Lantan katkılı TIIıns2 katmanlı ferroelektrik yarıiletken kristallerin piroelektrik özelliklerine ışık veya elektrik alan ile uyarılmış yapısal safsızlıkların etkisi
Effect of structural defects excited by light or electric field on the pyroelectric properties of lantanium doped TIIins2 layered ferroelectric semiconductor crystals
- Tez No: 891762
- Danışmanlar: PROF. DR. MİRHASAN SEYİTSOY
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Gebze Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 74
Özet
Bu tez çalışmasında, lantanyum katkılı katmanlı TlInS2 (TlInS2+La) ferroelektrik yarı- iletken kristalindeki 80–300 K sıcaklık aralığında piroelektrik akım ve ışık uyarımlı geçici akım spektroskopisi (Photo–induced Current Transient Spectroscopy: PICTS) araştırma sonuçları sunulmuştur. Elde edilen sonuçlar ve veriler karşılaştırmalı olarak yapılmıştır. Farklı olan safsızlık merkezleri belirlenip tanımlanmıştır. Kristallerin yapısında bulunan kusurların piroelektrik özelliklerini belirleyebilmek için deneysel verilerin analizi yapılmıştır. Derin seviyeye yerleşmiş olan tuzakların yakalama tesir kesitleri ve iyonlaşma akti- vasyon enerji değerleri farklı ısıtma hızı ile elde edilmiştir. Düşük sıcaklıklarda etkili olan (156 K) ve aktivasyon enerjisi 0.29 eV yakalama tesir kesiti sırası ise 2.2×10−10cm2 olan derin enerji seviyesi tuzağı BTE43'ün lantanyum katkısından kaynak-landığı an- laşılmıştır. PICTS ölçümlerinde derin seviye tuzak merkezi B5, TlInS2+La kristallerinde olan oransız faz bölgelerini içeren sıcaklık aralıklarında yapısal düzensizleşmeye, düzen bozulmasına bağlı çok büyük bir statik dielektrik sabit etkin hale gelmektedir. B5 için yapılan PICTS modellemesinden alınan ölçümlerde katkısız TlInS2 kristaline özgü olan derin seviye tuzağının aktivasyon enerjisinin 0.3 eV olarak, yakalama tesir kesiti ise 1.8 × 10−16cm2 olarak belirlenmiştir.
Özet (Çeviri)
In this thesis, the results of the investigation on pyroelectric current and photo-induced current transient spectroscopy (PICTS) in the temperature range of 80–300 K for lan- thanum doped layered TlInS2 (TlInS2+La) ferroelectric semiconductor crystal are pre- sented. The obtained results and data have been compared. Different impurity centers have been identified and characterized. An analysis of the experimental data has been performed to determine the pyroelectric properties of the defects present in the crystal structure. The capture cross-sections and ionization activation energy values of deep–level traps were obtained at different heating rates. It was understood that the deep energy level trap BTE43, which is effective at low temperatures (156 K) and has an activation energy of 0.29 eV and a capture cross-section of 2.2 × 10−10cm2, originated from lanthanum doping. In the PICTS measurements, the deep-level trap center B5, associated with the temperature ranges containing disordered phase regions in TlInS2+La crystals, becomes effective due to large static dielectric constant resulting from structural disorder. From the measurements obtained by PICTS modeling for B5, the activation energy of the deep-level trap specific to the undoped TlInS2 crystal was determined to be 0.3 eV, and the capture cross-section was 1.8 × 10−16cm2.
Benzer Tezler
- Lantan katkılı çinko boratların kinetik parametrelerinin belirlenmesi
Determination of kinetic parameters of lanthanum doped zinc borates
AZİZ HALİT GÖZEL
Yüksek Lisans
Türkçe
2014
Fizik ve Fizik MühendisliğiAdıyaman ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. MUSTAFA TOPAKSU
YRD. DOÇ. DR. NİL KÜÇÜK
- Antiferroelektrik seramiklerin yüksek enerji yoğunluğuna sahip kapasitör ve elektrokalorik uygulamalar için incelenmesi
Investigation of antiferroelectric ceramics for high energy density capacitor and electrocaloric applications
NAMIK KEMAL GÖZÜAÇIK
Doktora
Türkçe
2023
Metalurji MühendisliğiGebze Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. SEDAT ALKOY
- Lantanit katkılı yarı iletken ince filmlerin optik özelliklerinin incelenmesi
Optical properties of lanthanide doped semiconductor thin films
ÖZLEM GÜLDALI
Doktora
Türkçe
2017
Endüstri Ürünleri TasarımıSakarya ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. İBRAHİM OKUR
- Lanthanum doped calcium silicate nanoparticles for drug delivery and X-ray contrast imaging
İlaç salımı ve x-ray kontrast görüntüleme için nanopartikül lantanum katkılı kalsiyum silikat
YOUSSOUF ABAKAR ADAM
Yüksek Lisans
İngilizce
2021
BiyomühendislikKarabük ÜniversitesiBiyomedikal Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ AMMAR ZEİDAN GHAİLAN ALSHEMARY
- Modifiye biyoaktif cam üretimi ve karakterizasyonu
Synthesis and characterization of modified bioactive glasses
ALKIN ESKİMERGEN
Yüksek Lisans
Türkçe
2023
Metalurji Mühendisliğiİstanbul Üniversitesi-CerrahpaşaMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ALİYE ARABACI