Küresel grafitli dökme demirde kısmi östenitleme ve östemperleme ısıl işleminin mikroyapı ve mekanik özellikler üzerine etkisi

Effect of partially austenisation and austempering haet treatment on microstructures and mechanical properties in ductile cast iron

  1. Tez No: 155958
  2. Yazar: VOLKAN KILIÇLI
  3. Danışmanlar: DOÇ.DR. MEHMET ERDOĞAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Teknik Eğitim, Metallurgical Engineering, Technical Education
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2004
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 139

Özet

Bu çalışmada, kritik sıcaklıklardan östemperlemenin alaşımsız küresel grafitti dökme demirin mikroyapı ve çekme özellikleri üzerine etkisi incelenmiştir. Bu amaçla %3,50 C, %2,63 Si, %0,318 Mn, %0,0471 Mg, %0,019 P ve %0,009 S içeren ferritik küresel grafitti dökme demir, 795 °C, 805 °C ve 815 °C kritik sıcaklıklarda 20 dk tavlamanın ardından 365 °C'de 30, 60, 90, 120, 150 ve 180 dk süre tie östemperlenmiştir. İnce ösferritik morfolojiye sahip numuneler elde etmek amacıyla bir grup numuneler 900 °C den su verilmiş ve daha sonra kritik tavlama sıcaklıklarından östemperlenmiştir. Mekanik özellikleri karşılaştırma amacıyla bir grup numuneler geleneksel olarak östemperlenmiştir (900 °C de tavlama+365 °C de farklı sürelerde östemperleme). Sonuçlar artan kritik tavlama sıcaklığı ile birlikte ösferrit hacim oranının arttığım göstermiştir, ösferrit hacim oram artışı ile akma ve çekme dayanımı artmış, % uzama ve kesit alanı daralmasının azalmıştır. Ancak kaba ösferritik yapıya sahip numunelerde, çekme özeltiklerindeki bu değişim ince ösferritik yapıya sahip numunelere göre daha az olmuştur. Kritik sıcaklıklarından östemperlenmiş(kaba ösferrit morfolojisine sahip) numunelerde, yeni ferrit (epitaksiyel ferrit) fazının varlığı tespit edilmiştir. Artan kritik tavlama sıcaklığı ve östemperleme süresi ile yeni ferrit hacim oranı da artmıştır. Kaba ösferrit morfolojisine sahip numunelerde 90-150 dk aralığında, ince ösferrit morfolojisine sahip numunelerde ise 60-120 dk aralığında optimum çekme dayanımı-% uzama kombinasyonları sağlanmıştır. Kritik sıcaklıklarda tavlanmış ve östemperlenmiş küresel grafitli dökme demirlerin (çift fazlı matris yapıya sahip küresel grafitli dökme demirlerin) çekme özellikleri, ASTM standart küresel grafitli dökme demirlerin çekme özellikleri ile karşılaştırıldığında, % uzama olarak geleneksel östemperleme ısıl işlemi uygulanmış, ferritik ve perlitik küresel grafitli dökme demir sınıflarına göre daha fazla, bununla beraber dayanımları geleneksel östemperleme ısıl işlemi uygulanmış küresel grafitli dökme demirlerden daha düşük, ancak ferritik ve perlitik küresel grafitli dökme demirlerden, daha fazla olduğu belirlenmiştir.Anahtar Kelimeler : Östemperlenmiş Küresel Grafitli Dökme Demir(ÖKGDD), Çift Fazlı Matrisli Yapı (ÇFM), Ösferrit Hacim Oranı, Kritik Tavlama Sıcaklığı, Yeni Ferrit (Epitaksiyel Ferrit)

Özet (Çeviri)

In this study, effect of austempering from intercritical annealing temperature on microstracture and tensile properties of unalloyed ductile cast iron were investigated. For this aim, ferritic ductile cast iron containing 3.50 %C, 2.63 %Si, 0,318 %Mn, 0.047 %Mg, 0.019 %P and 0.009 %S were annealed at intercritical annealing temperature of 795 °C, 805 °C and 815 °C for 20 min and then austempered at 365 °C for 30, 60, 90, 120, 150 and 180 min. To obtain fine ausferritic morphology some part of specimens were quenched from 900 °C and then austempered from intercritical annealing temperatures. To compare mechanical properties some part of specimens were conventionally austempered (annealing at 900 °C+austempered at 365 °C for various times). The results showed that ausferrite volume fraction increased with increasing intercritical annealing temperature. The, proof and tensile strength increased and % elongation and reduction in area decreased with increasing ausferrite volume fraction. However this change in tensile properties at coarse ausferritic structures were lower than specimens with fine ausferritic structures. The existence of new ferrite phase was found out in the specimen with coarse ausferritic structure austempered from intercritical annealing temperatures. New ferrite volume fraction increased with increasing intercritical annealing temperature and austempering time. Optimum combinations of tensile strength- elongation were obtained 90-150 min for coarse ausferrite morphology and 60- 120 min for fine ausferrite morphology. When tensile properties of intercritically annealed and austempered ductile cast irons (austempered ductile iron with dual matrix structures) compared to tensile properties of ASTM standard ductile irons, elongation of DMS structures was much higher than conventional austempered, ferritic-pearlitic ductile cast irons grades. However their strength lowers than conventional austempered ductile cast iron but higher than ferritic and pearlitic ductile irons grades.Key Words : Austempered Ductile Iron (ADI), Dual Phase Matrix Structure, (DMS), Ausferrite Volume Fraction, Intercritical Annealing Temperature, New Ferrite (Epitaxial Ferrite)

Benzer Tezler

  1. Östemperleme sıcaklık ve süresinin çift matris yapılı östemperlenmiş küresel grafitli dökme demirin mikroyapı ve mekanik özellikleri üzerine etkisi

    Effect of austempering temperature and time on microstructure and mechanical properties of austempered ductile iron with dual matrix structure

    AHMET UYAR

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Metalurji MühendisliğiGazi Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ VOLKAN KILIÇLI

  2. Östemperlenmiş küresel grafitli dökme demirden dişli üretimi ve yorulma davranışlarının incelenmesi

    Production of gears made up of austempered ductile iron and investigation of their fatigue behaviour

    AHMET SAĞIN

    Doktora

    Türkçe

    Türkçe

    1999

    Metalurji MühendisliğiYıldız Teknik Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    PROF. DR. NİŞAN SÖNMEZ

  3. Küresel grafitli dökme demirde martensit hacim oranı ve partikül boyutunun mekanik özellikler üzerine etkisi

    The Effect of martensite volume fraction and martensite particle size on the mechanical properties of spheroidal cast iron

    MELİKA CERAH

    Yüksek Lisans

    Türkçe

    Türkçe

    2003

    Metalurji MühendisliğiGazi Üniversitesi

    Metal Eğitimi Ana Bilim Dalı

    YRD. DOÇ. DR. KADİR KOCATEPE

  4. Yüksek silisyum, krom, alüminyum ve molibden içeren dökme demirlerin oksidasyon davranışının incelenmesi

    Investigation of the oxidation behaviour of high silicon, chromium, aluminum, and molybdenum containing cast irons.

    MELİH YILMAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ NURİ SOLAK

  5. Küresel grafitli dökme demirde küreleşme oranının mekanik özelliklere etkisinin incelenmesi

    Başlık çevirisi yok

    AYHAN SÖĞÜT

    Yüksek Lisans

    Türkçe

    Türkçe

    1998

    Eğitim ve ÖğretimGazi Üniversitesi

    Metal Eğitimi Ana Bilim Dalı

    DOÇ. DR. MEHMET TÜRKER