Yüksek entropili CrMnFeCoNi alaşımına tungsten karbürün (%3-%5-%10) farklı oranlarda ilavesinin mekanik ve mikro yapı özelliklerine etkisinin incelenmesi
Investigation of the effect of addition of tungsten carbide (3%-5%-10%) to high entropy CrMnFeCoNi alloy at differentRates onmechanical and microstructural properties
- Tez No: 845847
- Danışmanlar: DOÇ. DR. YAHYA TAŞGIN
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Munzur Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 78
Özet
Bu çalışmada toz halinde bulunan Cr, Mn, Fe, Co, Ni ve WC elementleri ile üretilen Yüksek Entropili Cr20MnxFe20Co20Ni20WCx alaşımı incelenerek alaşımdaki Mn ve WC oranını değiştirip Cr20Mn20-xFe20Co20Ni20WCx alaşımlı malzemeye farklı oranlarda (%3-%5-%10) Tungsten Karbür (WC) ilavesi yapılarak homojen bir karışım elde edilmiştir. Karışımların toz metalurjisi yöntemiyle üretilip 6 ton basınç altında 30 gr ağırlıkta olacak şekilde preslenerek numuneler metalografik işlemler için hazır hale getirilmiştir. Ark eritme yöntemi ile 8 adet alaşım numunesi üretilmiş olup, 4 adet alaşım numunesi 24 saat süre ile 950 oC'de ısıl işleme tabi tutularak 4 adet ısıl işlemli ve 4 adet normal numune üretilmiştir. Üretilen numunelere aşınma deneyi, mikro sertlik, XRD, SEM ve EDS analizleri yapılarak mikro yapı özelliklerine etkisi araştırılmıştır. Yapılan deneysel çalışmalarda ısıl işleme tabi tutulmuş numunelerin normal numunelerden daha fazla sertlik değeri ortalamasına sahip olduğu ve XRD, SEM ve EDS mikro yapıları incelenen numunelerin tane yapılarının korunduğu ancak oranlarında değişim olduğu tespit edilmiştir. Aşınma deneyi sonucunda WC (%3-%5-%10) ilaveli ısıl işlemli numuneler, normal numuneler ile karşılaştırıldığında ısıl işlemli numunelerin kütle kayıplarının olumlu yönde azaldığı görülmüştür. Cr20Mn20-xFe20Co20Ni20WCx alaşımındaki elementlerin oranı değiştirilerek veya daha farklı elementler kullanılarak yapılacak yeni çalışmalara ışık tutabileceği değerlendirilebilir.
Özet (Çeviri)
In this study, High Entropy Cr20MnxFe20Co20Ni20WCx alloy produced with Cr, Mn, Fe, Co, Ni and WC elements in powder form was investigated and a homogeneous mixture was obtained by changing the ratio of Mn and WC in the alloy and adding Tungsten Carbide (WC) at different ratios (3%-5%-10%) to Cr20Mn20-xFe20Co20Ni20WCx alloy material. The mixtures were produced by powder metallurgy method and pressed under 6 tons of pressure to a weight of 30 g and the samples were made ready for metallographic processes. Eight alloy samples were produced by arc melting method, 4 alloy samples were heat treated at 950 oC for 24 hours and 4 heat treated and 4 normal samples were produced. Wear tests, microhardness, XRD, SEM and EDS analyzes were performed on the produced samples and the effect on microstructure properties was investigated. In the experimental studies, it was determined that the heat treated samples had a higher average hardness value than the normal samples and the grain structures of the samples whose XRD, SEM and EDS microstructures were examined were preserved, but their ratios changed. As a result of the wear test, it was observed that the mass loss of the heat-treated samples with the addition of WC (3%-5%-10%) decreased positively compared to the normal samples. It can be evaluated that new studies by changing the ratio of elements in Cr20Mn20-xFe20Co20Ni20WCx alloy or using different elements can shed light on new studies.
Benzer Tezler
- Yüksek entropili CrMnFeCoNiAl alaşımlarına bor ilavesinin etkisi
The effects of boron addition to CrMnFeCoNiAl alloys of high entropy
YUSUF KARACA
Yüksek Lisans
Türkçe
2019
Metalurji MühendisliğiNevşehir Hacı Bektaş Veli ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. CEMAL ÇARBOĞA
- Machine learning assisted design of biomedical high entropy alloys with low elastic modulus for orthopedic applications
Ortopedik uygulamalar için düşük elastik modüle sahip biyomedikal yüksek entropili alaşımların makine öğrenimi destekli tasarımı
HÜSEYİN CAN ÖZDEMİR
Doktora
İngilizce
2024
Makine MühendisliğiKoç ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. DEMİRCAN CANADİNÇ
- Mekanik alaşımlama yöntemi ile refrakter yüksek entropi HfMoNbVW-(Cr, Ni) alaşımlarının sentezlenmesi, ark ergitme ve basınçsız sinterlerme yöntemleriyle yoğunlaştırılması ve ilişkin karakterizasyon çalışmaları
Synthesis of refractory high entropy HfMoNbVW-(Cr, Ni) alloys by mechanical alloying method, densification by arc melting and pressureless sintering methods and related characterization studies
ZEYNEP BEYZA DOĞAN
Yüksek Lisans
Türkçe
2022
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA LUTFİ ÖVEÇOĞLU
- CoCrFeNiAlx (x=0.2; 0.6; 1.0; 1.5) yüksek entropili alaşım sistemlerin mekanik alaşımlamasının optimizasyonu ve B4C takviyesinin spark plazma sinterleme prosesine etkisinin araştırılması
Optimization of mechanical alloying of CoCrFeNiAlx (x=0.2; 0.6; 1.0; 1.5) high entropy alloy systems and investigation the effect of B4C addition on spark plasma sintering process
YUSUF BARAN ÇİÇEK
Yüksek Lisans
Türkçe
2025
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. GÜLTEKİN GÖLLER
- Yüksek entropili bir alaşımın çevrimli ve izotermal oksidasyon davranışlarının incelenmesi
Investigation of cyclic and isothermal oxidation behaviour of a high entropy alloy
PINAR EZGİ BAT
Yüksek Lisans
Türkçe
2024
Metalurji MühendisliğiOndokuz Mayıs ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. KADİR MERT DÖLEKER