Entodontik perforasyonların tamirinde kullanılan üç farklı materyalin sitotoksisite ve antimikrobiyal etkilerinin incelenmesi
Evaluation of cytotoxicity and antimicrobial activity of three different materials used to repair endodontic perforations
- Tez No: 163930
- Danışmanlar: PROF. DR. LALE ZAİMOĞLU
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Antimikrobiyal etkinlik, Dyract AP, IRM, MTA, sitotoksisite, Antimicrobial activity, Dyract AP, IRM, MTA, cytotoxicity
- Yıl: 2005
- Dil: Türkçe
- Üniversite: Ankara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Endodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 118
Özet
93 ÖZET Endodontik Perforasyonların Tamirinde Kullanılan Üç Farklı Materyalin Sitotoksisite ve Antimikrobiyal Etkilerinin İncelenmesi Bu çalışmanın amacı, diş perforasyonlarının tamirinde kullanılan MTA, IRM ve Dyract AP'nin L-929 hücre kültüründe MTT testi ile sitotoksisitesi ile Candida albicans, Enterococcus faecalis ve Streptococcus mutans üzerinde antimikrobiyal etkilerinin agar difüzyon yöntemi ile incelenmesidir. Çalışmanın birinci bölümünde, her bir materyalden 4 mm iç çapında ve 4 mm derinliğinde hazırlanan 12 adet örnek, hücre kültürü plakalarında, üzerine 5 mi DMEM/F12 ilave edilerek 24 ve 48 saat bekletilmiştir. Elde edilen ekstraksiyon sıvıları, L-929 hücre süspansiyonu içeren 96 gözlü hücre kültürü plakalarının her bir gözüne 100 ul yerleştirilmiştir. 24 saatlik inkübasyon süresi sonunda tabletlerden ekstraksiyon sıvıları uzaklaştırılmış ve her bir göze MTT solüsyonu ilave edilerek karanlık bir ortamda 4 saat süre ile bekletilmiştir. Bu sürenin sonunda spektrofotometrede 570 nm'de absorbansları ölçülmüştür. Çalışmanın ikinci bölümünde, materyallerden hazırlanan örnekler Candida albicans, Enterococcus faecalis ve Streptococcus mutans mikroorganizma süspansiyonlarının ekimi yapıldığı agar plaklarına yerleştirilmiştir. 24 ve 48 saatlik inkübasyon süresi sonunda agar plaklarındaki örneklerin etrafında oluşan inhibisyon zonlan ölçülmüştür. Çalışmanın birinci bölümünde 24 ve 48 saatlik deney periyodunda en yüksek hücre canlılığım MTA gösterirken, bunu Dyract AP takip etmiştir. En düşük hücre canlılığım ise IRM göstermiştir. MTA ve IRM'nin hücre canlılığı değerinin 48. saatte bir miktar arttığı gözlenirken bunun istatistiksel olarak anlamlı olmadığı (p>0,05), Dyract AP'nin hücre canlılığı değerinde gözlenen düşüşün ise istatistiksel olarak da anlamlı olduğu (p0,05).
Özet (Çeviri)
94 SUMMARY Evaluation of Cytotoxicity and Antimicrobial Activity of Three Different Materials Used to Repair Endodontic Perforations The aim of this study was to evaluate the cytotoxicity of perforation repair materials MTA, IRM and Dyract AP on L-929 cells with the MTT assay and the antimicrobial effect on Candida albicans, Enterococcus faecalis and Streptococcus mutans using the agar diffusion test. In the first part of this study, twelve 4x4 mm cylinders of each material were fabricated and placed in 5 ml of DMEM/F12 for 24 and 48 hours. One hundred microliters of eluate was transferred to a 96-well plate containing L-929 cell suspension. After 24 hours incubation the extracts were removed from the wells, MTT solution was added to each well and kept in a dark environment for 4 hours. Subsequently, the spectrophotometric absorbance was measured at 570 nm using a spectrophotometer. In the second part of this study, samples of each restorative material were placed on agar plates inoculated with Candida albicans, Enterococcus faecalis, Streptococcus mutans suspensions. After 24 and 48 hours incubation, the diameters of the zones of inhibition were measured. The results of the first part of this study showed that the cell viability rates were largest with MTA, followed by Dyract AP at 24 and 48 hours. IRM presented the lowest cell viability at 24 and 48 hours. At 48 hours, MTA and IRM demonstrated similar slightly increasing cell viability which did not reach statistical significance (p>0,05), whereas Dyract AP exhibited an inhibitory effect on cell viability and the difference was statistically significant (p0,05).
Benzer Tezler
- Furkasyon perforasyonlarının tamirinde kullanılan farklı biyomateryallerin sızdırmazlıklarının karşılaştırılması
Comparison of the sealing properties of different biomaterials used in the repair of furcation perforations
NURSELİ GÜNDOĞDU
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiKocaeli ÜniversitesiEndodonti Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SENA KAŞIKÇI
- Perforasyon tamirinde kullanılan iki farklı materyalin asit ve nötr ortamda sızdırmazlıklarının karşılaştırılması
Comparison of sealing efficiency of two different materials used in perforation repair in acidic and neutral environments
GÜNEY MUSTAFA YÜZER
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiDicle ÜniversitesiEndodonti Ana Bilim Dalı
PROF. DR. SADULLAH KAYA
- Endodontik perforasyonlarda kullanılan maddelerin in vivo olarak değerlendirilmesi
Başlık çevirisi yok
CENGİZ TOPBAŞ
Doktora
Türkçe
1998
Diş HekimliğiAnkara ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF. DR. LALE ZAİMOĞLU
- Alt molar dişlerde furkasyon perforasyonlarının tamirinde kullanılan farklı kalsiyum silikat bazlı materyallerin dişin renklenmesine etkisi: In-vitro çalışma
The effect of different calcium silicate based materials used in the repair of furcation perforation in lower molar teeth on tooth staining: İn-vitro study
SEVİL ZIRHLI
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiKaradeniz Teknik ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. DAVUT ÇELİK
- Perforasyon tedavisinde kullanılan çeşitli materyallerin sitotoksisite ve antimikrobiyal etki yönünden karşılaştırılması
Comparison of cytotoxicity and antimicrobial effects of various materials using for treatment of tooth perforations
ESMA ASUMAN ÇAVDAR TETİK
Doktora
Türkçe
2012
Diş HekimliğiAnkara ÜniversitesiEndodonti Ana Bilim Dalı
PROF. DR. MELTEM DARTAR ÖZTAN