CAD/CAM ile üretilen PMMA esaslı protez kaide materyaline uygulanan farklı yüzey işlemlerinin tamir bağlanma dayanımı üzerine etkisi
The effect of different surface tra-eatments applied to PMMA based denture base material produced with CAD/CAM on repair bond strenght
- Tez No: 801996
- Danışmanlar: PROF. DR. GÜLFEM ERGÜN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental materyaller, Dental protez-implant destekli, Dental protezler, Dental restorasyon, Dental stres analizi, Polietilmetakrilat, Takma diş tabanları, Dental materials, Dental prosthesis-implant supported, Dental prosthesis, Dental restoration, Dental stress analysis, Polyethylmethacrylate, Denture bases
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Polimetil metakrilat (PMMA), diş hekimliğinde yaygın olarak kullanılan protez kaide materyalidir. CAD/CAM (Bilgisayar destekli tasarım/Bilgisayar destekli üretim) ile üretilen PMMA materyali yüksek sıcaklık ve basınç altında enjeksiyon yöntemiyle elde edilerek, polimerizasyonu sağlanmaktadır. Bu çalışmanın amacı, PMMA materyaline uygulanan farklı yüzey işlemlerinin, bazı tamir materyallerinin bağlanma dayanımı üzerine etkilerini değerlendirmektir. Bu amaçla, pembe PMMA disklerden CAD/CAM yardımıyla 16x16x2 mm boyutunda toplam 320 adet, beyaz PMMA disklerden ise, 12x12x3 mm boyutunda toplam 80 adet test örneği elde edilmiştir. Pembe PMMA disklerden elde edilen test örnekleri rastgele 4 gruba ayrılarak farklı yüzey işlemleri uygulanmıştır. [Grup A: Yüzey, Al2O3 partikülleri ile kumlama cihazında kumlanarak pürüzlendirilmiştir (n:80). Grup B: Yüzey frez ile pürüzlendirilmiştir (n:80). Grup C: Yüzeye, %4'lük hidroflorik asit uygulanmıştır (n:80). Grup D: Herhangi bir yüzey pürüzlendirme işlemi yapılmamıştır. (Kontrol grubu n:80).] Test örneklerinin yüzey pürüzlülük değerleri profilometre cihazında incelenmiştir. Yüzey işlemi uygulanmış her bir ana grup kendi içerisinde 4 farklı alt gruba ayrılarak; kimyasal olarak polimerize olan akrilik rezin (n:20), ısı ile polimerize olan akrilik rezin (n:20), dişeti kompoziti (n:20) ve CAD/CAM ile üretilen dişlerin oluşturulmasında kullanılan beyaz PMMA (n:20) ile tamir işlemleri uygulanmıştır. Tamir işlemleri uygulama sonrası her bir alt gruptaki test örneklerinin yarısı (n:10) termal döngü cihazı kullanılarak yaşlandırma işlemine tabii tutulmuştur. Tüm test örneklerinin makaslama bağlanma dayanımı ölçümü, Universal test cihazı kullanılarak gerçekleştirilmiştir. Tüm test örnekleri arasında en yüksek yüzey pürüzlülük değerini kumlama grubu göstermiştir (p<0.001). Kumlama yüzey işlemi sonrasında ısı ile polimerize akrilik rezin en yüksek bağlanma dayanımını sergilemiştir. Yüzey işlemi uygulanmamış dişeti kompozitinde ise en düşük bağlanma dayanımı değerleri gözlemlenmiştir. Termal yaşlandırma tüm test gruplarında bağlanma dayanımı değerlerini azaltmıştır (p<0.001). Tamir materyalleri arasında en iyi bağlanma ısı ile polimerize akrilik rezin ile sağlanmıştır.
Özet (Çeviri)
Polymethyl methacrylate (PMMA) is a widely used denture base material. PMMA material produced with CAD / CAM (Computer-Aided Design / Computer-Aided Production) is obtained by injection method under high temperature and pressure, and its polymerization is provided. This study aims to evaluate the effects of different surface treatments applied to PMMA material on the bond strength of some repair materials. For this purpose, a total of 320 test specimens of 16x16x2 mm were obtained from pink PMMA discs with the help of CAD/CAM, and a total of 80 test specimens of 12x12x3 mm in size from white PMMA discs. The test samples obtained from pink PMMA discs were randomly divided into four Groups, and different surface treatments were applied. [Group A: The surface was roughened by sandblasting with Al2O3 particles (n:80). Group B: The surface is roughened with a bur (n:80). Group C: 4% hydrofluoric acid was applied to the surface (n:80). Group D: No surface roughening has been done. (Control Group n:80).] The surface roughness values of the test samples were examined in the profilometer device. Each test Group with surface treatment is divided into four different subgroups; Repair processes with chemically polymerized acrylic resin (n:20), heat-cured acrylic resin (n:20), gingival composite (n:20) and white PMMA (n:20) used for the creation of teeth produced with CAD/CAM has been applied. After the repair processes, half of the test samples (n:10) in each subgroup were aged using a thermal cycler. Shear bond strength measurement of all test specimens was performed using the Universal tester. The sandblasting Group showed the highest surface roughness value among all test samples (p<0.001). After the sandblasting surface treatment, the heat-cured acrylic resin exhibited the highest bond strength. The lowest tear strength values were observed in the untreated gingival composite. Thermal ageing decreased bond strength values in all test Groups (p<0.001). Ideal bonding between repair materials was achieved with heat-cured acrylic resin.
Benzer Tezler
- Yapay dişler üzerine uygulanan farklı yüzey işlemlerinin çeşitli yöntemlerle üretilen kaide materyallerine olan bağlanma dayanımının incelenmesi
Investigation of the bond strength of different surface treatments applied to artificial teeth to denture base materials fabricated by different methods
FATMA CANAN GÜVEN
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiSivas Cumhuriyet ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. FAİK TUĞUT
- Farklı yöntemlerle üretilen tam protez kaide materyalinin mekanik ve fiziksel özelliklerinin değerlendirilmesi
Evaluation of the mechanical and physical properties of complete denture base materials produced by different methods
NARMIN ALIYEVA
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SERDAR POLAT
- Farklı yöntemlerle üretilen geçici sabit restoratif materyallerin renk stabilitesinin değerlendirilmesi
Evaluation of color stability of temporary fixed restorative materials produced by different methods
ŞEYMANUR ECE YAŞAR
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. GÜLFEM ERGÜN
- Silikon esaslı yumuşak astar materyallerinin CAD/CAM ile üretilen kaide materyallerine bağlantısına farklı yüzey işlemlerinin etkisi
Effect of different surface treatments on the bonding of silicone-based soft li̇ni̇ng materials to base materials manufactured with CAD/CAM
SİNAN TEVKİR
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiOrdu ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. AYÇA TULGA
- CAD/CAM sistemi ile üretilen hibrit abutment destekli anterior restorasyonda kemik rezorpsiyon riskinin ve stres dağılımının sonlu elamanlar analizi ile incelenmesi
Investigation of bone resorption risk and stress distribution in hybrid abutment supported anterior restoration produced with CAD/CAM system by finite element analysis
CİHAN AKDOĞAN
Doktora
Türkçe
2024
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. HATİCE ÖZDEMİR