3D printer ile farklı daimi reçine materyallerinden üretilen implantüstü kronların mekanik ve fiziksel özelliklerinin değerlendirilmesi
Evaluation of the mechanical and physical properties of implant-supported crowns fabricated from different permanent resin materials using 3D printing technology
- Tez No: 945518
- Danışmanlar: PROF. DR. DERYA ÖZDEMİR DOĞAN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Üç Boyutlu Baskı, Bilgisayar Destekli Tasarım, Bilgisayar Destekli Üretim, Yüzey Özellikleri, Sentetik Reçineler, Reçineler-yapay, Printing, Three-Dimensional, Computer-Aided Design, Computer-Aided Manufacturing, Surface Properties, Resins, Synthetic, Computer aided design, Computer aided manufacturing, Resins-synthetic, 3D printing
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Sivas Cumhuriyet Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, sabit dental restorasyonlarda kullanılan farklı üretim teknikleriyle elde edilen daimi reçine materyallerin mekanik ve fiziksel özelliklerini karşılaştırarak, dijital üretim yöntemlerinin klinik başarıya etkisini değerlendirmektir. Bu kapsamda, 3D baskı teknolojisi ile üretilen beş farklı marka daimi reçine materyali ile freze yöntemiyle üretilen hibrit seramik materyalin kırılma direnci, yüzey pürüzlülüğü ve mikrosertlik özellikleri incelenmiştir. Yöntem: Beş farklı 3D baskı hibrit reçine materyali ve bir freze yöntemiyle üretilmiş hibrit seramik olmak üzere altı grup oluşturuldu. Her gruptan 20 molar diş formunda kron üretildi, yaşlandırma öncesi ve sonrası değerlendirilmek üzere ikiye ayrılarak toplam 120 kron üzerinde kırılma dayanımı testi uygulandı. 120 disk örneği ise her grup için 10 disk mikrosertlik ve 10 disk yüzey pürüzlülüğü (Ra) analizi yapılacak şekilde ikiye ayrıldı. Böylece toplamda 240 örnek değerlendirildi. Kronlar, kendi gruplarına ait materyallerle hazırlanarak rezin siman ile parmak basıncı altında simante edildi ve universal test cihazında kırılma dayanımı testine tabi tutuldu. Disk örneklerinin yüzey pürüzlülüğü, profilometre cihazıyla üç noktadan ölçülerek ortalama Ra değerleri hesaplandı. Mikrosertlik testleri, Vickers elması ile donatılmış otomatik mikrosertlik test cihazı ile yapılıp her diskin üç noktasından alınan ölçümlerin ortalaması alındı. Tüm gruplar yaşlandırma protokolüne (termal çevrim) tabi tutuldu, ardından testler tekrarlanarak yaşlandırmanın etkisi değerlendirildi. Veriler SPSS programı ile istatistiksel olarak analiz edildi. Bulgular: Kırılma dayanımı açısından gruplar arasında anlamlı fark saptandı (p<0.05). Flexcera grubu en yüksek değerleri gösterirken, Senertek grubu, Formlabs ve Bego gruplarına göre daha yüksek bulundu. Diğer gruplar arasında fark görülmedi. Yaşlandırma sonrası tüm gruplarda dayanımda düşüş oldu, bu azalma Senertek ve Saremco gruplarında anlamlı bulundu (p<0.05). Ra analizlerinde yaşlandırma öncesinde Senertek ve Vita grupları daha yüksek pürüzlülük gösterdi. Yaşlandırma sonrası genel olarak anlamlı değişim gözlenmedi; yalnızca Senertek grubunda anlamlı düşüş saptanmadı (p<0.05). Mikrosertlik ölçümlerinde freze grubunun değerleri tüm 3D baskı gruplarından yüksek elde edildi. Yaşlandırma sonrası Vita grubu hariç tüm gruplarda sertlikte artış gözlendi ve bazı gruplarda bu artış belirgin oldu. Sonuç: Çalışmanın sonuçları, sabit protez uygulamalarında kullanılacak materyal ve üretim yönteminin seçiminde, klinik ihtiyaçların dikkate alınması gerektiğini göstermektedir. Freze yöntemiyle elde edilen hibrit seramikler, mekanik açıdan avantaj sunarken; bazı eklemeli üretim materyalleri, yüzey pürüzlülüğü açısından daha iyi performans sergilemiştir. Bu bulgular, dijital üretim teknolojilerinin uygun materyal seçimiyle birlikte sabit restorasyonlarda etkili şekilde kullanılabileceğini ortaya koymaktadır.
