahip olan katmanlı üretim metoduyla çalışan üç boyutlu yazıcıdan(3B yazıcı) pompa ve pompanın çarkları üretilmiştir. Piyasada kullanılan pompaların enerji tüketiminde verim düşüklüğü, dünyamızın enerji ihtiyacının çok olduğu bu dönemde problem oluşturmaktadır. Pompa çarklarına yapılacak kaplamanın ardından yüzeydeki hidrofobik özelliğin pompa performansına etkisi deneysel olarak bu çalışmada incelenmiştir. Ayrıca 3B yazıcı üretimi olan pompa parçalarının yüzey pürüzlülüğü ve çekme dayanımı incelenmiştir. Polietilen tereftalat glikol (PETG) hammaddesinden üretilen pompa çarklarına şeffaf epoksi kaplama, kütlesel olarak farklı oranlarda (%3, %7.5, %10) TiO2 ve SiO2 nanopartikül katkılı epoksi kaplamalar yapılmıştır. PETG hammaddesinden üretilen parçaların yüzeyleri 70° temas açısına sahiptir ve hidrofilik yüzeydir. Kaplanan yüzeyler arasında 110° hidrofobik temas açısına sahip kütlesel olarak %7.5 SiO2 katkılı epoksi kaplama en iyi sonucu vermiştir. Kütlesel olarak %7.5 SiO2 katklı epoksi ile kaplama yapılan PETG hammaddesinden üretilmiş çark yüzeylerinin pürüzlülük analizi yapıldığında, kaplamasız yüzeyin Ra değeri 8.5 µm, kaplama sonrasında Ra değeri 0.5 µm değerine düşürülerek parça yüzeylerindeki pürüzlülük iyileştirilmiştir. Yapılan çekme testinde kaplamasız malzemenin çekme dayanımı 48MPa çıkmıştır. Kaplama sonrasında bu değer 57MPa çıkarılarak malzemenin çekme dayanımı arttırılmıştır. Üç farklı pompa çark tipi üretilmiştir. Pompa çark yüzeylerine yapılan kütlesel olarak %7.5 SiO2 epoksi kaplama sonrasında hidrofobik yüzeye sahip olmuşlardır. Hazırlanan pompa performans deney düzeneğinde pompa performansı ölçülmüştür. Deneyler sonucunda hidrofobik yüzeye sahip olan çarklarda pompanın debisi, pompa basma yüksekliği ve pompanın veriminin arttığı ispatlanmıştır. Ayrıca pompa çarklarındaki geotmetrik olarak farklılık olsa da, çarkların yüzeyinin hidrofobik özellikteki yüzeye çevrildiğinde veriminin arttığı deneysel olarak ispatlanmıştır.

Özet (Çeviri)

In this study, the pump and the impellers of the pump were produced from a three-dimensional printer (3D printer) working with the additive manufacturing method, which has a more affordable production cost compared to its counterparts. The low efficiency in energy consumption of pumps used in the market poses a problem in this period when the world's energy needs are high. The effect of the hydrophobic feature on the surface after the coating on the pump impellers on the pump performance has been experimentally investigated in this study. In addition, the surface roughness and tensile strength of the pump parts produced by 3D printers were examined. Transparent epoxy coating, TiO2 and SiO2 nanoparticle added epoxy coatings in different mass ratios (%3, %7.5, %10) were applied to the pump impellers produced from polyethylene terephthalate glycol (PETG) raw material. The surfaces of the parts produced from PETG raw material have a contact angle of 70° and are hydrophilic. The epoxy coating with a hydrophobic contact angle of 110° between the coated surfaces, with %7.5 by mass SiO2 added, gave the best results. When the roughness analysis of the impeller surfaces made of PETG raw material coated with epoxy with massive %7.5 SiO2 additive was performed, the Ra value of the uncoated surface was reduced to 8.5 µm and the Ra value of 0.5 µm after coating, and the roughness on the part surfaces was improved. In the tensile test, the tensile strength of the uncoated material was 48MPa. After coating, this value was increased to 57MPa, increasing the tensile strength of the material. Three different pump impeller types were produced. After the epoxy coating of %7.5 by mass of SiO2 on the pump impeller surfaces, they have a hydrophobic surface. Pump performance was measured in the prepared pump performance test setup. As a result of the experiments, it has been proven that the flow rate of the pump, the pump head and the efficiency of the pump increase in impellers with hydrophobic surfaces. In addition, although there are geometrical differences in the pump impellers, it has been experimentally proven that the efficiency of the impellers increases when the surface of the impellers is turned to the hydrophobic surface.

Benzer Tezler

  1. Pompalarda yüzey pürüzlülüğünün ve kaçakların performans üzerindeki etkilerinin incelenmesi

    Research of the affects of surface roughness and loses on pumps's performance

    ERKAN GÜLMEZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2006

    Makine MühendisliğiUludağ Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. İRFAN KARAGÖZ

  2. İki farklı santrifüş çark yüzey pürüzlülüğü değiştirilmesi ile pompa karakteristiklerinin değişiminin saptanması üzerinde bir araştırma

    Başlık çevirisi yok

    ŞENEL KOÇOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    1998

    ZiraatTrakya Üniversitesi

    Tarım Makineleri Ana Bilim Dalı

    DOÇ. DR. BAHATTİN AKDEMİR

  3. Santrifüj pompalarda çark malzemesine ve yüzey kaplamasına bağlı kavitasyon hasarı değerlendirmesi

    Evaluation of cavitation damage related to impeller material and surface coating in the centrifugal pumps

    AHMET TUNÇ

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Makine MühendisliğiErciyes Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. SEDAT ÖZDEN

  4. Sulama amaçlı yatay milli santrifüj pompaların imalat karakteristiklerinin bilgisayar destekli tasarımla geliştirilmesi

    To improve by computer aided design (cad.) of production characteristics of centrifugal pumps with horizontal axis used in irrigation

    RECAİ GÜRHAN

    Doktora

    Türkçe

    Türkçe

    1990

    ZiraatAnkara Üniversitesi

    Tarımsal Mekanizasyon Ana Bilim Dalı

    PROF. DR. MUSA AYIK

  5. Santrifüj pompaların verim ve kavitasyon açısından çok amaçlı optimizasyonu

    Multi-objective optimization of centrifugal pumps in terms of efficiency and cavitation

    ELİFNUR DEMİREL

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Makine Mühendisliğiİstanbul Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. LEVENT ALİ KAVURMACIOĞLU

    DR. ÖĞR. ÜYESİ AYDIN HACI DÖNMEZ