Işkın bitkisinden karbon nokta yapıların yeşil sentezi ve Schottky diyot fabrikasyonu

Green synthesis of carbon dot structures from Rheum ribes plant and Schottky diode fabrication

  1. Tez No: 828048
  2. Yazar: MUHAMMED TAHA DURMUŞ
  3. Danışmanlar: DOÇ. DR. EBRU BOZKURT
  4. Tez Türü: Yüksek Lisans
  5. Konular: Elektrik ve Elektronik Mühendisliği, Electrical and Electronics Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2023
  8. Dil: Türkçe
  9. Üniversite: Atatürk Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Nanobilim ve Nanomühendislik Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 61

Özet

Amaç: Bu tez çalışmasında, doğal bir materyal olan ışkın bitkisi (Rheum Ribes) ilk defa kullanılarak hidrotermal sentez yöntemi ile tek aşamada yeni karbon nokta yapılar (CDs) sentezlemek ve tamamen doğal bir materyal ile elde edilen yeni CDs kullanılarak diyot fabrikasyonu alanındaki çalışmalara katkıda bulunmak amaçlanmıştır. Yöntem: CDs, literatürde yaygın olarak tercih edilen hidrotermal sentez yöntemi ile elde edilmiştir. Elde edilen bu karbon nokta yapıların morfolojisi ve boyutları için TEM, Zetasizer cihazları kullanılmış olup, yapısal karakterizasyonları için XRD, XPS, FT-IR Spektrofotometresi, Mikro Raman Spektroskopisi cihazları kullanılmıştır. CDs'ın optiksel karakterizasyonu ise absorpsiyon ve durgun hal floresans ölçümleri ile yapılmıştır. Çalışmanın ikinci kısmında silisyum substrat üzerine CDs stoğundan yaklaşık 50 µl damlatılarak buharlaştırma yoluyla CDs ince filmi oluşturulmuştur. Son aşamada oluşturulan CDs film üzerine gölge maske tekniği ile altın buharlaştırılarak diyot yapısı elde edilmiş ve bu diyotun akım-voltaj karakteristiği incelenmiştir. Bulgular: Tamamen doğal ürün olan ışkın bitkisinden hidrotermal sentez yöntemi ile CDs tek aşamada sentezlenmiş ve bu yeni doğal ürün temelli yarıiletken materyalin elektronik alanında önemli bir yeri olan Schottky diyot fabrikasyonunda kullanılabileceği tespit edilmiştir. Sonuçlar: Işkın bitkisinden hidrotermal sentez yöntemi ile tek aşamada yeni karbon nokta yapılar (CDs) başarı ile sentezlenmiştir. Sentezlenen CDs'ın ortalama 1,5 nm boyutlarında küresel, negatif yüzey yüküne sahip ve yapısında %73,3 , %24,0 ve %2,7 oranlarında C, O ve N elementlerinin bulunduğu tespit edilmiştir. Bununla birlikte bu CDs'ın yaklaşık 394 nm'de floresans özelliğe sahip olduğu belirlenmiştir. Tüm karakterizasyonları yapılan CDs, schottky diyot tasarımında yarıiletken materyal olarak kullanılmış ve Schottky diyodun oluşumunu gösteren doğrusal olmayan bir doğrultma davranışı sergilediği gözlenmiştir.

Özet (Çeviri)

Purpose: In this thesis, it is aimed to synthesize new carbon dot structures (CDs) in a single step by using a natural material Rheum Ribes for the first time, and to contribute to the studies in the field of diode fabrication by using new CDs obtained with a completely natural material. Method: CDs were obtained by hydrothermal synthesis method, which is widely preferred in the literature. TEM and Zetasizer devices were used for the morphology and sizes of these carbon dot structures, and XRD, XPS, FT-IR Spectrophotometer and Micro Raman Spectroscopy devices were used for their structural characterization. Optical characterization of CDs was done by absorption and steady-state fluorescence measurements. In the second part of the study, approximately 50 µl of CDs stock was dropped onto the silicon substrate and CDs thin film was formed by evaporation. The diode structure was obtained by evaporating gold with shadow mask technique on the CDs film formed in the last stage, and the current-voltage characteristic of this diode was examined. Findings: CDs were synthesized in a single step by hydrothermal synthesis method from the completely natural product of Rheum Ribes and it was determined that this new natural product-based semiconductor material could be used in Schottky diode fabrication, which has an important place in the field of electronics. Results: New carbon dot structures (CDs) were successfully synthesized in a single step by hydrothermal synthesis method from Rheum Ribes. It has been determined that the synthesized CDs are spherical with an average 1.5 nm size, have a negative surface charge and contain 73.3%, 24.0% and 2.7% C, O and N elements in their structure. However, these CDs were determined to have fluorescence at approximately 394 nm. The CDs were used as semiconductor material in the schottky diode design and it was observed that they exhibited a nonlinear rectification behavior indicating the formation of the Schottky diode.

Benzer Tezler

  1. Fotokatalitik ilaç giderimi için Rheum ribes (Işkın) bitkisinden hazırlanmış azot katkılı karbon kuantum noktalar (N-CQDS) ile dekore edilmiş ZnO ve TiO2 heteroeklemlerin tasarımı ve performans değerlendirmesi

    Design and performance evaluation of ZnO and TiO2 heterojunctions decorated with nitrogen doped carbon quantum dots (N-CQDS) prepared from rheum ribes (Iskın) plant for photocatalytic pharmaceutical removal

    CANAN KARACA

    Doktora

    Türkçe

    Türkçe

    2023

    KimyaAtatürk Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. SEMRA KARACA

  2. Rumex crispus L. (evelik) bitkisinden hazırlanan azot katkılı karbon kuantum noktalarla (N-CQDS) dekore edilen TiO2 ve ZnO heteroeklemlerinin mor ötesi ve görünür bölgede fotokatalitik ilaç oksidasyonunda performanslarının değerlendirilmesi

    Evaluation of the performance of TiO2 and ZnO heterojunctions decorated with nitrogendoped carbon quantum dots (N-CQDS) prepared from Rumex crispus L. (evelik) plant inphotocatalytic pharmaceutical oxidation in the ultraviolet and visible regions

    MELİKE KARACA

    Doktora

    Türkçe

    Türkçe

    2023

    KimyaAtatürk Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. SEMRA KARACA

  3. Işkın bitkisinden (Rheum ribes) elde edilen sulu ekstraktların mikroenkapsülasyonu

    Aqueous extracts obtained from rhubarb plant (Rheum ribes) microencapsulation

    SEDA DEMİRBAĞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Gıda Mühendisliğiİnönü Üniversitesi

    Gıda Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT YILMAZTEKİN

  4. Yukarı Fırat havzasında yetişen kenger (Gundelia tournefortii L.), güllük (Eremurus spectabilis M. Bieb.) ve ışkın (Rheum ribes L.) bitkilerindeki polifenollerin ve bazı metallerin tayini

    Determination of phenolic compounds and metals in the kenger (Gundelia tournefortii L.), gulluk (Eremurus tpectabilis M. Bieb.)and iskin (Rheum ribes L.) of the plant grown in upper euphrates basin

    SERHAT YILDIZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    KimyaFırat Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. ALİ ÖLÇÜCÜ

  5. Phylotacca amerıcana bitkisinden elde edilen pigmentlerin boya duyarlı güneş pillerinde kullanımlarının incelenmesi

    Investigation of pigments extracted from Phytolacca americana plant for applications in dye-sensitized solar cells

    ÖMER FARUK TUTAR

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    KimyaSakarya Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. İLKAY ŞİŞMAN