Magnezyum alaşımlarının korozyonu ve FBB kaplamaların korozyon davranışlarına etkisi

Corrosion of magnesium alloys and the effect of PVD coatings on the corrosion behaviour

PDF İndir

  1. Tez No: 155619
  2. Yazar: HİKMET ALTUN
  3. Danışmanlar: DOÇ.DR. SADRİ ŞEN, PROF.DR. HANİFİ SARAÇ
  4. Tez Türü: Doktora
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Magnezyum alaşımları, korozyon, FBB, Magnesium alloys, corrosion, PVD
  7. Yıl: 2004
  8. Dil: Türkçe
  9. Üniversite: Atatürk Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 156

Özet

Magnezyum ve alaşımları, birçok uygulama için çok iyi fiziksel ve mekanik özelliklere sahiptir. Özellikle yüksek mukavemet/ağırlık oram, magnezyumu, hafifliğin oldukça önemli olduğu otomotiv ve uzay endüstrisinde ideal bir metal durumuna getirir. Bunun sonucu olarak bu hafif alaşımlar, ümit verici bir geleceğe sahiptirler. Bununla birlikte, magnezyum ve alaşımları korozyona karşı dayanıksızdırlar. Bu durum, saldırgan çalışma koşullarının kaçınılmaz olduğu otomobil ve uzay endüstrisinde bu alaşımların kullanımını sınırlamaktadır. Korozyonu önlemenin en basit yolu, çevresiyle temasım önlemek amacıyla magnezyum esaslı taban malzemeyi kaplamaktır. Bu çalışmada önce, magnezyum esaslı AZ63 magnezyum-alüminyum-çinko alaşımının NaCl ve Na2SC*4 çözeltileri içerisindeki korozyon davranışına, çözeltinin pH değerinin ve konsantrasyonunun etkisi araştırılmıştır. Bunun için ağırlık kaybı ve potansiyodinamik polarizasyon deneylerinden yararlanılmıştır. Daha sonra ise, AZ31, AZ61, AZ63 ve AZ91 magnezyum alaşımları üzerine fiziksel buhar biriktirme (FBB) kaplama tekniği kullanılarak, DC manyetik alanda sıçratma (magnetron sputtering) yöntemiyle tek tabakalı A1N, üç tabakalı A1N (A1N+A1N+A1N) ve AlN+TiN kaplamalar yapılmış ve bu kaplamaların belirtilen magnezyum alaşımlarının korozyon davranışlarına etkisi incelenmiştir. Elektrokimyasal korozyon deneylerinde potansiyostat, kaplama işlemlerinde FBB kaplama sistemi, kaplamaların bileşim analizlerinde X-ışını difraktometresi (XRD) ve yüzey incelemelerinde taramalı elektron mikroskobu (TEM) cihazları kullanılmıştır. Magnezyum alaşımlarının NaCl ve Na2SC*4 çözeltileri içerisindeki korozyon hızının artan konsantrasyon ve azalan pH değeriyle genellikle arttığı belirlenmiştir. Magnezyum alaşımları üzerine DC manyetik alanda sıçratma tekniğiyle yapılan kaplamaların, özellikle maruz kalınan çözelti çok aşın saldırgan olmadığında bu alaşımların korozyon direncini artırdığı; ancak korozyondan koruma yeteneğini belirleyen temel parametrenin, kaplama tabakaları içerisinde mevcut olan ve kaplama prosesi ile taban malzemeden kaynaklanabilen gözenek, boşluk, çatlak vb. küçük yapısal kusurlar olduğu tespit edilmiştir. 2004, 140 sayfa

Özet (Çeviri)

