Evaluatıon of the color stabılıty of HEAT-cured and cad/cam acrylıc resın materıals used ın removable dentures agaınst varıous staınıng agents
Hareketli protezlerde kullanılan ısı ile sertleşen ve CAD/CAM akrilik rezin materyallerinin çeşitli boyayıcı ajanlara karşı renk stabilitelerinin değerlendirilmesi
- Tez No: 785857
- Danışmanlar: PROF. DR. İDİL DİKBAŞ
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Akrilik rezin, renk stabilitesi, spektrofotometre, CAD/CAM, Akrilik reçineler, Diş renk değişikliği, Protezler ve implantlar, Spektrofotometri, Acrylic resin, color stability, spectrophotometer, CAD/CAM, Acrylic resins, Tooth discoloration, Prostheses and implants, Spectrophotometry
- Yıl: 2023
- Dil: İngilizce
- Üniversite: Yeditepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, hareketli protezlerde kullanılan ısı ile sertleşen ve CAD/CAM akrilik rezin materyallerinin çeşitli boyama ajanlarına karşı oluşabilecek renk değişimlerini değerlendirmek ve karşılaştırmaktır. Materyal ve Metod: 3 marka CAD / CAM akrilik rezin bloğu (Dentsply/Lucitone 199, Merz/M-PM ve Ondent/Tempo-Cad) ve 1 marka ısı ile sertleşen akrilik rezin materyali (Heraeus Kulzer/Paladent 20) test edildi. Numuneler 4 farklı solüsyona daldırıldı: distile su, çay, kahve ve kırmızı şarap. Her akrilik grup için 15 mm çapında ve 2 mm kalınlığında 40 adet disk şeklinde örnek hazırlandı (n=10). Örnekler çözeltilere daldırılmadan önce, bir spektrofotometre kullanılarak baseline (T0) renk ölçümü yapıldı. Toplamda 6 renk ölçümü gerçekleştirildi. Renk farklılıklarını (ΔE) belirlemek için CIE L*a*b*renk alanı kullanıldı. İstatistiksel analiz için ANOVA testleri ve Sequential Bonferroni testi kullanıldı. Bulgular: 5 haftalık daldırma sonunda, en yüksek renk değişimi (ΔE), kırmızı şarap için CAD/CAM 1 Dentsply grubunda (ΔE=6.28±0.24). Çay ve kahve solüsyonlarında ise, 5 haftalık daldırma sonunda en yüksek ΔE deeğrleri CAD/CAM 3 Ondent grubunda bulunmuştur ve ΔE değerleri sırasıyla belirtilmiştir (ΔE=5.54±0.21), (ΔE=5.25±0.25). Distile su haricinde çay, kahve ve kırmızı şarap için en düşük renk değişimi (ΔE) CAD/CAM 2 Merz grubunda gözlenmiştir ve ΔE değerleri sırasıyla belirtilmiştir (ΔE=4.23±0.14), (ΔE=3.48±0.18), (ΔE=5.24±0.18). Tüm akrilik rezin gruplarında çalışma sonunda distile su dışındaki tüm solüsyonlar klinik olarak belirgin renk değişikliğine neden olmuştur (3<NBS<6). 4 farklı akrilik resin grubunun 4 farklı solüsyondaki renk stabilitesi arasında önemli bir fark bulunmuştur (p<0.05). Sonuç: Tüm akrilik rezin gruplarına ait ΔE değerleri artan daldırma zamanıyla doğru orantılı olarak artış göstermiştir. Isı ile sertleşen akrilik rezin, renk stabilitesi açısından CAD/CAM akrilik rezinlerle karşılaştırılabilir değerlerde bulunmuştur.
Özet (Çeviri)
Aim: The aim of this study is to evaluate and compare the changes in the color of heat-cured and CAD/CAM acrylic resin materials used in removable dentures against various staining agents. Materials and Method: 3 brands of CAD/CAM acrylic resin blocks (Dentsply/Lucitone 199, Merz/M-PM, and Ondent/Tempo-Cad) and 1 brand of heat-cured acrylic resin material (Heraeus Kulzer/Paladent 20) were tested. The samples were immersed in 4 different solutions: Distilled water, tea, coffee and red wine. For each acrylic groups, 40 disc-shaped samples with 15 mm in diameter and 2 mm in height were prepared (n=10). Before the samples were immersed in the solutions, a spectrophotometer was used to measure the baseline color measurement (T0). 6 color measurements were made in total. The CIE L*a*b*color space was used to determine color differences (ΔE). ANOVA tests and sequential Bonferroni adjustment were used in statistical analysis. Results: At the end of 5 weeks of immersion, the highest color change (ΔE) was observed for the CAD/CAM 1 Dentsply group immersed in red wine (ΔE=6.28±0.24). The highest ΔE values for tea and coffee solutions were observed in CAD/CAM 3 Ondent group, respectively (ΔE=5.54±0.21), (ΔE=5.25±0.25) at the end of the 5 weeks of immersion. The lowest color change (ΔE) was observed for the CAD/CAM 2 Merz group was immersed in tea, coffee and red wine (except distilled water), respectively (ΔE=4.23±0.14), (ΔE=3.48±0.18) (ΔE=5.24±0.18). In all acrylic resin groups, all solutions caused clinically marked color change except distilled water, at the end of the study (3<NBS<6). The color stability of 4 different acrylic resin groups in 4 different solutions showed a significant difference (p<0.05). Conclusion: ΔE values of all acrylic resin groups increased proportionally with increasing immersion time. The color stability of heat-cured acrylic resin was comparable to that of the CAD/CAM acrylic resins.
Benzer Tezler
- İsmayıl Hakkı Baltacıoğlu'nun kültür ve eğitim kavramı üzerine bir inceleme
An Examination of the concepts of culture and education of Ismayıl Hakkı Baltacıoğlu
ABDULLAH DİKİCİ
Doktora
Türkçe
1986
Eğitim ve ÖğretimUludağ ÜniversitesiEğitim Bilimleri Ana Bilim Dalı
DOÇ. DR. SUAT ANAR
- Gebelik ve doğum olgularında prolaktin düzeylerinin değerlendirilmesi
The Evaluation of prolactin values during pregnancy labour and in deliveries
TÜLİN AKAN
Tıpta Uzmanlık
Türkçe
1987
Kadın Hastalıkları ve DoğumGazi ÜniversitesiKadın Hastalıkları ve Doğum Ana Bilim Dalı
DOÇ.DR. MÜLAZIM YILDIRIM
- Yenileme yatırımları
Başlık çevirisi yok
OSMAN NURİ FİLİZ
Yüksek Lisans
Türkçe
1986
İşletmeGazi ÜniversitesiEndüstri Mühendisliği Ana Bilim Dalı
DOÇ. DR. OSMAN OKKA
- Bromtimol mavisi, bromkresol moru ve klorfenol kırmızısı indikatörleri katılmış özel besiyerlerinin sütlerde antibiyotik belirtilmesine uygunluğu üzerine araştırmalar
Başlık çevirisi yok
ESENGÜL TUNCER
Yüksek Lisans
Türkçe
1985
Gıda MühendisliğiEge ÜniversitesiSüt Teknolojisi Ana Bilim Dalı
PROF. DR. HASAN YAYGIN