S460MC ince taneli yapı çeliklerinin MAG kaynak yöntemi ile birleştirilmesinde akım ve koruyucu gaz karışımının mikro yapı ve mekanik özelliklere etkisinin incelenmesi

Investigation of the effect of curent and protective gas mixture on microstructural and mechanical properties in joining S460MC fine grain structural steels with MAG welding method

  1. Tez No: 821533
  2. Yazar: YASİN KARGIN
  3. Danışmanlar: DOÇ. DR. ERDOĞAN KANCA
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: İskenderun Teknik Üniversitesi
  10. Enstitü: Lisansüstü Eğitim Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 74

Özet

Bu çalışmada yüksek mukavemetli ince taneli bir çelik olan S460MC çelik plakalar iki farklı koruyucu gaz kompozisyonu ve iki farklı kaynak akımı değerlerinde, kaynak hızı sabit tutulup MAG (Metal Aktif Gaz) kaynak yöntemiyle alın-alına kaynak edilmiştir. Kaynak işleminde kullanılan akım değerleri 140 Amper(A) ve 210 Amperdir. Kullanılan gaz karışımları ise %82 Ar + %18 CO2 ve %92 Ar + %8 CO2 olarak seçimiştir.140 Amper akım değerinde iki gaz karışımı ile de ayrı ayrı kaynak işlemi yapılmış olup 210 Amper akım değerinde de yine bu iki gaz karışımı ile ayrı ayrı kaynak yapılmıştır. Bu kaynak işlemleri esnasında kaynak hızı ve diğer parametreler sabit tutulmuş ve kaynağın kök kısmında sarkma veya kötü bir form oluşmaması amacıyla seramik altlık kullanılmıştır. Kaynak sonrasında numunelere ilk olarak görsel muayene ve sonrasında çekme testi, eğme testi, sertlik testi ve makro-mikro analizler uygulanmıştır. Böylece S460M çeliğinin kaynaklanmasında hem kaynak akımındaki değişimin hem de karışım gazı olarak Argon gazı ile (Ar) beraber kullanılan CO2 gazı oranındaki değişimin mikro yapı ve mekanik özelliklere etkisi incelenmiştir. Yapılan testler sonucunda görsel muayene ve makro yapı incelemelerinde artan CO2 gazı oranı ve akım ile beraber daha geniş bir kaynak metali (KM) görülmüştür. Mikro yap incelemelerinde ısıdan etkilenmiş bölge (IEB) CO2 oranının ve akım değerinin artması ile tane irileşmesi görülmüş ayrıca perlit(P) ve ferrit(F) fazından oluşan yapıda martensit(M) oluşumu da gözlemlenmiştir. Sertlik ölçüm sonuçlarına bakıldığında akım ve CO2 oranının artması ile beraber ısı girdisinin artması ve daha yavaş soğuma nedeniyle IEB ve KM bölgelerinde sertlik değerlerinde düşme görülmüştür. Çekme testi sonuçlarına bakıldığında ise kaynak akımındaki ve CO2 miktarındaki artış akma ve çekme dayanımlarını düşürmüştür. Son olarak eğme testleri sonucuna göre kaynaklı birleştirmelerde herhangi bir çatlak, yırtılma, mikro gözenek veya kalıntıya rastlanmamıştır. 180º hem kep hem de kök eğme testlerinin sorunsuz bir şekilde tamamlandığı görülmüştür.

Özet (Çeviri)

In this study, S460M steel plates, a high strength fine grained steel, were welded face-to-face with two different shielding gas compositions and two different welding current values, keeping the welding speed constant, with MAG (Metal Active Gas) welding method. The current values used in the welding process are 140 Amperes (A) and 210 Amperes. The gas mixtures used were 82% Ar + 18% CO2 and 92% Ar + 8% CO2. Welding was done separately with two gas mixtures at 140 Ampere current value, and also with these two gas mixtures at 210 Ampere current value.During these welding processes, the welding speed and other parameters were kept constant and a ceramic backing plate was used in order to prevent sagging or a bad form in the root of the weld. After welding, first visual inspection and then tensile test, bending test, hardness test and macro-micro analysis were applied to the samples. Thus, the effect of both the change in welding current and the change in the ratio of CO2 gas used together with Argon gas (Ar) gas as the mixing gas, on the microstructure and mechanical properties of S460M steel were investigated.As a result of the tests performed, a wider weld metal (WM) was observed with the increased CO2 gas rate and flow in visual inspection and macro structure examinations. In the microstructure investigations, grain coarsening was observed with the increase of the CO2 ratio and the current value in the heat-affected zone (HAZ). When the hardness measurement results are examined, it was observed that the hardness values decreased in the HAZ and WM regions due to the increase in the heat input and slower cooling with the increase in the current and CO2 ratio. When the tensile test results were examined, ıt was observed that increase in the welding current and the amount of CO2 decreased the yield and tensile strengths. Finally, according to the results of the bending tests, no cracks, tears, micropores or residues were found in the welded joints. It has been observed that both the cap and root bending tests at 180º were completed without any problems.

Benzer Tezler

  1. Yüksek mukavemetli çeliklerde çok pasolu kaynağının mekanik ve mikroyapı özelliklerine etkisi

    Effects of multipass welding on mechanical and micro structure features in hight strength steels

    İSMAİL KALKAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Metalurji MühendisliğiDüzce Üniversitesi

    İmalat Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ SERKAN APAY

  2. İnce cidarlı CM22NBK malzemesi için sıvayarak delik delme (flowdrill) ve alternatif malzeme analizi

    Tapping and alternative material analyzing of thin wall CM22NBK material flowdrill process

    DİLEK SÖZÜGÜZEL

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    Makine MühendisliğiGazi Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. NİHAT GEMALMAYAN

  3. Soğuk şekillendirmeye uygun yüksek mukavemetli çelik malzeme ile LPG tüpü imalatında tozaltı kaynak parametrelerinin dikiş kalitesine etkilerinin incelenmesi

    Investigation of the effects of submerged arc welding parameters on the weld bead quality in manufacturing of LPG cylinder to be manufactured from high strength and cold formable steel

    UĞUR NUHOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiYıldız Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. TOLGA MERT

    DOÇ. DR. MUSTAFA TÜMER

  4. Alevle doğrultma işlemi yapılırken s460mc çelikleri üzerindeki mukavemet özelliklerinin değişimlerinin incelenmesi

    Investigation of changes in strength properti̇es of s460mc steels during straightening process with flame

    YUSUF EVRİM GÖKALP

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Mühendislik BilimleriSakarya Uygulamalı Bilimler Üniversitesi

    İmalat Mühendisliği Ana Bilim Dalı

    PROF. DR. SALİM ASLANLAR

  5. Gazaltı kaynağı ile birleştirilen farklı özellikteki çeliklerin mekanik özelliklerinin incelenmesi

    Research of mechanical properties of different steels combined with gas metal arc welding

    YİĞİT OKUROĞULLARI

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiBursa Uludağ Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. HAKAN AYDIN