Karbon malzemelerin ılık derin çekme prosesinde yağlayıcı olarak kullanılabilirliğinin araştırılması ve sıcak koşullar için düşük maliyetli yağlayıcı geliştirilmesi
Investigation of the usability of the carbon materials as lubricant in warm deep drawing process and development of low cost lubricant for hot conditions
- Tez No: 890715
- Danışmanlar: DOÇ. DR. MUHAMMET HÜSEYİN ÇETİN, DOÇ. DR. NURİ ŞEN
- Tez Türü: Doktora
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Karabük Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 156
Özet
Bu çalışmada hidrotermal karbon (HTC) yağlayıcının sentezi ve sıcak endüstriyel koşullarda yağlayıcı olarak kullanılabilirliği araştırılmıştır. Bu kapsamda, organik kaynaklardan düşük maliyetle ve kısa sürede sentezlenerek üretilen hidrotermal karbonun (HTC) karakterizasyonu yapılmış ve tribolojik performansı detaylı olarak analiz edilmiştir. Hidrotermal karbonizasyon yöntemi ile üretilen HTC yağlayıcı SEM görüntüsü ve EDS analizi ile karakterize edilmiştir. HTC'nin farklı sıcaklıklarda sürtünmeye etkisinin belirlenmesi için AA5754 malzemesi ile pin-on-disk aşınma deneyine tabi tutulmuştur. HTC'nin derin çekme prosesine tribolojik etkisinin analizi için farklı yağlayıcı, sıcaklık, baskı plakası basıncı ve şekillendirme hızı parametrelerinin şekillendirme kuvvetine etkisi istatistiksel olarak analiz edilmiştir. HTC'nin performansı teflon, fulleren, grafen ve karbon nano-tüp (CNT) malzeme ile kıyaslanmıştır. Aşınma deneylerinden elde edilen sonuçlara göre en düşük sürtünme katsayısı değerinin fulleren yağlayıcı ortamında elde edildiği ve sıcaklık arttıkça sürtünme katsayısının azaldığı belirlenmiş, HTC'nin oksidasyon sebebiyle aşınma deneyinde fullerenden daha düşük performans gösterdiği görülmüştür. Derin çekme parametrelerinin şekillendirme kuvvetine etkisi analiz edildiğinde en etkili parametrelerin sırasıyla sıcaklık (%72,32) ve yağlayıcı (%20,89) parametreleri olduğu sonucu elde edilmiştir. S/N analizi sonuçlarına göre minimum şekillendirme kuvvetinin teflon katı yağlayıcı, 250°C sıcaklık, 15 bar baskı plakası basıncı ve 2 mm/s şekillendirme hızı koşullarında elde edildiği belirlenmiştir. HTC ile teflon arasındaki tribolojik performans farkı %1 seviyesindedir. Elde edilen sonuçlar HTC'nin endüstriyel yağlayıcı olarak kullanılabilirliğini kanıtlar niteliktedir.
Özet (Çeviri)
In this study, the synthesis of hydrothermal carbon (HTC) lubricant and its usability as a lubricant under hot industrial conditions were investigated. In this context, the characterization of HTC produced from organic sources at low cost and in a short time was performed, and its tribological performance was analysed in detail. HTC produced by the hydrothermal carbonization method was characterized through SEM images and EDS analysis. To determine the effect of HTC on friction at different temperatures, HTC was subjected to a pin-on-disc wear test with AA5754 material. The effect of various lubricants, temperatures, blank holder pressure, and forming speed parameters on the forming force for the analysis of the tribological effect of HTC on deep drawing processes were statistically analysed. The performance of HTC was compared with Teflon, fullerenes, graphene, and carbon nanotube (CNT) materials. According to the results obtained from wear tests, the lowest friction coefficient value was achieved in the presence of fullerenes as the lubricant, and as the temperature increased, the friction coefficient decreased. It was observed that HTC exhibited lower performance in the wear test compared to fullerenes due to oxidation. When the effect of deep drawing parameters on the forming force was analysed, it was concluded that the most effective parameters were temperature (72.32%) and lubricant (20.89%). According to the S/N analysis results, the minimum forming force was obtained under the conditions of solid Teflon lubricant, 250°C temperature, 15-bar blank holder pressure, and 2 mm/s forming speed. The tribological performance difference between HTC and Teflon is at the 1% level. The results demonstrate the potential industrial usability of HTC as a lubricant.
Benzer Tezler
- Toz metalurjisi ile üretilen Ni-Mo VE WNi-Mo çeliğine presleme ve sinterleme parametrelelerinin mekanik özelliklere etkisi
Effect of pressing and sintering parameters on mechanical properties on Ni-Mo VE WNi-Mo steel manufactured by powder metallurgy
MEHMET AKİF ERDEN
Yüksek Lisans
Türkçe
2021
Makine MühendisliğiKarabük ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA GÜNAY
- Investigation of effect of bitumen chemical composition, polymer and warm mix asphalt additives on the properties of bitumen by using response surface method
Bitüm kimyasal içeriği, polimer ve ılık karışım asfalt katkılarının bitüm özellikleri üzerine etkisinin tepki yüzeyi yöntemiyle incelenmesi
EMEL BAŞKENT
Yüksek Lisans
İngilizce
2016
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. MUSTAFA HULUSİ ÖZKUL
- Doğal hidroksiapatit toz üretimi, karakterizasyonu ve antibakteriyel özelliklerinin belirlenmesi
Natural hydroxyapatite powder production characterization and determination of antibacterial properties
SERDAR GÖKHAN AKÇA
Yüksek Lisans
Türkçe
2016
Mühendislik BilimleriSakarya Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
DOÇ. DR. FATİH ÇALIŞKAN
- Novel light-emitting devices of semiconductor quantum dots and conjugated polymer nanoparticles
Yarı iletken kuantum noktacıkları ve konjüge polimer nanoparçacıkların yenilikçi ışık yayan aygıtları
TALHA ERDEM
Doktora
İngilizce
2016
Elektrik ve Elektronik Mühendisliğiİhsan Doğramacı Bilkent ÜniversitesiElektrik-Elektronik Mühendisliği Ana Bilim Dalı
PROF. DR. HİLMİ VOLKAN DEMİR
- High-resolution sediment records of Lake Salda (SW anatolia) for the last millennium: Past climate changes driven by solar forcing
Salda Gölü'nün son bin yildaki yüksek çözünürülüklü çökel kayıtları: Güneş etkisiyle oluşan geçmiş iklim değişimleri
ILIYA BAUCHI DANLADI
Yüksek Lisans
İngilizce
2015
Jeoloji MühendisliğiMuğla Sıtkı Koçman ÜniversitesiJeoloji Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. SENA AKÇER ÖN
YRD. DOÇ. DR. BEDRİ KURTULUŞ