Farklı yapıdaki cam iyonomer esaslıu materyallerin florür serbestlemeleri ve antibakteriyel etkilerinin değerlendirilmesi
Evaluation of fluoride release and antibacterial effects of different types of glass lonomer based materials
- Tez No: 165294
- Danışmanlar: PROF.DR. YILDIRIM BAĞIŞ
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Geleneksel CİS, RMClS, PMKR, florür serbestleme, antibakteriyel aktivite, Conventional GIC, RMGIC, PMRC, fluoride release, antibacterial activity
- Yıl: 2005
- Dil: Türkçe
- Üniversite: Ankara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Diş Hastalıkları ve Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
114 ÖZET Farklı Yapıdaki Cam İyonomer Esaslı Materyallerin Florür Serbestlemeleri ve Antibakteriyel Etkilerinin Değerlendirilmesi Bu çalışmanın amacı, üç farklı geleneksel CİS, üç farklı RMClS ve üç farklı PMKR'in florür serbestleme davranışlarını ve bu materyallerin beş farklı mikroorganizma üzerindeki antibakteriyel etkilerini incelemektir. Araştırma iki kısımdan oluşmaktadır. İlk kısımda, cam iyonomer esaslı materyallerin florür serbestleme davranışları incelenmiştir. Bu amaçla, her materyalden on adet test örneği, iki parçaya ayrılabilen teflon kalıp kullanılarak (8 mm çap X 2 mm yükseklik) hazırlandı. Her örnek 20 mL yapay tükürük içeren plastik kaba yerleştirildi. Kapların kapakları kapatıldı ve 37°C sabit ısı ortamında bekletildi. Toplam 90 adet disk şeklindeki materyalin, 24 saat, 24-48 saat, 48 saat-7 gün, 7-30 gün, 30-90 gün ve 90-180 gün florür salım miktarları florür iyon seçici elektrodu kullanılarak hesaplandı. Araştırmamızın ikinci bölümünde, ilk bölümde test edilen cam iyonomer esaslı materyallerin, beş farklı mikroorganizma üzerindeki antibakteriyel etkileri değerlendirildi. İncelenen her materyalden yedişer örnek, steril şartlar altında, ilk bölümde anlatılan şekilde hazırlandı. Disk şeklindeki örnekler, steril presel yardımıyla, daha önce besi yeri üzerinde hazırlanan yuvalara yerleştirildiler. Her petri kutusunda bir bölge kontrol amaçlı olarak boş bırakıldı. Her bakteri susu için 7 adet 15 cm çapında petri kutusu kullanıldı. Ekimi yapılan petri kutuları, 37°C etüvde inkübe edildi ve 24 saat, 48 saat ve 7 gün sonunda antibakteriyel değerlendirme gerçekleştirildi. Bu değerlendirme, petri kutularının içinde bulunan örneklerin etrafında oluşan inhibisyon zonu kalınlığının bir kumpas yardımıyla ölçülmesi şeklinde yapılmıştır. Florür serbestleme deney sonuçlarına göre, test edilen tüm materyaller, en yüksek miktarda florürü, ilk 24 saatte serbestlemiş, daha sonra bu değerler zamanla birlikte azalmaya başlamıştır. Geleneksel CİS'ların florür salımları arasında ilk 24 saatte en fazla salımı, lonofil Molar (Grup 1.3) 4.97 ppm'lik değerle gerçekleştirmiştir. Bu değer, diğer geleneksel CİS'lardan istatistiksel olarak farklıdır (p<0.01). Araştırmamızda test edilen RMCİS'lar (Grup 1.4-6) incelendiğinde ise, ilk 24 saatteki en fazla florür salimini Vitremer (Grup 1.5)'in 2.26 ppm'lik değerle gerçekleştirdiği görülmektedir. Bu değer, diğer iki RMCİS'dan istatistiksel olarak farklıdır (p<0.01). Araştırmamızda değerlendirmeye alınan PMKR (Grup 1.7-9)'ler incelendiğinde ise, ilk 24 saatteki en fazla florür salimini F2000 (Grup 1.9)'in 0.55 ppm'lik değerle gerçekleştirdiği görülmektedir. Bu sonuç, test edilen diğer PMKR'lerden istatistiksel olarak farklıdır (p<0.01). Çalışmada test edilen bütün cam iyonomer esaslı materyallerin florür salım değerleri karşılaştırıldığında ise, ilk 24 saatlik sürede, en yüksek miktarda florürü, geleneksel CİS' farın serbestlediği, bu materyalleri, RMClS ve PMKR' lerin takip ettiği görülmektedir. Test edilen bütün materyallerin 24-48. saatler arasında serbestledikleri florür miktarları birbirleriyle karşılaştırıldığında, ilk 24 saate benzer şekilde en yüksek miktarda florürü, geleneksel CİS'ların serbestlediği, bu materyalleri, RMClS ve PMKR'lerin takip ettiği görülmektedir.115 Test edilen bütün materyallerin araştırmanın sonunda serbestledikleri florür miktarları birbirleriyle karşılaştırıldığında kümülatif olarak geleneksel CİS'ların RMClS'lardan, RMClS'ların da PMKR'lerden daha fazla florür serbestledikleri görülmektedir. Test edilen tüm materyallerde en fazla antibakteriyel etki ilk 24 saatte oluşmuştur. Vivaglass Liner (2.6. Grup) ve Dyract (2.8. Grup) test edilen hiçbir mikroorganizma üzerinde antibakteriyel etki göstermemiştir. Test edilen tüm cam iyonomer esaslı materyaller arasında test edilen mikroorganizmalar üzerinde en başarılı antibakteriyel etki, bir tür RMCİS olan Vitremer (2.5. Grup) ile hazırlanan örneklerde tespit edilmiştir. Bu sonuç, istatistiksel olarak da diğer gruplardan farklıdır (p<0.01). Geleneksel CİS, RMClS ve PMKR'lerin florür salımı ile antibakteriyel etkileri arasında bir korelasyon yoktur. 7 gün sonundaki antibakteriyel etki ile, 90-180 gün sonundaki florür salımı dikkate alınacak olursa Vitremer (2.5. Grup), her iki test yönteminde de en başarılı sonuçları sergilemiştir.
