Mineral indükleyici peptid ilave edilmiş geleneksel cam iyonomer simanın flor salınımı ve mekanik özelliklerinin incelenmesi
Evaluation of fluoride release and mechanical properties of conventional glass ionomer cement modified with a mineralization-promoting peptide
- Tez No: 945131
- Danışmanlar: DOÇ. DR. CENKHAN BAL
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Cam iyonomer siman, flor salınımı, mikrosertlik, mineralizan peptit, sıkışma dayanımı, Glass ionomer cement, fluoride release, microhardness, mineralization-promoting peptide, compressive strength
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Sağlık Bilimleri Üniversitesi
- Enstitü: Gülhane Diş Hekimliği Fakültesi (ankara)
- Ana Bilim Dalı: Çocuk Diş Hekimliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu tez çalışmasında, geleneksel cam iyonomer siman olan Ketac Molar Easy Mix'e yeni bir biyomimetik peptid olarak adlandırılan Mineralizasyonu destekleyen peptid 3 (MPP3) ilave edilmesinin flor salınımı ile mekanik ve fiziksel özelliklere etkisinin değerlendirilmesi amaçlanmıştır. MPP3'ün geleneksel cam iyonomer simana ilavesinin, flor salınımı ile mekanik ve fiziksel özelliklere etkilerinin incelendiği literatürde bilinen ilk çalışmadır. Gereç ve yöntem: Bu çalışmada, biri yalnızca geleneksel cam iyonomer siman (kontrol), diğeri ise 0.2 mM MPP3 eklenmiş cam iyonomer siman (deney) olmak üzere iki grup oluşturulmuştur. Flor salınımı için 4x6 mm boyutlarında silindirik şekilde hazırlanan numuneler oral kavite koşullarını taklit eden inkübatörde deiyonize su içinde bekletilmiş ve flor iyon-seçici elektrot yöntemiyle 1, 2, 7, 14, 21, 28. günlerde ölçüm yapılmıştır. Mekanik özelliklerin değerlendirilmesi için mikrosertlik, sıkışma dayanımı testleri uygulanmış; yüzey morfolojisi ve yapısal değişiklikler ise SEM, EDS ve Raman spektroskopisi analizleriyle incelenmiştir. Mikrosertlik, sıkışma dayanımı, SEM, EDS ve Raman spektroskopisi için 4x6 mm boyutlarında silindirik şekilde hazırlanan hazırlanan numuneler, analiz günlerine kadar oral kavite koşullarını taklit eden inkübatörde yapay tükürük sıvısında bekletilmiştir. Ölçümler 1. ve 28. günlerde gerçekleştirilmiştir. Verilerin istatistiksel analizinde IBM SPSS Statistics (21 version) paket programı kullanılmıştır. İstatistiksel anlamlılık için p<0.05 değeri kullanılmıştır. Bulgular: Flor salınımında her iki grupta da en yüksek değer 1. günde ölçülmüş, ardından 28. güne kadar düzenli bir azalma görülmüş, flor salınımı açısından her iki grup arasında anlamlı bir fark tespit edilmemiştir. Mikrosertlik testi sonuçları, MPP3 ilavesinin yüzey sertliğinde anlamlı bir fark oluşturmadığını göstermiştir. Sıkışma dayanımı testinde 28. günde deney grubu ile kontrol grubu arasında istatistiksel olarak anlamlı fark saptanmıştır. SEM görüntülerinde her iki grupta da yeni kristal oluşumları gözlemlenmiş, MPP3 grubunda kristallerin daha belirgin ve düzenli olduğu izlenmiştir. EDS analizinde her iki grupta da benzer elementel dağılım saptanmış (C, Si, Al, F). Raman spektroskopisi verilerine göre polimerizasyon oranlarında anlamlı fark gözlenmemiştir. Sonuç: Cam iyonomer simana MPP3 ilavesinin, cam iyonomer simanın flor salınımı ile mekanik ve fiziksel özelliklerine olumsuz bir etkide bulunmadığı sonucuna ulaşılabilir. Bu sonuçlar, MPP3'ün cam iyonomer simanlara reminerilazsyon açısından potansiyel katkılar sunabileceğini ancak daha kapsamlı çalışmalarla desteklenmesi gerektiğini göstermektedir.
