Plastik deformasyon sonrası TNTZ, inconel ve nitinol'un mekanik özelliklerinin araştırılması

Investigation of mechanical properties of TNTZ, inconel and nitinol after plastic deformation

  1. Tez No: 800695
  2. Yazar: SEDA BAYRAM
  3. Danışmanlar: DOÇ. DR. SİNAN SEZEK
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2023
  8. Dil: Türkçe
  9. Üniversite: Atatürk Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Amaç: TNTZ, Inconel 925 ve NiTi alaşımlarının plastik deformasyona ile uğratılarak mekanik özelliklerinin iyileştirilmesi Yöntem: Plastik deformasyon için haddeleme yöntemi kullanılmıştır. TNTZ, Inconel 925 ve NiTi alaşımlarının %30,50 ve 70 oranlarında deforme olması edilmesi durumunda çeşitli mekanik deneyler (mikrosertlik, aşınma, korozyon ve basma testi) uygulanarak mekanik özelliklerdeki değişim incelenmiştir. Bulgular: TNTZ, Inconel 925 ve NiTi alaşımlarının mikro yapısındaki değişim karakterizasyon yöntemleri kullanılarak araştırılmıştır. Bunun sonucunda deformasyon oranı arttıça özellikle alaşımların mikro yapı %70 deforme olmuş numunelerde ince taneli ve anizotropik bir yapıda olduğu tespit edilmiştir. Yapılan mekanik deneyler sonucunda da TNTZ, Inconel 925 ve NiTi alaşımlarının deformasyon oranı arttıkça mekanik özelliklerinde de iyileşmenin sağlandığı görülmştür. Özelliklede %70 deforme olan numunelerde bu iyileşmenin daha fazla olduğu tespit edilmiştir. Sonuç: Bu çalışmada NiTi, TNTZ ve Inconel 925 alaşımlarının biyomedikal sektöründe metalik biyomalzeme olarak kullanımını yaygınlaştırmak için plastik deformasyon yöntemi ile bu alaşımların sertliği ve buna bağlı olarak mekanik özelliklerinin geliştirilmesi hedefi ile çalışmalar yapılmıştır. Yapılan deneysel çalışmalarda en iyi serlik artışı % 69 ile Inconel 925 alaşımında elde edilmiştir. Basma deneyi sonucunda en iyi akma dayanımı 2350 MPa ile TNTZ alaşımında elde edilmiştir. En iyi korozyon direnci de yine 1,02 mpy ile Inconel 925 alaşımında sağlandığı tespit edilmiştir. Yapılan deneysel çalışmalar ışığında bu alaşımların biyomalzeme olarak kullanım trendini artıracak mekanik özelliklerin artırılmış olduğu tespit edilmiştir.

Özet (Çeviri)

Purpose: Improvement of mechanical properties of TNTZ, Inconel 925 and NiTi alloys by plastic deformation Method: The rolling method was used for plastic deformation. In case of deformation of TNTZ, Inconel 925 and NiTi alloys at 30.50% and 70%, the change in mechanical properties was investigated by applying various mechanical tests (microhardness, wear, corrosion and compression test). Results: Changes in the microstructure of TNTZ, Inconel 925 and NiTi alloys were investigated using characterization methods. As a result of this, as the deformation rate increased, it was determined that the alloys had a fine-grained and anisotropic structure, especially in the samples whose microstructure was 70% deformed. As a result of the mechanical experiments, it was observed that the mechanical properties of TNTZ, Inconel 925 and NiTi alloys increased as the deformation rate increased. It has been determined that this improvement is more especially in the samples that are 70% deformed. Conclusion: In this study, studies were carried out with the aim of improving the hardness and mechanical properties of these alloys by plastic deformation method in order to popularize the use of NiTi, TNTZ and Inconel 925 alloys as metallic biomaterials in the biomedical sector. In the experimental studies, the best hardness increase was obtained in Inconel 925 alloy with 69%. As a result of the compression test, the best yield strength was obtained in TNTZ alloy with 2350 MPa. It was determined that the best corrosion resistance was obtained in Inconel 925 alloy with 1.02 mpy. In the light of experimental studies, it has been determined that these alloys have increased mechanical properties that will increase the trend of use as biomaterials.

Benzer Tezler

  1. Investigation of the mechanical behavior of severely deformed aluminum alloy under multi-directional forging

    Aşırı plastik deformasyon uygulanmış alüminyum alaşımının çok yönlü dövme sonrası mekanik davranışının incelenmesi.

    BURAK BAHAT

    Yüksek Lisans

    İngilizce

    İngilizce

    2023

    Makine MühendisliğiÖzyeğin Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. GÜNEY GÜVEN YAPICI

  2. Üç farklı kaide materyalinin termal siklus sonrası çekme dayanımlarının ve plastik deformasyonlarının karşılaştırılması

    Comparison of tensile strengths and plastic deformations of three different denture base materials after thermocycling

    BURAK TANIŞ

    Doktora

    Türkçe

    Türkçe

    2015

    Diş HekimliğiGazi Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. LEVENT NALBANT

  3. Plastik deformasyon ile cıvata üretiminde vida diş profilinde sertlik değişimine neden olan parametrelerin araştırılması

    Investigation of the parameters causing hardness change in screw thread profile in bolt production with plastic deformation

    HALİL İBRAHİM KÜÇÜKÖZEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Makine MühendisliğiPamukkale Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ RECEP YURTSEVEN

  4. HII çelik levhasının kaynak kabiliyetine soğuk plastik deformasyon miktarının etkisi

    Effect of cold working rate on the weldability of HII steel plate

    REMZİ KANBURELOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    2000

    Eğitim ve ÖğretimGazi Üniversitesi

    Metal Eğitimi Ana Bilim Dalı

    YRD. DOÇ. DR. YUSUF ÖZÇATALBAŞ

  5. Aşırı plastik deformasyon uygulanmış saf titanyum üzerinde hidroksiapatit oluşturulması ve elektrokimyasal davranışı

    Hydroxyapatite formation on pure titanium produced by severe plastic deformation and investigation of electrochemical behaviour

    İLYAS HACISALİHOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    2011

    Makine MühendisliğiAtatürk Üniversitesi

    Makine Mühendisliği Bölümü

    PROF. DR. AKGÜN ALSARAN