Farklı protez temizleme solüsyonlarının farklı tekniklerle üretilen akrilik kaide materyalleri ile yapay dişlerin bağlantısına etkisi
The effect of different cleaning solutions on the bonding strength of artificial teeth with acrylic base produced with different techniques
- Tez No: 803988
- Danışmanlar: PROF. DR. DOĞU ÖMÜR DEDE
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Akrilik Rezin, CAD/CAM, Eklemeli Üretim, Eksiltmeli Üretim, Makaslama Bağlantı Dayanımı, Yapay Diş, Akrilik reçineler, Dental bonding, Dental protezler, Dental stres analizi, Dental çimentolar, Katmanlı üretim, Protezler ve implantlar, Takma diş tabanları, Takma dişler, Çözeltiler, Acrylic Resin, Additive Manufacturing, Artificial Teeth, CAD/CAM, Shear Bond Strength, Subtractive Manufacturing, Acrylic resins, Dental bonding, Dental prosthesis, Dental stress analysis, Dental cements, Prostheses and implants, Denture bases, Dentures, Solutions
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Ordu Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu tez çalışmasının amacı; farklı üretim yöntemleriyle elde edilmiş protez kaide materyallerinin ve yapay dişlerin, farklı içerikli protez temizleme solüsyonlarına daldırıldıktan sonraki makaslama bağlanma dayanımlarının (MBD) değerlendirilmesidir. Gereç ve Yöntem: Konvansiyonel, CAD/CAM eksiltmeli ve CAD/CAM eklemeli üretim yöntemleri kullanılarak toplamda 150 adet kaide ve diş örneği elde edilmiştir (n=50). Örnekler, daldırılan temizleme solüsyon gruplarına göre; Distile su (Ds), Corega (Cor), Aktident (Akti), Curaprox (Cur) ve Sodyum hipoklorit (Hipo) olmak üzere göre beş alt gruba ayrılmıştır (n=10). Tüm grupların 180 günlük daldırma periyodu tamamlandıktan sonra örneklere üniversal test cihazı ile 1 mm / dk kafa hızında MBD testi uygulanmıştır. MBD testi değerleri megapaskal (MPa) olarak kaydedilmiştir. Elde edilen veriler iki yönlü varyans analizi (ANOVA) ve Bonferroni Çoklu Karşılaştırma Testi ile istatistiksel olarak analiz edilmiştir. Bulgular: İki yönlü varyans analizi (ANOVA) sonuçlarına göre üretim yöntemi ve temizleme solüsyonu içeriğinin MBD değerleri üzerinde istatistiksel olarak anlamlı derecede etkili olduğu görülmüştür (P<,001). Üretim yöntemi grupları bağlantı değerlerine göre karşılaştırıldığında en yüksek değerler eklemeli üretim grubunda distile su alt grubunda görülürken (19,45 ± 1,39 MPa); en düşük değerler eksiltmeli üretim grubunda distile su alt grubunda (8,70 ± 0,70 MPa) görülmüştür. Solüsyonların etkileri karşılaştırıldığında, en yüksek değerler Akti (18,51 ± 0,81 MPa) ve Cur (18,11 ± 0,92 MPa) solüsyon gruplarında eklemeli üretim yönteminde olduğu görülürken; en düşük değer sodyum hipoklorit solüsyon grubunda (4,83 ± 0,50 MPa) eksiltmeli üretim yönteminde olduğu görülmüştür (P<,05). Sonuç: Üretim yöntemi ve temizleme solüsyonu içeriği kaide rezini-yapay diş arasındaki bağlantıyı etkilemiştir. Kimyasal içerikli temizleme solüsyonu kaide rezini ve yapay dişin üretim yönteminde kullanılacak materyale göre seçilmelidir.
Özet (Çeviri)
Aim: The aim of the present study is to evaluate the shear bond strength (SBS) of denture base materials and artificial teeth obtained by different manufacturing methods after immersion in a denture cleaning solutions with different contents. Material and Method: A total of 150 bases and artificial tooth samples were prepared using conventional, subtractive and additive manufacturing methods (n=50). Samples were divided into five subgroups according to the immersed cleaning solution groups; Distilled water (Ds), Corega (Cor), Aktident (Akti), Curaprox (Cur), and Sodium hypochlorite (Hipo) (n=10). After the 180-day immersion period of all groups was completed, the SBS test was applied to the samples with a universal test device at a crosshead speed of 1 mm/min. Shear bond strength data were recorded as megapascal (MPa) and statistically analyzed with a two-way ANOVA and the Bonferroni Multiple Comparison Test. Results: According to the results of the two-way analysis of variance (ANOVA), the manufacturing method and the content of the cleaning solution were found to be a significant effect on SBS values (P<.001). When the manufacturing method groups are compared according to SBS values, the highest values were observed in the additive manufacturing groups distilled water subgroup (19.45 ± 1.39 MPa); the lowest values were observed in the subtractive manufacturing groups distilled water subgroup (8.70 ± 0.70 MPa). When the effects of the solutions were compared, the highest values were observed in the Akti (18.51 ± 0.81 MPa) and Cur (18.11 ± 0.92 MPa) solution groups in the additive manufacturing method; the lowest value was observed in the Hipo solution group (4.83 ± 0.50 MPa) in the subtractive manufacturing method (P<.05). Conclusion: The manufacturing method and cleaning solution content affected the SBS between the base resin and artificial tooth. The chemical-containing cleaning solution should be selected according to the base resin and the artificial tooth material to be used in the manufacturing method.
Benzer Tezler
- Protez temizleyicilerinin farklı tekniklerle üretilen protez kaide materyallerinin renk stabilitesi üzerine etkisi
The effect of denture cleansers on color stability of denture base materials produced by different techniques
YONCA ÖZDEMİR
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiSüleyman Demirel ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. IŞIN KÜRKÇÜOĞLU
- Protez temizleme solüsyonlarının farklı polisaj yöntemleri uygulanan kaide materyallerinin yüzey özelliklerine etkilerinin incelenmesi
Investigation of the effects of prosthesis cleaning solutions on the surface properties of base materials applied with different poli̇shi̇ng methods
İLKAY BALTACI
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiSivas Cumhuriyet ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. GİRAY BOLAYIR
- Dental implant protetik üst yapı ataşman tutuculuğuna farklı protez temizleme solüsyonlarının etkisinin in vitro incelenmesi
In vitro evaluation of the effect of different denture cleaning solutions on the retention of the dental implant prosthetic superstructure attachment
ASLI KARAPINAR
Doktora
Türkçe
2020
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. TAYFUN BİLGİN
- Temporomandibular eklem rahatsızlıkları için farklı yöntemlerle üretilen oklüzal splint materyallerine uygulanan yüzey işlemleri sonrası oluşan hacimsel kaybın in-vitro olarak değerlendirilmesi
In-vitro evaluation of the volumetric loss after surface treatment of occlusal splint materials produced by different methods for temporomandibular joint disorders
AYŞENUR KARA
Doktora
Türkçe
2024
Diş HekimliğiSağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SİMEL AYYILDIZ
- Çeşitli yüzey pürüzlendirme işlemleri ve temizleme ajanlarının PEKK-kompozit yapısının bağlanma dayanımı ve rengi üzerine etkisi
The effect of different surface treatment and denture cleansers on the bond strenght and color stability of PEKK-composite structure
KÜBRA ERDEM
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiBezm-İ Alem Vakıf ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ÖZGÜN YUSUF ÖZYILMAZ