Özet (Çeviri)
116 SUMMARY Evaluation of Fluoride Release and Antibacterial Effects of Different Types of Glass lonomer Based Materials The aim of this study is to investigate fluoride release potentials and on five different microorganisms the antibacterial effects of three different conventional GIC, three different RMGIC and three different PMCR. This research consists of two parts. The fluoride release behavior of Glass lonomer based materials is studied in the first part. For this reason, 20 disc shaped specimens (8 mm diameter X 2 mm height) were prepared utilising split teflon mould. Each specimen were placed into 20 ml artificial saliva in plastic containers. The lid of the containers were closed and the containers kept in standart temperature 37 °C. The fluoride release values of total 90 disc shaped specimens were recorded after 24 hour, 24-48 h, 48 hours-7 days, 7-30 days, 30-90 days and 90-180 days by the help of ion sellective electrode. In the second part, the antibacterial effects of the Glass lonomer based materials which studied in the first part on five different microorganisms were studied. Seven disc shaped specimen prepared for each group under sterile conditions as mentioned previously. Handling the disc shaped specimens with a sterile pressel, they were placed in the holes prepared previously in the medium. One hole left empty as a controle group. For every bacteria, 7 Petri dishes of 15 cm in diameter were used. Petri dishes incubated in a sterilizer at 37 °C and antibacterial evaluation realized after 24 hours, 48 hours and 7 days. This evaluation realized by way of a mesurement of inhibition zones that formed around specimens with a compass. According to the fluoride release results, every material displayed the highest fluoride release values in the first 24 h period and decreased in the latest measurements. In the conventional Glass lonomer group lonofil Molar (Group 1.3) displayed the highest fluoride, release value, with 4.97 ppm, in the first 24 h period. This group found significantly different than the other conventional Glass lonomer groups (p<0.01). In the RMGIC group in the first 24 h Vitremer (Group 1.5) released the highest fluoride with 2.26 ppm than the other two RMGIC's (Group 1.4-6). This value is statistically different than the other RMGIC groups (p<0.01). In the PMRC group (Group 1.7-9) F2000 (Group 1.9) released the highest fluoride with 0.55 ppm in the first 24 h period. This value is statistically different than the other RMGIC groups (p<0.01). When comparing all the Glass lonomer based groups in the first 24 h period GIC's displayed the highest fluoride release value. RMGIC's and PMRC's displayed lower values than GIC's respectevely. The 24-48 h fluoride release values, similar to the 24 h values GIC's displayed the highest fluoride release value. RMGIC's and PMRC's displayed lower values than GIC's respectively. When comparing all the Glass lonomer based groups at the end of the study, conventional GIC's released more fluoride than RMGIC's and RMGIC's released more fluoride than PMRC's cumulatively.117 The highest antibacterial effect observed in the first 24 h period in all test groups. No antibacterial effect was observed considering Vivaglass Liner (Group 2.6) and Dyract (Group 2.8). Vitremer (Group 2.5) a RMGIC showed the highest antibacterial effect upon all Glass lonomer based materials and the values displayed significant differences than other groups' values (p<0.01). There is no corelation between fluoride release potentials of GIC, RMGIC and PMRC and their antibacterial effect. When considering the antibacterial effect after 7 days and fluoride release values after 90-180 days Vitremer (Group 2.5) displayed the most successful results.
Benzer Tezler
- Farklı yapıdaki cam iyonomer esaslı restoratif materyallerin polimerizasyonu esnasında süt dişi pulpa odasında oluşan sıcaklık değişikliklerinin değerlendirilmesi
The evaluation of the temperature changes in primary teeth pulp chamber during the polymerization of different glass ionomer based restorative materials
ÇİĞDEM ÇUKURCU
Diş Hekimliği Uzmanlık
Türkçe
2019
Cumhuriyet ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
Yükleniyor...
- Bulkfil uygulamalı farklı yapıdaki restoratif materyallerin fiziksel özelliklerinin karşılaştırılması ve yüzey örtücü ile kaplanmalarının fiziksel özellikleri üzerine etkisinin değerlendirilmesi
The comparison of bulkfill applied restorative materials and the physical effects of surface coating on these materials
GÜLDEN ÇIRALI
- Cam iyonomer cam karbomer giomer ve rezin yapıdaki fissür örtücülerin etkinliklerinin değerlendirilmesi
Başlık çevirisi yok
ZELİHA ERCAN BEKMEZOĞLU
- Dimetakrilat rezin esaslı dental restoratif materyallerden radyoterapi sonrası artık monomer salımı
Residual monomer release from dimethacrylate resin based dental restorative materials after radiotherapy
BÜŞRA GÜLEÇ
Diş Hekimliği Uzmanlık
Türkçe
2024
Atatürk ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
Yükleniyor...
- Cam iyonomer içerikli farklı yapıdaki biyoaktif restoratif materyallerin süt dişlerindeki mikrosızıntı ve bağlanma kuvvetlerinin karşılaştırılması
Comparison of microleakage and shear bond strength of different bioactive restorative materials contained glass ionomer in primary teeth
İNCİ ÇİL
Diş Hekimliği Uzmanlık
Türkçe
2021
Sivas Cumhuriyet ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
Yükleniyor...