Yüksek sıcaklık minerallerinden psödowollastonitin seramik ürünlerde mekanik ve kimyasal dayanıma etkileri

The Effect of pseudowollastonite a high temperature mineral, on the mechanical and chemical resistance of ceramic products

  1. Tez No: 125302
  2. Yazar: NERGİS KILINÇ
  3. Danışmanlar: Y.DOÇ.DR. NECDET SAKARYA
  4. Tez Türü: Yüksek Lisans
  5. Konular: Arkeometri, Güzel Sanatlar, Archaeometry, Fine Arts
  6. Anahtar Kelimeler: Yüksek Sıcaklık Mineralleri, Psodowollastonit, Forsterit, Mikromorfoloji, Fırınlama Programı, High temperature minerals, pseudowollastonite, forsterite, micromorphology, furnacing progrmme
  7. Yıl: 2002
  8. Dil: Türkçe
  9. Üniversite: Çukurova Üniversitesi
  10. Enstitü: Sosyal Bilimler Enstitüsü
  11. Ana Bilim Dalı: Seramik Ana Sanat Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 158

Özet

ÖZET YÜKSEK SICAKLIK MİNERALLERİNDEN PSÖDOWOLLASTONİTİN SERAMİK ÜRÜNLERDE MEKANİK VE KİMYASAL DAYANIMA ETKİLERİ Nergis KILINÇ Yüksek Lisans Tezi, Seramik Anasanat Dalı Danışman: Yrd. Doç. Dr. Necdet SAKARYA Haziran 2002, 158 Sayfa Bu çalışmada uygun firın programlan geliştirerek kalsiyum içerikli hammaddelerle psodowollastonit (CaSiCb) yüksek sıcaklık mineralinin oluşturulması ve bu mineralin seramik ürünlerin mekanik ve kimyasal dayanıma etkilerinin araştırılması amaçlanmıştır. Çalışmada kil-kaolen-dolomit üçgen diyagramları üzerinde 12 adet nokta seçilmiştir. 250u.m'luk eleklerden geçirilen hammaddelerin bu noktalardaki karışımları hazırlanmıştır. El presi ile şekillendirilen deney tabletleri 1000°C, 1150°C ve 1200°C'deki sıcaklıklarda sırayla 2°C/dk firm programı ile 5, 3, 1 saat finnlanmıştır. Fırınlanmış her bir tabletin sertlik, su emme ve pişme küçülme değerleri yüzde olarak hesaplanmıştır. Bu örnekler içerisinde en az su emme ve en fazla sertlik gösteren tabletler toz haline getirilerek x-ışını kırınımı analizleri yapılmış ve her bir sıcaklık için ikişer deney örneği taramalı elektron mikroskobunda incelenmiştir. Çalışmada oluşması beklenen psodowollastonit yüksek sıcaklık minerali yerine forsterit (Mg2Si04) yüksek sıcaklık mineralinin oluştuğu saptanmıştır. Kil düzeyi yüksek olan tabletlerin en az su emme değerine sahip olduğu ve bünyede sıcaklığın artmasıyla kil kütanlan/plakalan/agregatlan oluşarak sert yapı kazandıkları saptanmıştır.

Özet (Çeviri)

m ABSTRACT THE EFFECT OF PSEUDOWOLLASTONITE, A HIGH TEMPERATURE MINERAL, ON THE MECHANICAL AND CHEMICAL RESISTANCE OF CERAMIC PRODUCTS Nergis KILINÇ MSc. Thesis, Department of Ceramic Arts Supervisor: Yrd. Doç. Dr. Necdet SAKARYA June 2002, 158 Pages The formation of pseudowollastonite, a high temperature mineral, using calcium rich raw materials at proper furnacing programs along with the determination of its effect on the mechanical and chemical resistance of the ceramic products were studied. On the clay-kaolen-dolomite mixture triangle 12 mixture points were selected and selected mixtures were prepared following sieveing from 250um sieves. The experimental bars, prepared by hand press, were fired at temperatures of 1000°C, 1150^ and 1200°C for 5, 3 and 1 hours respectively with 2°C/m furnacing program. Each bar is analysed for its strength, water absorption and firing shrinkage properties, and the ones with lowest water absorption and highest strenght values were grinded for X-ray diffraction analysis. Moreover, scanning electron microscope analyses were undertaken on two experimental tablets for each firing temperatures. Instead of expected pseudowollastonite formation, forsterite (MgiSiO^, another high temperature mineral, was developed in the experimental mixtures. Results revealed that bars with high clay content have lowest water absorption rates, and with the increase of firing temperature in the core, the formation of clay coating/plates/aggregates seemed to have strenghten the body.

Benzer Tezler

  1. Serpantin minerallerinin faz değişimlerinin incelenmesi: Guleman ofiyoliti örneği

    Investigation of phase changes of serpentine minerals: Guleman ophiolite example

    ÖZKAN YILDIRIM

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Jeoloji MühendisliğiFırat Üniversitesi

    Jeoloji Mühendisliği Ana Bilim Dalı

    DOÇ. DR. AYŞE DİDEM KILIÇ

  2. Investigation of the inhibition characteristics of different polyamines under several temperature and shale contamination conditions in drilling fluids

    Sondaj akışkanlarında farklı sıcaklıklarda ve şeyl kirlenmesi şartlarında farklı poliaminlerin şeyl inhibitör özelliklerinin incelenmesi

    BERFİN ÇIRA

    Yüksek Lisans

    İngilizce

    İngilizce

    2023

    Petrol ve Doğal Gaz Mühendisliğiİstanbul Teknik Üniversitesi

    Petrol ve Doğal Gaz Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ YILDIRAY PALABIYIK

    DOÇ. DR. MUSTAFA HAKAN ÖZYURTKAN

  3. Çeşitli bor minerallerinden hidrofobik ve nanoyapılı çinko borat üretim yöntemlerinin geliştirilmesi

    The development of production methods of hydrophobic and nano zinc borate from different boron minerals

    EMRE ÖZTÜRK

    Yüksek Lisans

    Türkçe

    Türkçe

    2011

    Kimya MühendisliğiYıldız Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. NURCAN TUĞRUL

  4. Kolemanitin borik asit çözeltilerindeki çözünürlüğü

    Başlık çevirisi yok

    MUHAMMET HAMDİ DEMİRHAN

    Yüksek Lisans

    Türkçe

    Türkçe

    1993

    Kimya MühendisliğiAtatürk Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. M. MUHTAR KOCAKERİM

  5. Uleksitten borik asit üretiminin optimizasyonu

    Başlık çevirisi yok

    SİNAN YAPICI

    Yüksek Lisans

    Türkçe

    Türkçe

    1987

    Kimya MühendisliğiAtatürk Üniversitesi

    DOÇ. DR. M. MUHTAR KOCAKERİM