Östenitik paslanmaz çelik ve bakır çiftinin difüzyon kaynağı ile birleştirilmesinede kaynak parametrelerinin birleşmeye etkisi
The Effect of welding parameters on joining of stainless steel with copper by diffusion welding
- Tez No: 83951
- Danışmanlar: DOÇ. DR. HALİS ÇELİK
- Tez Türü: Doktora
- Konular: Eğitim ve Öğretim, Metalurji Mühendisliği, Education and Training, Metallurgical Engineering
- Anahtar Kelimeler: Difüzyon Kaynağı, Katı Hal Kaynağı, Elektriksel İletkenlik, Diffusion Welding, Solid State Welding, and Electrical Conductivity
- Yıl: 1999
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 121
Özet
HI ÖZET Doktora Tezi ÖSTENİTİK PASLANMAZ ÇELİK VE BAKIR ÇİFTİNİN DİFÜZYON KAYNAĞI İLE BİRLEŞTİRİLMESİNDE KAYNAK PARAMETRELERİNİN BİRLEŞMEYE ETKİSİ. Osman YILMAZ Fırat Üniversitesi Fen Bilimleri Enstitüsü Metal Eğitimi Anabilim Dalı 1999 Sayfa: 109 Bu çalışmada, östenitik paslanmaz çelik (AISI 304) ve elektrolitik bakırın difüzyon kaynağı ile birleştirilmesinde, kaynak parametrelerinin birleşmeye etkisi incelenmiştir. Yapılan deneyler sonucunda, kaynak parametrelerinin birleşme üzerindeki etkileri incelendiğinde, en uygun difüzyon kaynağının, 800 °C sıcaklık, 30 dakika kaynak süresi ve 1.2 Mpa basınçta gerçekleştiği anlaşılmıştır. Bu kaynaklı birleştirme sonucunda, numunelerin ne oranda kaynak edilebildiğinin anlaşılması amacıyla metalografi ve mekanik testler kullanılmıştır. Metalografik olarak, optik mikroskop ve SEM ile kaynak bölgesi incelenmiş, EDS analizleri yapılarak kaynak çiftinin birleşme bölgesinde, elementlerin difüzyon sonucu konsantrasyon dağılımı ve difüzyon mesafelerini içeren grafikler elde edilmiştir. Bu sonuçlar kullanılarak, kaynak bölgesinde oluşan muhtemel intermetalik fazlar, faz diyagramları yardımıyla belirlenmeye çalışılmıştır. Mekanik olarak İse, sertlik ve çekme testleri uygulanmış,, elde edilen sonuçlarla; kaynak bölgesinde, kaynak parametrelerinin sertlik üzerindeki etkileri ve metal çiftinin mekanik dayanımı tespit edilmeye çalışılmıştır.IV Çalışmanın bir diğer bölümünde, lehimli birleştirme ile bir mukayese yapabilmek amacıyla, difüzyon kaynağı ve sert lehim ile birleştirilen numuneler arasındaki elektriksel iletkenlik farkı incelenerek, kaynak ara yüzeyinde oluşan intermetalik fazların iletkenlik üzerindeki etkileri araştırılmıştır. Sonuçta; difüzyon kaynaklı metal çiftin lehimli metal çiftin yerine kullanılabileceği tespit edilmiştir.
Özet (Çeviri)
SUMMARY PhD Thesis THE EFFECT OF WELDING PARAMETERS ON THE JOINING OF STAINLESS STEEL WITH COPPER BY DIFFUSION WELDING Osman YILMAZ Fırat University Graduate School Of Natural and Applied Sciences Department of Metallurgy Education 1999, Page: 109 In this thesis, the effects of welding parameters on the joining of stainless steel to copper by diffusion bonding were searched. Depending on the effect of welding parameters, the best diffusion welding condition is determined as 800 °C temperature, 30 minute time and 1.2 Mpa pressure. At the end of this study, metallographic and mechanical tests were applied to examine the quality of bonding. As metallographic tests, optical microscope and SEM were applied and the distribution of elements present inside this two metal represented by using EDS analysis. Possible intemetallic phases were tried to be detected at welding area by using these results on the phase diagrams. As mechanical tests, hardness and tensile tests were applied. Taking the results into account, the effect of welding parameters on the hardness of welding area and strength of have been tried to be determined. At another section of this study, electrical resistivity of diffusion welded and soldered bimetals measured. Comparisons between these measurements were done. Moreover the effect of intermetalic phases on the electrical resistivity were deduced. Finally, it was seen that diffusion welded bimetal can be used instead of soldered bimetal.
Benzer Tezler
- Paslanmaz çelik ve bakır malzemenin sert lehimleme ile birleşebilirliğinin araştırılması
Researching of joining stainless steel and copper material with brazing
FURKAN ÖZDEMİR
Yüksek Lisans
Türkçe
2023
Metalurji MühendisliğiGazi ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. BEHÇET GÜLENÇ
- Sürtünme kaynağıyla birleştirilmiş paslanmaz çelik ve bakır parçaların kaynak bölgesi özelliklerinin incelenmesi
Investigation of the welding zone properties of stainless steel and copper parts joined with friction welding
ENDER ÇİL
Yüksek Lisans
Türkçe
2009
Makine MühendisliğiTrakya ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. MÜMİN ŞAHİN
- Design of a stainless steel composite bridge according to the eurocodes and cost analysis
Paslanmaz çelik ile kompozit bir köprünün eurocode'a göre tasarımı ve maliyet analizi
TİJEN BAYER
Yüksek Lisans
İngilizce
2014
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. BARLAS ÖZDEN ÇAĞLAYAN
- Elektrokimyasal yöntem ile ergiyik tuz çözeltisi içerisinden MgB2 ince film kaplanması
Plating of MgB2 thin films from molten salts via electrochemi̇cal tecnique
AYKUT GÜNERİ
Yüksek Lisans
Türkçe
2014
Metalurji MühendisliğiYıldız Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. AHMET SAĞIN
- Östenitik (304) ve ferritik (430) paslanmaz çeliklerin bakır aratabaka kullanılarak difüzyon kaynağı ile birleştirilmesi
Joining austenitic (304) and ferritic (430) stainless steels by diffusion welding using copper interlayer
GAMZE TOSUN
Yüksek Lisans
Türkçe
2022
Makine MühendisliğiDicle ÜniversitesiMühendislik Bilimleri Ana Bilim Dalı
DR. ÖĞR. ÜYESİ HALUK KEJANLI