3B yazıcı ile üretilen farklı daimi kron materyallerinin renk stabilitelerinin değerlendirilmesi
Evaluation of the color stability of different 3D printed definitive crown materials
- Tez No: 1018488
- Danışmanlar: DOÇ. DR. MEHMET UĞUR
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: 3 Boyutlu Yazıcı, CAD/CAM, Daimî Kron Reçinesi, Renk Stabilitesi, 3D Printing, CAD/CAM, Color Stability, Definitive Crown Resin
- Yıl: 2026
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, farklı daimî kron reçinelerinden elde edilen restorasyon materyallerinin çay, kahve ve distile suya belirli sürelerle maruz bırakılması sonrasında meydana gelen renk değişimlerinin değerlendirilmesi ve karşılaştırılmasıdır. Gereç ve Yöntem: Çalışmada VarseoSmile Triniq (VST), P-Crown v4 (PC), Crowntec (CT) ve Alias Dental Crown (ADC) olmak üzere 4 farklı daimî kron reçinesi ile Cerasmart (CS) CAD/CAM materyali kullanılmıştır. Kron reçineleri ve CAD/CAM materyalinden; çay, kahve ve distile suda bekletilmek üzere her grupta 12 örnek bulunacak şekilde toplam 180 örnek hazırlanmıştır (n=12). Renk ölçümleri başlangıç, 7. gün ve 30. günde gerçekleştirilmiştir. Renk ölçümleri VITA Easyshade V dijital spektrofotometresi kullanılarak yapılmış, renk farkı değerleri CIEDE2000 formülüne göre hesaplanmıştır. Elde edilen veriler SPSS 26.0 (IBM Corp., Armonk, NY, USA) programında analiz edilmiştir. L*, a*, b* ve ΔE00 değerlerinin istatistiksel analizinde tekrarlı ölçümler varyans analizi (Repeated Measures ANOVA) kullanılmış, anlamlı farklılık saptanan durumlarda Bonferroni düzeltmeli çoklu karşılaştırma testleri uygulanmıştır (α=0,05). Bulgular: Materyal tipi, solüsyon tipi ve zaman faktörünün renk değişimi üzerinde istatistiksel olarak anlamlı etkileri olduğu belirlenmiştir (p<0,05). En yüksek renk değişimi, 0–30 günlük periyotta kahve içerisinde bekletilen PC grubunda izlenirken (ΔE00=6,58 ± 1,36), en düşük renk değişimi distile suda bekletilen VST grubunda gözlenmiştir (ΔE00=0,23 ± 0,11). Tüm materyaller değerlendirildiğinde, kahve solüsyonunda bekletilen örneklerin daha yüksek renk değişimi gösterdiği, distile su grubunun ise en düşük renk değişim değerlerine sahip olduğu saptanmıştır. Sonuç: Kahve ve çay solüsyonlarının, 3B yazıcı ile üretilen daimî kron reçineleri ve CAD/CAM restoratif materyallerde klinik olarak anlamlı renk değişimlerine neden olabildiği belirlenmiştir. Bu nedenle restoratif materyal seçiminde, materyallerin renk stabilitesi özellikleri ve hastaların renklendirici içecek tüketim alışkanlıklarının dikkate alınmasının önemli olduğu düşünülmektedir.
Özet (Çeviri)
Objective: The aim of this study was to evaluate and compare the color changes of restorative materials obtained from different definitive crown resins after exposure to tea, coffee, and distilled water for specific periods of time. Materials and Methods: In this study, four different definitive crown resins, including VarseoSmile Triniq (VST), P-Crown v4 (PC), Crowntec (CT), and Alias Dental Crown (ADC), together with the Cerasmart (CS) CAD/CAM block material, were used. A total of 180 specimens were prepared from the crown resins and CAD/CAM material, with 12 specimens in each group for immersion in tea, coffee, and distilled water (n=12). Color measurements were performed at baseline, on the 7th day, and on the 30th day. Color measurements were carried out using a VITA Easyshade V digital spectrophotometer, and color difference values were calculated according to the CIEDE2000 formula. The obtained data were analyzed using SPSS 26.0 software (IBM Corp., Armonk, NY, USA). Repeated measures ANOVA was used for the statistical analysis of L*, a*, b*, and ΔE00 values, and Bonferroni-adjusted multiple comparison tests were performed when significant differences were detected (α=0.05). Results: Material type, solution type, and time factor had statistically significant effects on color change (p<0.05). The highest color change was observed in the PC group immersed in coffee during the 0–30 day period (ΔE00=6.58 ± 1.36), whereas the lowest color change was observed in the VST group immersed in distilled water (ΔE00=0.23 ± 0.11). Overall, specimens immersed in coffee exhibited higher color change values, while the distilled water group showed the lowest color change values. Conclusion: Coffee and tea solutions may cause clinically significant color changes in 3D-printed definitive crown resins and CAD/CAM restorative materials. Therefore, it is important to consider the color stability properties of materials and patients' consumption habits of staining beverages during restorative material selection.
Benzer Tezler
- 3 boyutlu yazıcı ile üretilen daimi kron materyallerine farklı yüzey bitirme ve cila işlemlerinin pürüzlülük ve renk stabilitesi üzerine etkisi
Effect of different surface finishing and polishing procedures on the surface roughness and color stabitily of 3d-printed permanent crown materials
BÜŞRA NUR SERVİ
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. İSA YÖNDEM
- Kahve ısıl döngüsünün eklemeli ve eksiltmeli yöntemler ile üretilen daimi kron materyallerinin mikrosertliği, yüzey pürüzlülüğü, yüzey özellikleri ve renk stabilitesi üzerindeki etkisi
The effect of coffee thermal cycling on the microhardness, surface roughness, surface properties, and color stability of permanent crown materials manufactured via additive and subtractive techniques
NURGÜL ERSOY
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiFırat ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. SAMET TEKİN
- Farklı fırınlama sayılarının CAD-CAM ve 3D yazıcı ile üretilen zirkonyanın faz değişimi, optik ve mekanik özelliklerine etkisinin incelenmesi
Investigation of the effect of different firing numbers on phase change, optical and mechanical properties of CAD-CAM and 3D printed zirconia
FURKAN KARATAŞ
Doktora
Türkçe
2024
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ALPER ÖZDOĞAN
- Eklemeli imalat yöntemi ile üretilen farklı kalınlıklarda daimi kron materyallerinin artık monomer içeriğinin karşılaştırılması
Comparison of residual monomer content in permanent crown materials fabricated by additive manufacturing at different thicknesses
AYBÜKE KARA
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiFırat ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ AYŞE RENÇBER KIZILKAYA
- Farklı post-polimerizasyon uygulamalarının eklemeli yöntem ileüretilen daimi kron rezinlerinin aşınmaları üzerine etkisi
The effect of different post-polymerization methods on the wear ofadditively manufactured permanent crown resins
MERVE SOYDAN
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiHatay Mustafa Kemal ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ TAHA YAŞAR MANAV