Farklı kalsiyum silikat içeren materyallerle tamir edilen yapay oluşturulmuş iç kök rezorpsiyonlu dişlerin kırılma dirençlerinin karşılaştırılması

Comparison of fracture resistance of teeth with simulated internal root resorption cavities repaired with different calcium silicate containing materials

  1. Tez No: 848011
  2. Yazar: HAVVA GÖZDE ŞEN
  3. Danışmanlar: DOÇ. DR. AYÇA YILMAZ
  4. Tez Türü: Doktora
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Endodonti, İç Kök Rezorpsiyonu, Kalsiyum Silikat Materyaller, Kırılma Direnci, Kırılma Tipi, Calcium Silicate Materials, Endodontics, Fracture Resistance, Fracture Pattern, Internal Root Resorption
  7. Yıl: 2023
  8. Dil: Türkçe
  9. Üniversite: İstanbul Üniversitesi
  10. Enstitü: Sağlık Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Endodonti Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 105

Özet

Bu çalışmanın amacı, dört farklı kalsiyum silikat içerikli materyalin, yapay iç kök rezorpsiyonu oluşturulan dişlerde kullanılması sonucu kırılmaya karşı gösterdikleri direncin karşılaştırılmasıdır. 72 adet çekilmiş üst insan 1. kesici dişi kullanılan çalışmada, dişlerin kuron ve kökleri kök boyu 14 mm kalacak şekilde ayrılmış ve örnekler rastgele 6 gruba ayrılmıştır (n=12). Pozitif kontrol grubundaki örneklerde rezorpsiyon kavitesi oluşturulmamıştır. Negatif kontrol grubunda ise rezorpsiyon kavitesi oluşturulmuş ancak doldurulmamıştır. Tüm gruplarda aynı kanal şekillendirme ve doldurma yöntemi uygulanmıştır. Kök kanalı son şekillendirmesi resiprokal hareket ile çalışan Reciproc R40 sistemi ile yapılmıştır. 10 numara rond frez ile kanal girişinden düz bir şekilde 6 mm ilerlenerek yapay iç kök rezorpsiyon alanları oluşturulmuştur. Kök kanalının apikal kısmı Reciproc R40 sistemine uyumlu güta-perka ve AH Plus kanal dolgu patı ile tek kon yöntemiyle doldurulmuştur. Kanal dolguları, rezorpsiyon alanının başlangıç bölgesinden olacak şekilde ısı ile uzaklaştırılmıştır. Yapay oluşturulan rezorpsiyon kaviteleri 4 farklı kalsiyum silikat siman ile doldurulmuştur. Bu materyaller ProRoot MTA, Biodentine, NeoMTA 2 ve BioMTA+'dır. 7 mm'si dışarıda kalacak şekilde akrilik bloklara gömülen tüm örneklere universal test cihazı kullanılarak 1 mm/dk hız ile kuvvet uygulanmış ve değerler Newton cinsinden kaydedilmiştir. Veriler istatistiksel olarak değerlendirilmiştir. Gruplar arasındaki anlamlı farklılık negatif kontrol grubu ile Biodentine grubundan kaynaklanmaktadır. Biodentine grubu negatif kontrol grubuna göre istatistiksel olarak anlamlı derecede yüksek kırılma direnci göstermiştir. Diğer gruplarda elde edilen ortalama değerler arasında ise istatistiksel anlamlı fark bulunmamıştır. Tüm deney gruplarında kırılma tipi açısından istatistiksel olarak anlamlı farklılık bulunmamaktadır. Bu çalışmanın sınırları dahilinde kırılma direnci ve kırılma tipi gruplar arasında anlamlı farklılık göstermediğinden, iç kök rezorpsiyonuna sahip dişlerde rezorpsiyon alanında kullanılan bu kalsiyum silikat materyaller arasında anlamlı farklılık bulunmamaktadır.

