Monolitik CAD-CAM seramiklerinin diş fırçalama simülasyonu sonrası optik ve yüzey özelliklerinin değerlendirilmesi
Evaluation of the optical and surface properties of monolithic CAD-CAM ceramics after tooth brushing simulation
- Tez No: 844726
- Danışmanlar: PROF. DR. MERVE BANKOĞLU GÜNGÖR
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, Dental materyaller, Dental porselen, Diş fırçalama, Optik özellikler, Yüzey özellikleri, CAD/CAM, Dental materials, Dental porcelain, Toothbrushing, Optical properties, Surface properties
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı, monolitik CAD-CAM seramiklerinde diş fırçalama simülasyonu sonrası meydana gelen renk, parlaklık, yüzey pürüzlülüğü ve yüzey topoğrafisi değişimlerini değerlendirmektir. Çalışmada, monolitik zirkonya, lityum disilikat (prekristalize ve kristalize), zirkonya ile güçlendirilmiş lityum silikat (prekristalize ve kristalize), hibrit seramik, lösit ile güçlendirilmiş seramik, feldspatik seramik ve hibrit nanoseramik olmak üzere dokuz farklı materyalden 1,5 mm kalınlığında örnekler hazırlandı (n=10). Mekanik polisaj sonrasında her bir seramik materyalinin renk parametreleri, parlaklık ve yüzey pürüzlülüğü değerleri ölçüldü. Sonrasında örnekler 10000 siklus (1 yıllık simülasyon) ve 50000 (5 yıllık simülasyon) siklus şeklinde iki aşamada fırçalama simülasyonuna tabi tutuldu. Fırçalama simülasyonu sonrasında CIEDE2000 formülü ile renk değişimi (ΔE00) miktarları hesaplandı. Parlaklık ve yüzey pürüzlülüğü değerleri ölçüldü. Veriler istatistik olarak iki yönlü tekrarlı ölçümlü ANOVA ve Bonferroni çoklu karşılaştırma testi ile değerlendirildi. Monolitik zirkonya hariç diğer materyal ve fırçalama simülasyonu gruplarında, renk değişimi değerleri algılanabilirlik eşik değerinin (0,8) altında bulundu. Monolitik zirkonyada ise 10000 fırçalama siklusunda renk değişimi değeri 0,79; 50000 siklus sonrasında renk değişimi değeri 1,09 olarak belirlendi. Monolitik zirkonya hariç diğer materyal ve fırçalama simülasyonu gruplarında, yüzey parlaklığı değerlerinin genel olarak arttığı ancak anlamlı bir fark görülmediği tespit edildi (P>0,05). Monolitik zirkonyada fırçalama simülasyonu sonrası yüzey parlaklığı değerlerinin başlangıca göre anlamlı artış gösterdiği belirlendi (P<0,05). Monolitik zirkonya, prekristalize lityum disilikat, prekristalize ve kristalize zirkonya ile güçlendirilmiş lityum silikat seramik gruplarında ortalama yüzey pürüzlülüğü değerlerinin 10000 ve 50000 fırçalama siklusu sonrasında anlamlı olarak arttığı görüldü (P<0,05). 10000 siklus ve 50000 siklus diş fırçalama simülasyonu sonrası renk, parlaklık, yüzey pürüzlülüğü ve yüzey topoğrafisi değişimleri değerlendirildiğinde, fırçalama simülasyonunun materyallerin yüzey parlaklığı ve yüzey pürüzlülüğü üzerinde etkili olduğu bulundu. Deney gruplarına ait renk değişimi değerlendirildiğinde; sadece materyal faktörünün renk değişimi üzerinde etkili olduğu ve monolitik zirkonyada meydana gelen renk değişim değerinin klinik olarak gözle farkedebilir eşik değerin üzerine çıktığı belirlendi.
Özet (Çeviri)
The aim of this study is to evaluate the changes in color, gloss, surface roughness and surface topography of monolithic CAD-CAM ceramics after tooth brushing simulation. In the study, specimens were prepared in 1.5 mm thickness from nine different materials as monolithic zirconia, lithium disilicate (precrystallized and crystallized), zirconia reinforced lithium silicate (precrystallized and crystallized), hybrid ceramic, leucite reinforced ceramic, feldspathic ceramic and hybrid nanoceramic (n=10). After mechanical polishing, the color parameters, gloss and surface roughness values of each specimen were measured. Then, the specimens were subjected to tooth brushing simulation in two stages as 10000 cycles (1-year) and 50000 (5-year). After the brushing simulation, the color change (ΔE00) values were calculated and the gloss and surface roughness values of the specimens were measured. Data were statistically analyzed with two-way repeated measures of ANOVA and Bonferroni multiple comparison tests. Except monolithic zirconia, the color change values were found to be below the perceptibility threshold (0.8) in the experimental groups. In monolithic zirconia, the color change value was 0.79 after 10000 brushing cycles. After 50000 cycles, the color change value was determined as 1.09. Except monolithic zirconia, the surface gloss values increased in general, but the differences were not found to be statistically significant (P>0.05). It was determined that after brushing simulation in monolithic zirconia, the gloss values significantly increased (P<0.05). The surface roughness values of monolithic zirconia, precrystallized lithium disilicate, precrystallized and crystallized zirconia reinforced lithium silicate ceramic groups increased significantly after 10000 and 50000 brushing cycles (P<0.05). When the color, gloss, surface roughness and surface topography changes were evaluated after 10000 cycles and 50000 cycles of tooth brushing simulation, it was found that brushing simulation was effective on the surface gloss and surface roughness of the materials. When the color change of the experimental groups was evaluated, it was determined that only the material factor was effective on the color change and the color change value in monolithic zirconia exceeded the clinical perceptibility threshold value.
Benzer Tezler
- Monolitik CAD/CAM seramiklerin farklı diş renkleri üzerinde maskeleme özelliklerinin karşılaştırılması
Comparison of masking properties of monolithic CAD/CAM ceramics on different tooth colors
ENGİN ESENTÜRK
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SEÇİL NEMLİ
- Farklı yüzey işlemleri uygulanan zirkonya seramik ile adeziv reçine siman bağlantısının in vitro olarak değerlendirilmesi
Effect of different surface treatment methods on bond strength of zirconia and resin cement
MERVE SONGÜL GÜDÜK
Doktora
Türkçe
2014
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. BEGÜM AKKAYAN KESMEZACAR
- Farklı kalınlıklardaki CAD/CAM seramiklerin dual-cure ve light-cure rezin siman polimerizasyonlarına etkisi
Effect of CAD/CAM ceramics of different thicknesses on dual-cure and light-cure resin cement polymerizations
BURHAN ARSLAN
Doktora
Türkçe
2023
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. TUBA YILMAZ SAVAŞ
- Farklı CAD/CAM materyallerinin yüzey parlaklığı ve pürüzlülüğü üzerine polisaj, glaze ve aşındırma işlemlerinin etkisi
The effect of polishing, glazing and grinding procedures on the surface gloss and roughness of different CAD/CAM materials
ÇİĞDEM ÇEBİ TÜYSÜZ
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. NECLA DEMİR
- Sinterleme hızının ve sıcaklığının monolitik zirkonyanın mikroyapısı, bükülme dayanımı ve optik özellikleri üzerindeki etkisinin değerlendirilmesi
Evaluation of the effect of sintering speed and temperature on the microstructure, bend strength and optical properties of monolithic zirconia
PELİN AÇIK
Doktora
Türkçe
2025
Diş HekimliğiGaziantep ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. FATİH SARI
PROF. DR. CEMAL AYDIN