Magnesium and its alloys have excellent physical and mechanical properties for a number of applications. In particular its high strength to weight ratio makes it an ideal metal for automotive and aerospace applications, where low weight is of significant concern. As a consequence, this light alloys have a promising future. However, magnesium and its alloys are susceptible to corrosion. This has limited their use in the automotive and aerospace industries, where exposure to aggressive service conditions is unavoidable. The simplest way to avoid corrosion is to coat the magnesium-based substrate to prevent contact with the environment. In this study, firstly, the effect of solution pH and concentration on the corrosion behaviour of magnesium-based AZ63 magnesium-aluminum-zinc alloy in NaCl and Na2SÛ4 solutions was investigated. For this purpose, the weight-loss and potentiodynamic polarization tests were used. Afterwards, single-layered A1N, multilayered A1N (A1N+A1N+A1N), and AIN+TiN were coated on the magnesium alloys (AZ31, AZ61, AZ63, and AZ91) using physical vapour deposition (PVD) technique of DC magnetron sputtering, and the influence of the coatings on the corrosion behaviour of the magnesium alloys was examined. A potentiostat for electrochemical corrosion tests, a PVD coating system for coating processes, X-ray difractometer (XRD) for compositional analysis of coating, and scanning electron microscopy (SEM) for surface examinations were used. It was determined that the corrosion rate of magnesium alloys in NaCl and Na2S04 solutions generally increased with increasing concentration and decreasing pH value. It was also determined that DC magnetron sputtering coatings deposited on magnesium alloys increased the corrosion resistance of these alloys especially when the solution exposed wasn't very aggressive, however the basis factor determining the ability of protection from corrosion was small structural defects in the coating, e.g. pores, pinholes, cracks that could arise from the coating process or substrate. 2004, 140 pages

Benzer Tezler

  1. Tez No

    223228

    Katodik ark FBB yöntemi ile Ti6Al4V altlık malzemesi üzerine kaplanmış magnezyumun morfolojisine bias geriliminin etkisi

    Effects of bias voltage on the morphology of magnesium coatings deposited on Ti6Al4V substrates via cathodic arc PVD

    GİZEM OKTAY

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    İleri Teknolojiler Ana Bilim Dalı

    DOÇ.DR. ALİ ARSLAN KAYA

    PROF.DR. MUSTAFA ÜRGEN

  2. Tez No

    636351

    Investigation of the effect of micro arc oxidation and shot peening on corrosion and wear behavior of AZ31- xLaand AZ31-xNd alloys

    AZ31-xLa ve AZ31-xNd alaşımlarının aşınma ve korozyon direncine mikro ark oksidasyon ve bilyeli dövme isleminin etkisinin incelenmesi

    GALAL ELMENSOURI

    Doktora

    İngilizce

    İngilizce

    2020

    Metalurji MühendisliğiKarabük Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    Prof. Dr. HAYRETTİN AHLATCI

  3. Tez No

    718478

    Plazma püskürtme tekniği ile magnezyum ve alaşımlarının TiO2 ve Al2O3 kaplanması ve korozyonu

    TiO2 and Al2O3 coating and corrosion of magnesium and its alloys by plasma spray technique

    TUĞBA BAYRAM

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Metalurji MühendisliğiAfyon Kocatepe Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. YUSUF KAYALI

  4. Tez No

    812195

    T6 ve derin kriyojenik ısıl işlemleri uygulanmış alüminyum esaslı magnezyum alaşımlarının mikroyapı, aşınma ve deniz suyu korozyonu performansının incelenmesi

    Investigation of microstructure, wear and seawater corrosion performance of T6 and deep cryogenic heat treated aluminum based magnesium alloys

    BURAK KARAHİSAR

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Havacılık MühendisliğiEskişehir Osmangazi Üniversitesi

    Havacılık Bilimi ve Teknolojileri Ana Bilim Dalı

    DOÇ. MUSTAFA ÖZGÜR ÖTEYAKA

  5. Tez No

    352165

    Elektriksiz Ni-B kaplamaların magnezyum alaşımlarının korozyon davranışına etkisinin belirlenmesi

    The effect of electroless Ni-B coating on the corrosion behaviour of magnesium alloys

    HAMED AKBARI KHANTAKHTI

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    Makine MühendisliğiAtatürk Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. HİKMET ALTUN

Geri Dön