Farklı çimento ve kalsiyum sülfat numunelerinin kendinden yayılan şapların fiziksel ve kimyasal özelliklerine etkisi

The effect of different cement and calcium sulphate samples on the physical and chemical properties of self leveling screeds

PDF İndir

  1. Tez No: 833175
  2. Yazar: YASEMİN KAREL
  3. Danışmanlar: PROF. DR. ÖMER METE KOÇKAR, DR. ÖĞR. ÜYESİ EVREN ARIÖZ
  4. Tez Türü: Doktora
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2023
  8. Dil: Türkçe
  9. Üniversite: Eskişehir Teknik Üniversitesi
  10. Enstitü: Lisansüstü Eğitim Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Proses ve Reaktör Tasarımı Bilim Dalı
  13. Sayfa Sayısı: 99

Özet

Türkiye'de hızla büyüyen inşaat sektöründe yapı verimliliğine verilen önem giderek artmaktadır. Kendinden yayılan şaplar (SLM) ve betonlar bu amaç için geliştirilmiştir. Bu çalışmada SLM'lerde kullanılan Portland çimento (OPC), kalsiyum alüminalı çimento (CAC) ve kalsiyum sülfat kaynağından (CŚ) oluşan tekli, ikili ve üçlü bağlayıcı sistemler referans alınmıştır. Bu sistemlerin farklı kompozisyonlarının harcın fiziksel ve kimyasal yapısına etkisi araştırılmıştır. Sabit su/bağlayıcı oranında taze harçların priz başlangıç ve bitiş süreleri test edilmiştir. Farklı kür sürelerindeki eğilme ve basınç dayanımları, büzülme/genleşme oranları ölçülmüştür. Aynı zamanda X-ışını floresans spektrofotometresi (XRF) ve Taramalı Elektron Mikroskopu (SEM) bulgularından harç sistemlerinin hidratasyon mekanizmaları anlaşılmaya çalışılmıştır. Elde edilen sonuçlar incelendiğinde, %80 OPC - %20 (CAC) içeren R2 numunesinin 0,4 su/bağlayıcı oranında, hidratasyonunda priz başlangıç süresini %100 OPC içeren R1 numunesine göre 240 dakikadan 15 dakikaya hızlandırdığı tespit edilmiştir. Priz süresindeki bu etkiye rağmen R1 harcının 1 günlük mukavemetinin 18,98 MPa'dan 13,43 MPa'ya düşmesine neden olduğu görülmüştür. Hızlı etrenjit oluşumundan kaynaklanan olumsuz etkiyi minimize etmek için eklenen CŚ kaynaklarından anhidritin düşük oranını içeren A1 numunesinde erken mukavemette 16,12 MPa ile en iyi etkiyi yaptığı belirlenmiştir. 28 günlük geç mukavemette ise düşük miktarda dihidrat içeren D1 numunesinin en iyi sonucu verdiği tespit edilmiştir. 44,28 MPa olarak ölçülen basınç mukavemeti değeri %100 OPC içeren R1 numunesinde 48,82 MPa olarak bulunmuştur. Hemihidratın CAC çimentosundan kaynaklanan priz süresindeki kısalmaya bir etkisi olmamıştır. Tüm denemeler karşılaştırıldığında, en yüksek büzülme/genleşme değeri %2,4 oranı ile dihidratın yüksek oranda kullanıldığı D2 numunesinde görülmüştür.

Özet (Çeviri)

In the rapidly growing construction sector in Turkey, the importance given to building efficiency is increasing. Self-leveling screeds (SLM) and concretes were developed for this purpose. In this study, single, double and triple binder systems consisting of Portland cement (OPC), calcium aluminate cement (CAC) and calcium sulphate source (CŚ), which are used in SLM formulations, are taken referance. The effects of different compositions of these systems on the physical and chemical structure of the mortar were investigated. Set starting and ending times of fresh mortars at constant water/binder ratio were tested. Bending and compressive strengths, shrinkage/expansion ratios at dfferent curing times were measured. At the same time, hydration mechanisms of mortar systems were tried to be understood from obtained by X-ray flourescence spectrophotometer (XRF) and Scanning Electron Microscope (SEM). According to results obtained, it was determined that R2 sample containing %80 OPC and %20 CAC (R2) at a water/binder ratio of 0,4 accelerated the setting start times in hydration process from 240 minute to 15 minute in hydration compared to R1 specimen containing %100 Portland Cement. Despite of this effect, it was observed that the compressive strength of the R1 sample decreased from 18,98 MPa to 13,43 MPa after 1 day. In order to minimize this negative effect caused by rapid etrengite formation, it was determined that the low ratio of anhydrite (A1), one of the CŚ sources added, had the best effect with 16,12 MPa in early strength. D1 sample containing low amount of dihydrate gave the best result after 28 days. The compressive strength of specimen of D1 was 44,28 MPa, while the compressive strength of specimen of R1 containing % OPC was measured 48,82 MPa. The hemihydrate had no effect on the shortening of the setting time caused by the CAC cement. When all trials were compared, the highest shrinkage/expansion value of %2,4 was determined in D2 sample in which dihydrate is used at high ratio.

Benzer Tezler

  1. Tez No

    244762

    Kendiliğinden yerleşen betonun taze haldeki temel özellikleri ve sülfat direnci üzerine iri agrega çeşidi ve çimento tipinin etkisi

    Effect of coarse aggregate and cement types on the main characteristics and sulphate resistance of self compacting concrete

    MEŞKÜRE AKARSU

    Yüksek Lisans

    Türkçe

    Türkçe

    2009

    İnşaat MühendisliğiAtatürk Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. REMZİ ŞAHİN

  2. Tez No

    766784

    Adana Havzası çimento esaslı malzemelerin dış sülfat atağına karşı duyarlılık değerlendirmeleri

    Susceptibility assessments of cement-based materials to external sulphate attack in Adana Basin

    MOHAMMED ZAINEL QADER QADER

    Doktora

    İngilizce

    İngilizce

    2022

    Jeoloji MühendisliğiÇukurova Üniversitesi

    Jeoloji Mühendisliği Ana Bilim Dalı

    PROF. DR. TOLGA ÇAN

  3. Tez No

    885956

    Korozyon inhibitörlerinin çimentolu harçlarda agresif ortamlara karşı gösterdiği etkinin araştırılması

    Investigation of the effect of corrosion inhibitors in cementitious mortars against aggressive environments

    İLKAY KARA

    Doktora

    Türkçe

    Türkçe

    2024

    İnşaat MühendisliğiEskişehir Osmangazi Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. İLKER BEKİR TOPÇU

  4. Tez No

    668903

    Mechanical and durability assessment of geopolymer concrete containing elasto-plastic fibers and recycled aggregate

    Elasto-plastik lif ve geri dönüşümlü agrega içeren jeopolimer betonun mekanik ve dayanıklılık özelliklerinin değerlendirmesi

    ABDELAZIZ YOUSUF MOHAMED

    Yüksek Lisans

    İngilizce

    İngilizce

    2021

    İnşaat MühendisliğiYıldız Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ORHAN CANPOLAT

    DR. ÖĞR. ÜYESİ MUKHALLAD ALMASHHADANI

  5. Tez No

    152389

    Çimentonun fiziksel özelliklerinin üretilen standart harcın mukavemetine etkilerinin araştırılması

    Properties of portland cement

    GÜLRU ÖZDÖL

    Yüksek Lisans

    Türkçe

    Türkçe

    2004

    Mimarlıkİstanbul Teknik Üniversitesi

    Mimarlık Ana Bilim Dalı

    PROF. DR. EROL GÜRDAL

Geri Dön