Evaluation of the fracture resistance and stress distribution of cad-cam post-core systems produced from different materials
Farklı materyallerden üretilen cad-cam post-kor sistemlerinin kırılma dayanımı ve stres dağılımının değerlendirilmesi
- Tez No: 903674
- Danışmanlar: DOÇ. DR. ÖZGE PARLAR ÖZ, DR. ÖĞR. ÜYESİ İREM KARAGÖZOĞLU
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD-CAM, PEEK, Trinia, post-kor, CAD-CAM, PEEK, Trinia, post-core
- Yıl: 2024
- Dil: İngilizce
- Üniversite: Gaziantep Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
CAD-CAM sistem kullanılarak PEEK, nano hibrit seramik, fiberle güçlendirilmiş kompozit ve zirkonyumdan üretilen monoblok post-kor restorasyonların kırılma dirençlerini ve sonlu elamanlar analizi ile stres dağılımlarını in-vitro olarak araştırmaktır. Çalışmamızda tek köklü 48 adet mandibular 2. premolar dişin kanal tedavisi yapıldı ve 4 gruba ayrıldı (n=12). Çalışma grupları; PEEK, nano seramik, GFR-C (cam fiberle güçlendirilmiş kompozit) ve zirkonyum olarak belirlendi. Post-korlar CAD-CAM sistem ile üretildi. Termal siklus cihazında yaşlandırılan örneklere universal test cihazında dişin uzun aksına 45 açıyla statik yükleme yapıldı. Sonlu elemanlar analizi için modellenen mandibular 2. premolar dişin uzun aksına 45 açı ile 100 N kuvvet uygulandı. Maksimum Von Misses stresleri kaydedildi. Kırılma dayanımı istatistiksel olarak Tek Yönlü Varyans Analizi (One-Way ANOVA) ile değerlendirildi. İkili gruplar arası anlamlılık Post-Hoc karşılaştırmalar Dunnet t testi ile yapıldı. PEEK ve nano seramik post-korlar benzer kırılma direncine sahipti (p>0,05). Ancak GFR-C ve zirkonyum post-korlardan anlamlı düzeyde daha düşüktü (p<0,05). Zirkonyum post korlar anlamlı düzeyde hepsinden daha yüksek kırılma direncine sahipti (p<0,05). Post-korlar için maksimum Von Misses değerleri en yüksek zirkonyum post-korda kaydedilirken, diş kökünde oluşan maksimum Von Misses değerleri ise en yüksek PEEK post-korlu modelde kaydedildi. Kırılma dayanımı değeri en yüksek zirkonyum post-korda elde edilirken, nano seramik post-korlar düşük kırılma dayanımına sahipti. Tüm post korların kırılma dayanımı değerleri klinik açıdan kırılma riski gösteren değerin oldukça üzerindeydi.
Özet (Çeviri)
The aim is to investigate the fracture resistance and stress distributions of monoblock post-core restorations produced from PEEK, nano hybrid ceramic, fiber-reinforced composite, and zirconium using the CAD-CAM system in-vitro, and to analyze stress distributions using finite element analysis. In our study, root canal treatment was performed on 48 single-rooted mandibular second premolar teeth, and they were divided into four groups (n=12). The study groups were defined as PEEK, nano ceramic, GFR-C(glass fiber-reinforced composite)and zirconium. The post-cores were produced using the CAD-CAM system. The samples were aged in a thermal cycle device and subjected to static loading at a 45° angle to the long axis of the tooth in a universal testing machine. For the finite element analysis, a force of 100 N was applied at a 45° angle to the long axis of the modeled mandibular second premolar tooth. Maximum Von Mises stresses were recorded.Fracture resistance was statistically evaluated using one-way variance analysis (One-Way ANOVA). Post hoc comparisons between paired groups were made using the Dunnett t-test. PEEK and nano ceramic post-cores had similar fracture resistance (p>0.5). However, it was significantly lower than GFR-C and zirconium post-cores (p<0.05). Zirconium post-cores had significantly higher fracture resistance than all others (p<0.05). Maximum Von Mises values for post-cores were recorded highest in zirconium post-cores, while maximum Von Mises values in the tooth root were recorded highest in the PEEK post-core model. The highest fracture resistance value was obtained in zirconium post-cores, while nano ceramic post-cores had lower fracture resistance. The fracture strenght values of all post-cores were well above the value that indicates a clinical risk of fracture.
Benzer Tezler
- Farklı CAD/CAM materyallerinin, anterior diş morfolojisinin ve diş preparasyonunun laminate veneer restorasyonlarda stres dağılımına etkisinin değerlendirilmesi: Sonlu elemanlar analizi
Evaluation of the effects of different CAD/CAM materials, anterior tooth morphology and tooth preparation on stress distribution in laminate veneer restorations: Finite element analysis
EMRE SEFA ÇİNİ
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiBolu Abant İzzet Baysal ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. KÜBRA DEĞİRMENCİ
- Üç farklı post-kor sisteminin kırılma dayanımlarının incelenmesi ve sonlu eleman analizi ile stres dağılımlarının değerlendirilmesi
Investigation of the fracture strengths of three different post-core systems and evaluation of the stress distribution using finite element analysis
MERVE ÖZARSLAN
Doktora
Türkçe
2019
Diş HekimliğiAkdeniz ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ULVİYE ŞEBNEM BÜYÜKKAPLAN
- Post kor sistemlerinin fraktür analizi ve sonlu elemanlar stres analiz yöntemi ile değerlendirilmesi
Evaluation of post-core systems with fracture resistance and finite element analysis methods
MEHMET SELİM BİLGİN
Doktora
Türkçe
2008
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ATİYE NİLGÜN ÖZTÜRK
- İki farklı adeziv siman ile simante edilmiş implant destekli CAD/CAM monolitik kron restorasyonların dinamik yükleme sonrası kırılma dayanımlarının değerlendirilmesi
Evaluation of fracture resistance after dynamic loading of implant supported CAD/CAM monolithic crown restorations with two different adhesive cements
KAAN CEVAT ŞALVARLI
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiAydın Adnan Menderes ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ESRA TALAY ÇEVLİK
- Farklı CAD/CAM tam seramik materyallerin optik özellikleri ve makaslama bağlanma dayanımının değerlendirilmesi
The evaluation of optical properties and shear bond strength of different CAD/CAM full ceramic materials
MEHTAP BOZKURT
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ NECLA DEMİR