Geri Dön

Ferrokrom ark fırın baca tozunun çevresel karakterizasyonu ve stabilizasyonu

Environmental characterization of ferrochrome arc furnace dust and its stabilization

  1. Tez No: 185320
  2. Yazar: ÜLKÜ BULUT
  3. Danışmanlar: Y.DOÇ.DR. MEHMET ERDEM
  4. Tez Türü: Yüksek Lisans
  5. Konular: Çevre Mühendisliği, Environmental Engineering
  6. Anahtar Kelimeler: Ferrokrom, ark fırın baca tozu, krom(VI), stabilizasyon, solidifikasyon, TCLP, Ferrochrome, arc furnace dust, hexavalent chromium, stabilization, solidification, TCLP.II
  7. Yıl: 2006
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Çevre Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 80

Özet

ÖZETYÜKSEK L SANS TEZFERROKROM ARK FIRIN BACA TOZUNUN ÇEVRESEL KARAKTER ZASYONUVE STAB L ZASYONUÜlkü BULUTFırat ÜniversitesiFen Bilimleri EnstitüsüÇevre Mühendisliği Anabilim Dalı2006 Sayfa: 68Yapılan bu çalışmada, paslanmaz çelik ana hammaddesi olan ferrokrom üretimindeoluşan ark fırın baca tozunun (AFBT), değişik şartlar altındaki çözünürlük özellikleri ve TCLPtestiyle kirlilik potansiyeli incelenmiş ve kirletici bileşenler belirlenerek örneğe değişikstabilizasyon/solidifikasyon işlemleri uygulanmıştır. Ayrıca, elde edilen tüm stabilize/solidifiyeürünlerin de benzer şartlardaki çözünürlük özellikleri ve kirlilik potansiyelleri incelendi.Çözünürlük deneylerinde, çinko ve krom hariç AFBT'dan çözünen diğer metalikbileşenlerin konsantrasyonunun tayin limitlerinin altında kaldığı belirlendi. Ancak, krom veçinko pH, temas süresi ve sıvı/katı oranına bağlı olarak farklı konsantrasyonlarda çözeltiyegeçti. TCLP testiyle AFBT'den çözünen krom konsantrasyonunun müsaade edilen maksimumkonsantrasyon değeri olan 5 mg/l'nin üzerinde ve 9.8 mg/l olduğu bulundu. TCLP testsonuçlarına göre, AFBT'nin önemli bir kirletici potansiyeline sahip zararlı bir atık olduğusonucuna varıldı.AFBT'nin stabilizasyon/solidifikasyonu için, Portland çimentosu, Portland çimentosu-FeSO4, Portland çimentosu-kum, Portland çimentosu-kum-FeSO4, uçucu kül ve uçucu kül-FeSO4 karışımları kullanılmış ve aşağıdaki sonuçlar elde edilmiştir:Yalnızca Portland çimentosu kullanıldığında, katyonik formdaki metaller stabilizeolmasına rağmen, numunedeki Cr(VI)'nın Portland çimentosu ilavesine bağlı olarakdeğişmediği ve çözünür kromat formunda kaldığı tespit edilmiştir. Ayrıca, AFBT'nin puzzolanözelliğe sahip olmamasından dolayı yapısal sağlamlığın da zayıf olduğu görülmüştür. Portlandçimentosu-FeSO4 karışımı ile yapılan stabilizasyon/solidifikasyon deneylerinde, artan Portlandçimentosu ve FeSO4 miktarıyla Cr(VI) stabilizasyon etkinliği artmıştır. Optimum Portlandçimentosu ve FeSO4 dozu sırasıyla, % 30 ve AFBT'nın Cr(VI) içeriğine göre Cr(VI)'nın Fe(II)ile indirgenme stokiometrisinden hesaplanan stokiometrik miktarın 5 katı olduğu belirlenmiştir.ncelenen şartlarda etkin bir AFBT stabilizasyonu sağlanmasına rağmen, dayanıklı yekpare birkalıntı elde edilememiştir.AFBT'yi hem stabilize ve hem de solidifiye etmek için, Portland çimentosu-kum vePortland çimentosu-kum-FeSO4 karışımları ile deneyler yapıldı. Yalnızca Portland çimentosu-kum karışımıyla beklenilen Cr(VI) stabilizasyonu elde edilemedi. Ancak, en iyi stabilizasyonAFBT'ye 5 stokiometrik miktar FeSO4, % 30 Portland çimentosu ve % 16 kum karışımı ilaveedildiğinde sağlanabildi.Uçucu kül ve uçucu kül-FeSO4 karışımlarının kullanıldığı stabilizasyon/solidifikasyondeneylerinde sonuçların Portland çimentosu ve Portland çimentosu-FeSO4 karışımı için eldeedilen sonuçlara benzer olduğu bulundu.

