Doğal zeolit içeren geopolimer betonlarda mekanik ve durabilite özelliklerinin araştırılması
Investigation of mechanical and durability properties of natural zeolite containing geopolymer concretes
- Tez No: 880606
- Danışmanlar: DR. ÖĞR. ÜYESİ ALİ ÖZ
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 116
Özet
Amaç: Bu çalışmada yüksek fırın cürufu (YFC), doğal zeolit (Balıkesir-Bigadiç), metakaolin, mermer tozu, 1-3 mm. kuvars, 3-5 mm. kuvars ve bazalt lif kullanılarak üretilen geopolimer betonların mekanik ve iç yapı özellikleri araştırılmıştır. Yöntem: YFC ve yüksek fırın cürufuna ağılıkça %0, %5, %10 ve %15 oranlarında doğal zeolit ikamesiyle geopolimer betonlar üretilmiştir. Aktivatör olarak ise 12 M NaOH ve Na2SiO3 çözeltileri kullanılmıştır. Aktivatör etkisinin mekanik ve iç yapı özelliklerine etkisinin belirlenebilmesı için NaOH ve Na2SiO3 çözeltileri oranı 2,2,5 ve 3 olarak karışımlar tayin edilmiştir ve 8 saat süreyle 80 oC'de küre bırakılmıştır. Toplamda 12 karışım ve her karışımdan 18 adet küp, 6 adet kiriş numune dökülmüştür. Elde edilen numuneler farklı yüksek sıcaklık (200,400 ve 600 oC) etkisine maruz bırakılmıştır. Geopolimer betonlara basınç dayanımı, kılcal su emme, ağırlık değişimi,SEM, analizleri uygulanmıştır. Bulgular: Zeolitin ağırlıkça %0, %5, %10, ve %15 oranlarında kullanılmasıyla üretilen geopolimer betonların basınç dayanımları 39,2-74,2 MPa arasında değiştiği görülmektedir. Yaklaşık 12 saat gibi kısa bir sürede 50 MPa ve üzeri basınç dayanımları kolaylıkla elde edilmiştir. Yüksek sıcaklık sonrasında çoğu gruplarda basınç dayanımlarında azalma gözlemlenirken 200 oC sıcaklığa maruz kalan bazı geopolimer kompozitlerin basınç dayanımında artış gözlemlenmiştir. Sonuç: Mikroyapı incelemelerinde termal kürden dolayı yoğun olarak geopolimerik jellerin oluştuğu gözlenmiştir. SS/SH oranı 2,5 olan karışımlarda %10 DZ içeriğinin ve SS/SH oranı 3 olan karışımlarda %5 DZ içeriğinin dayanım ve dayanıklılık özellikleri açısından daha uygun olduğu tespit edilmiştir. Geopolimer kompozitlerin %10'a kadar DZ kullanılarak üretilebileceği belirlenmiştir.
Özet (Çeviri)
Purpose: It is effective blast furnace slag (BFC), natural zeolite (Balıkesir-Bigadiç), metakaolin, marble powder, 1-3 mm. quartz, 3-5 mm. quartz, the mechanics and internal structure material of geopolymer concrete produced using quartz and basalt fibers were investigated. Method: Geopolymer concretes were produced by substituting 0%, 5%, 10% and 15% natural zeolite by weight into blast furnace slag. 12 M NaOH and Na2SiO3 solutions were used as activators. In order to determine the effect of the activator effect on the mechanical and internal structure properties, the mixtures were determined with the ratio of NaOH and Na2SiO3 solutions as 2, 2,5 and 3, and the sphere was left at 80 oC for 8 hours. A total of 12 mixtures and 18 cube and 6 beam samples from each mixture were cast. The obtained samples were exposed to different high temperatures (200, 400 and 600 oC). Compressive strength, capillary water absorption, weight change, SEM analyzes were applied to geopolymer concretes. Findings: It is seen that the compressive strengths of geopolymer concretes produced by using 0%, 5%, 10%, and 15% by weight of zeolite vary between 39,2-74,2 MPa. Compressive strengths of 50 MPa and above were easily achieved in a short time of approximately 12 hours. While a decrease in compressive strength was observed in most groups after high temperature, an increase in the compressive strength of some geopolymer composites exposed to 200 oC temperature was observed. Conclusion: In microstructural examinations, it was observed that geopolymeric gels were intensely formed due to the thermal sphere. It has been determined that 10% NZ content in mixtures with an SS/SH ratio of 2,5 and 5% NZ content in mixtures with an SS/SH ratio of 3 are more suitable in terms of strength and durability properties. It was determined that geopolymer composites could be produced using up to 10% NZ.
Benzer Tezler
- Taguchi yöntemi ile uçucu kül ve kalker katkılı zeolit esaslı geopolimer harçların tasarlanması
Design of zeolite based geopolymer mortars with fly ash and limestone additives by Taguchi method
ROBLE IBRAHIM LIBAN
Doktora
Türkçe
2022
İnşaat MühendisliğiKonya Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. ÜLKÜ SULTAN KESKİN
- Geopolimer harçların reolojik davranışı üzerinde zeolit etkisinin incelenmesi
Investigation of the effect of zeolite on rheological behaviours of geopolymer mortars
CANER ÖZER
Yüksek Lisans
Türkçe
2018
İnşaat Mühendisliğiİnönü Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. İBRAHİM TÜRKMEN
- Doğal zeolit bazlı geopolimerlerin özellikleri
Properties of natural zeolite based geopolymers
DİDEM GÜNGÖR
Yüksek Lisans
Türkçe
2019
Jeoloji MühendisliğiRecep Tayyip Erdoğan ÜniversitesiJeoloji Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SEVGİ ÖZEN KARSLI
- Zeolit esaslı geopolimer harçların yüksek sıcaklık etkisindeki fiziksel ve mekanik özelliklerinin incelenmesi
Investigation of physical and mechanical properties of zeolite-based geopolymer mortars under the effect of high temperature
MUSTAFA DURSUN
Yüksek Lisans
Türkçe
2024
İnşaat MühendisliğiYozgat Bozok Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. MEHMET KAYA
DOÇ. DR. UĞUR DURAK
- Yemlerine farklı ve artan miktarlarda doğal zeolit (Klinoptilolit) katılan etlik piliçlerin besi performanslarının belirlenmesi
Determination of feeding performances with addition of increased concentraton zeolite (Clinoptylolide) in broiler chicken
GÜLİN GÖKCE
Yüksek Lisans
Türkçe
2017
ZiraatKahramanmaraş Sütçü İmam ÜniversitesiZootekni Ana Bilim Dalı
YRD. DOÇ. DR. BEYHAN YETER