Özet (Çeviri)
Objective: The aim of this study was to compare the mechanical and surface properties of hybrid ceramic materials produced using different fabrication techniques for fixed dental restorations, and to evaluate the clinical relevance of digital manufacturing technologies. In this context, five different brands of permanent hybrid resin materials fabricated using 3D printing technology and one hybrid ceramic material produced by milling were examined in terms of fracture resistance, surface roughness, and microhardness. Materials and Methods: Six groups were formed, including five different 3D-printed resin materials and one milled hybrid ceramic. From each group, 20 molar-shaped crowns were produced and divided into two subgroups for pre-aging and post-aging evaluations, resulting in a total of 120 crowns subjected to fracture resistance testing. Additionally, 120 disk-shaped specimens were prepared: 10 from each group were used for microhardness analysis and the remaining 10 for surface roughness (Ra) analysis. In total, 240 specimens were evaluated. Crown specimens were cemented using resin cement under finger pressure and subjected to fracture resistance testing using a universal testing machine. Surface roughness of the disks was measured using a profilometer at three different points, and the mean Ra values were recorded. Microhardness tests were performed using an automated Vickers hardness testing machine, and the mean values were calculated from three indentations per disk. All specimens were subjected to an artificial aging protocol (thermal cycling), and the same tests were repeated to assess the effect of aging. Data were statistically analyzed using SPSS software. Results: A statistically significant difference was found among the groups in terms of fracture resistance (p<0.05). The Flexcera group exhibited the highest fracture resistance values, while the Senertek group showed higher values compared to the Formlabs and Bego groups. No significant differences were observed among the remaining groups. After aging, all groups showed a decrease in fracture resistance, with Senertek and Saremco groups demonstrating a statistically significant reduction (p<0.05). In terms of surface roughness, Senertek and Vita groups presented higher Ra values before aging. Following aging, no significant changes were observed in general; however, a statistically significant decrease in Ra was recorded only in the Senertek group (p<0.05). Regarding microhardness, the milled hybrid ceramic group exhibited higher values than all 3D-printed groups. After aging, an increase in hardness was observed in all groups except Vita, with some groups showing a more pronounced improvement. Conclusion: The findings of this study suggest that the selection of material and fabrication technique for fixed prosthodontic applications should be based on specific clinical requirements. While milled hybrid ceramics offer superior mechanical performance, certain 3D-printed materials demonstrate better surface quality. These results indicate that digital manufacturing technologies, when combined with appropriate material choices, can be effectively utilized in fixed prosthetic restorations.
Benzer Tezler
- Hibrit seramik ve daimi reçine materyallerinden üretilen farklı restorasyon tasarımlarında stres dağılımının sonlu elemanlar analizi ile incelenmesi
Finite element analysis of stress distribution indifferent restoration designs fabricated from hybridceramic and permanent resin materials
EREN ÇAYIRLI
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiBolu Abant İzzet Baysal ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ HATİCE SEVMEZ
- Üç boyutlu yazıcılar ile üretilen rezin materyallerinin mekanik ve optik özelliklerinin değerlendirilmesi
Evaluation of the mechanical and optical properties of resin materials produced using 3D printers
EMRE ASLAN
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiOrdu ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. CENNET ELÇİN SAĞIRKAYA
- Postpolimerizasyonun makyaj yapılmış eklemeli yöntem ile üretilen daimi kron rezinlerinin renk stabilitesi ve renklemesine etkisi
The effect of post-polymerization on the color stability and discoloration of resin permanent crowns produced by the characterization of additive manufacturing
BEYZA NUR TERLER NALBAT
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiHatay Mustafa Kemal ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ TAHA YAŞAR MANAV
- Kürleme süresinin 3 boyutlu yazıcı ve farklı daimi reçineler ile üretilen endokronların yüzey doğruluğu üzerindeki etkisinin ı̇ncelenmesi
Investigation of the effect of post-curing time on the surface trueness of endocrowns manufactured with 3D printer and different permanent resins
ZEHRA KAHRAMAN
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiAfyonkarahisar Sağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SAFA ÖZDEN
- Üç boyutlu yazıcı ile üretilen farklı daimi restorasyon reçinelerinin renk özelliklerinin ve aşınma dirençlerinin karşlaştırılması
Comparison of colour properties and wear resistance of different permanent restoration resins produced by three dimensional printer
ZÜLAL ÇOBAN GÜNDOĞAN
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiBezm-İ Alem Vakıf ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ÖZLEM KARA