Özet (Çeviri)

ABSTRACTMASTER THESISENVIRONMENTAL CHARACTERIZATION OF FERROCHROME ARC FURNACEDUST AND ITS STABILIZATIONÜlkü BULUTFırat UniversityGraduate School of Natural and Applied SciencesDepartment of Environmental Engineering2006, Page: 68In this study, dissolution properties under different conditions and pollution potential byTCLP of arc furnace dust generated in ferrochrome, which is a raw material of stainless steelproduction, production were examined and some stabilization/solidification techniques wereapplied to the dust depending on contaminants determined. Dissolution properties and pollutionpotentials of all the stabilized/solidified materials prepared were also studied under the similarconditions.In the dissolution experiments, it was determined that except for chromium and zinc,metallic components concentration dissolved from AFBT were below the detection limits.However, chromium and zinc in different concentrations released into the solution depending onpH, contact time and liquid/solid ratio. The chromium concentration dissolved from AFBT byTCLP was found to be 9.8 mg/l, is higher than the maximum allowable concentration of 5 mg/l.According to TCLP test results, it was concluded that the AFBT has an important pollutionpotential, it was a hazardous waste.For the stabilization/solidification of the AFBT, Portland cement, Portland cement-FeSO4, Portland cement-sand, Portland cement-sand-FeSO4, fly ash and fly ash-FeSO4 mixtureswere tested and it was found the following results:IWhen the Portland cement was only used, it was determined that although metal ions incationic form were stabilized, Cr(VI) in the sample was not changed depending on Portlandcement addition and remained in the soluble chromate form. Also, weak structural integrity wasobserved due to non-pozzolanic properties of AFBT.In the stabilization/solidification experiments carried out with Portland cement-FeSO4mixture, the stabilization efficiency of Cr(VI) increased by the increasing amounts of Portlandcement and FeSO4. Optimum Portland cement and FeSO4 dosage was determined to be 30 %and 5 times of stoichiometric amount calculated from Cr(VI) reduction stoichiometry by ferrousiron with respect to Cr(VI) content of AFBT, respectively. Even though effective stabilizationof AFBT under the conditions investigated was established, monolithic solid residue could notbe obtained.In order to both stabilize and solidify to the AFBT, Portland cement-sand, Portlandcement-sand-FeSO4 mixtures were also tested. Results expected for Cr(VI) stabilization was notobtained by using Portland cement-sand. However, when the 5 times of stoichiometric amountof FeSO4, 30 % Portland cement and 16 % sand mixture was added to the AFBT, the beststabilization/solidification of AFBT was accomplished.In the stabilization/solidification experiments which were fly ash and fly ash-FeSO4mixtures were used, it was found that the results were similar to that of Portland cement andPortland cement-FeSO4 mixtures.

Benzer Tezler

  1. Geopolimer katkılı bitüm ve bitümlü sıcak karışımların performans özelliklerinin yaşam döngüsü değerlendirmesi destekli analizi

    The life cycle assessment supported analysis of the performance characteristics of bitumen and bituminous hot mix incorporating geopolymer

    BURAK YİĞİT KATANALP

    Doktora

    Türkçe

    Türkçe

    2023

    Mühendislik BilimleriEge Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. PERVİZ AHMEDZADE

  2. Recycling of ZnS from wastes and its utilization as an electrode material in supercapacitors

    Atıklardan ZnS'ün geri dönüşümü ve süperkapasitörlerde elektrot malzemesi olarak kullanılmasının araştırılması

    OZAN AYDIN

    Yüksek Lisans

    İngilizce

    İngilizce

    2022

    Metalurji MühendisliğiYıldız Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ BURAK BİROL

    DOÇ. DR. METİN GENÇTEN

  3. Antalya Ferrokrom İşletmesi'nin elektrik-ark fırını cüruflarının ve baca tozu atıklarının asfalt betonunda kullanılabilirliğinin araştırılması

    Investigation of electric-arc furnace slag and silica fume of Antalya Ferrochrome Establishment, as filler material in asphalt concrete

    ALTAN YILMAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2002

    İnşaat MühendisliğiAkdeniz Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. İLHAN SÜTAŞ

  4. Bir ferrokrom tesisinin eksergoekonomik analiz yöntemiyle verimliliğinin değerlendirilmesi

    Evaluation of the efficiency of a ferrochrome plant with exergoeconomic analysis method

    SİNAN KAPAN

    Doktora

    Türkçe

    Türkçe

    2023

    Makine MühendisliğiFırat Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. NEVİN ÇELİK

    PROF. DR. ÜNAL ÇAMDALI

  5. Termik santral ve metalurjik tesis artıklarından yapay zeolit ve geopolimer malzemelerin eldesi

    Production of synthetic zeolite and geopolymer materials from the tailings derived from thermal power plants and metallurgical plants

    SONER TOP

    Doktora

    Türkçe

    Türkçe

    2019

    Kimya MühendisliğiÇukurova Üniversitesi

    Maden Mühendisliği Ana Bilim Dalı

    PROF. DR. HÜSEYİN VAPUR

    DR. ÖĞR. ÜYESİ MİNE TAYKURT DADAY