Özet (Çeviri)
Aim: This thesis aimed to evaluate the effect of incorporating a novel biomimetic peptide Mineralization Promoting Peptide 3 (MPP3) into a conventional glass ionomer cement (Ketac Molar Easy Mix) on fluoride release and its mechanical and physical properties. To the best of our knowledge, this is the first study in the literature investigating the effect of MPP3 addition on the fluoride release and mechanical-physical properties of conventional glass ionomer cement. Materials and Methods: Two groups were prepared: a control group containing only conventional glass ionomer cement, and an experimental group with 0.2 mM MPP3 added. Cylindrical specimens (4x6 mm) were incubated in deionized water under simulated oral cavity conditions. Fluoride release was measured on days 1, 2, 7, 14, 21, and 28 using a fluoride ion-selective electrode. For mechanical evaluation, microhardness and compressive strength tests were conducted, while surface morphology and structural characteristics were analyzed using SEM, EDS, and Raman spectroscopy. Specimens were stored in artificial saliva until analysis on days 1 and 28. Statistical analyses were performed using IBM SPSS Statistics version 21, with significance set at p<0.05. Results: The highest fluoride release was observed on day 1 in both groups, followed by a steady decrease until day 28. No statistically significant difference was found between the two groups in terms of fluoride release. Microhardness results indicated that MPP3 incorporation did not significantly affect surface hardness. However, compressive strength was significantly higher in the experimental group on day 28. SEM images revealed new crystal formations in both groups, with more pronounced and regular crystals in the MPP3 group. EDS analysis showed similar elemental composition (C, Si, Al, F) in both groups. Raman spectroscopy results showed no significant difference in polymerization ratios. Conclusion: The addition of MPP3 to glass ionomer cement did not adversely affect fluoride release or its mechanical and physical properties. These results suggest that MPP3 may offer potential contributions to glass ionomer cements in terms of remineralization, although further comprehensive studies are needed to support this.
Benzer Tezler
- Demineralize edilmiş süt dişi numunelerinde mineral indükleyici peptit ilave edilmiş macun etkisinin ex vivo ortamda incelenmesi
Evaluation of the effect of a mineralization-inducing peptide-added toothpaste on demineralized pri̇mary tooth specimens in an ex vivo model
AYLİN ORUÇ
Diş Hekimliği Uzmanlık
Türkçe
2026
Sağlık Bilimleri ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
Yükleniyor...
- Mineral indükleyici peptidin daimi diş remineralizasyonuna etkisinin kazeinfosfopeptid-amorfkalsiyumfosfat ile karşılaştırmalı olarak ex vivo ortamda incelenmesi
Comparative evaluation of the effect of a mineralization-inducing peptide on the remineralization of permanent teeth in an ex vivo model in comparison with casein phosphopeptide–amorphous calcium phosphate
RIZA MERT ŞAHİN
Diş Hekimliği Uzmanlık
Türkçe
2026
Sağlık Bilimleri ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
Yükleniyor...
- Bitki büyümesine etki eden bakteriler: İzolasyonu, teşhisi, biyokimyasal özellikleri ve bitki gelişimindeki potansiyelinin belirlenmesi
Plant growth promoting bacteria: Isolation, identification, biochemical properties and determination of plant growth promoting potential
OSMAN BEDRETTİN AKKAYA
- Farklı rekombinant ekspresyon sistemlerinde peynir altı suyunun değerlendirilmesi
Utilization of whey in different recombinant expression systems
SEYHAN İÇİER
- Geriatrik popülasyonda APİ (aterojenik plazma indeksi) değerleri ve kmd (kemik mineral dansitometrisi) skorları arasındaki ilişkinin değerlendirilmesi
Evaluation of the relationship between AIP (atherogenic index of plasma ) values and bmd (bone mineral density) scores in the geriatric population
BESTE ATAHAN