Özet (Çeviri)

The purpose of this study was to evaluate the fracture resistance of four calcium silicate materials when used in teeth with simulated internal root resorption. 72 upper central incisors were decoronated to obtain a standard root length of 14 mm. The specimens were then randomly divided into six groups (n=12). The positive control group did not undergo the intentional creation of a resorption cavity. In contrast, the negative control group had a resorption cavity that was intentionally formed but was not filled calcium silicate materials. All of the groups underwent root canal treatment, with an identical procedure for both shaping and filling. The final step in the root canal treatment involved employing the Reciproc R40 system. An artificial internal resorption area was created by advancing 6 mm straight from the canal entrance, using a No. 10 round bur. For the apical portion of the root canal, the single-cone obturation method was performed using Reciproc R40 system gutta percha and AH Plus root canal filling paste for the filling process. Subsequently, the canal fillings were eliminated with heat from the initial region of the resorption area. Artificially induced resorption cavities were filled with four different calcium silicate cements: ProRoot MTA, Biodentine, NeoMTA 2, and BioMTA+. The specimens were embedded in acrylic blocks, with 7 mm exposed, and then subjected to a force of 1 mm/min using a universal testing machine. The results were recorded in Newtons and statistically analyzed. The significant difference within the groups arose when comparing the negative control group to the Biodentine group. The Biodentine group displayed a significantly higher fracture resistance than the negative control group In the experimental groups, fracture patterns were also not significantly different. In conclusion, neither fracture resistance nor fracture patterns have substantial variations among the different calcium silicate materials groups when used to treat teeth affected by internal root resorption.

Benzer Tezler

  1. Derı̇n çürüklü süt dı̇şlerı̇nı̇n pulpa kuafajında farklı kapaklama ajanlarının etkı̇nlı̇ğı̇nı̇n in-vivo olarak değerlendı̇rı̇lmesı̇

    Effectiveness of the different pulp capping material in pulp capping therapy of primary teeth with deep dentin caries: in vivo evaluation

    NACİYE NUR ŞAHİN

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2019

    Diş Hekimliğiİzmir Katip Çelebi Üniversitesi

    Pedodonti Ana Bilim Dalı

    DOÇ. DR. MERVE AKÇAY

  2. Hidroksiapatit doldurucuların rezin modifiye kalsiyum silikat simanın remineralizasyon etkinliği ve dentine bağlanma dayanımına etkisi

    Effect of hydroxyapatite filler on remineralization efficacy and dentin bond strength of resin modified calcium silicate cement

    ESRA AKTÜRK

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2021

    Diş HekimliğiSivas Cumhuriyet Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    PROF. DR. ÖZDEN ÖZEL BEKTAŞ

  3. Sonik, ultrasonik, fotonla uyarılmış fotoakustik dalgalanma ve xp-endo fınısher r ile yapılan aktivasyon işlemlerinin kanal dolgu materyallerinin uzaklaştırılmasındaki etkisinin değerlendirilmesi

    Evaluation of the effect of activation processes with sonic, ultrasonic, photon induced photoacoustic streaming and xp-endo finisher r on the removal of canal filling materials

    FATMA DURNA YURTSEVEN

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2023

    Diş HekimliğiKırıkkale Üniversitesi

    Endodonti Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ ALİ TÜRKYILMAZ

  4. Eğimli kök kanallarında farklı kök kanal patlarıyla yapılan kanal dolgusundaki boşlukların MİKRO-BT ile incelenmesi

    MİCRO-CT evaluation of voids in root canal filling with different root canal sealers in curved root canals

    İLÇİ BERK İÇMEZ

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2022

    Diş HekimliğiAnkara Üniversitesi

    Endodonti Ana Bilim Dalı

    PROF. DR. AYLİN KALAYCI

  5. Plazma destekli farklı tedavi protokollerinin dental eroziv lezyonlar üzerindeki etkisi

    The impact of various plasma-assisted treatment protocols on dental erosive lesions

    SEVGİ YILMAZ

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2022

    Diş HekimliğiSüleyman Demirel Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ ÖZGE KAM HEPDENİZ