Demir III(Fe+3), demir II (Fe+2) iyonları ile modifiye edilmiş beydellit minerali varlığında azo boya çözeltisinin heterojen foto fenton oksidasyonu.

Heterogeneous photo fenton oxidation of an azo dye solution by using beidellite as a catalyst modifed by iron (III) (Fe+3) and iron (II) (Fe+2)

  1. Tez No: 238668
  2. Yazar: GAYE SAĞLAR KESER
  3. Danışmanlar: YRD. DOÇ. DR. H. CENGİZ YATMAZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Çevre Mühendisliği, Chemical Engineering, Environmental Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2009
  8. Dil: Türkçe
  9. Üniversite: Gebze Yüksek Teknoloji Enstitüsü
  10. Enstitü: Mühendislik ve Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Çevre Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 97

Özet

Bu çalışmada, tekstil endüstrisinde kullanılan Reactive Mono Azo Remazol Brillant Orange 3R (C.I. Reactive Orange 16) boya çözeltisinin Fe+3 ve Fe+2 iyonları ile modifiye edilmiş beydellit minerali varlığında heterojen foto Fenton oksidasyonunda renk giderim verimleri incelenmiştir.İki farklı UVA dalga boyunda ve kaşılaştırmalı olarak UVC dalga boyunda kullanılarak Beydellit üzerine yüklü Fe+3 ve Fe+2 iyonlarının renk giderim verimleri incelenmiş ve homojen foto Fenton prosesi ile verim karşılaştırması yapılmıştır.Yapılan çalışmalarda boya konsantrasyonu 50 mg/L, katalizör konsantrasyonu 1 g/L, hidrojen peroksit(H2O2) konsantrasyonu 15mmol, sıcaklık 35 oC, pH çözeltinin başlangıç pH ı olan 5.2 olarak alınmış ve Fe+2 yüklü beydellit'in Fe+3 yüklü Beydellit'e göre daha iyi renk giderim performansı gösterdiği görülmüş, homojen prosesler ile karşılaştırıldığında ise Fe+2 yüklü Beydellit'in homojen prosesler kadar iyi verim verdiği görülmüştür.UVA dalga boyundaki lambaların her ikisininde benzer verim verdiği, yapay ışık dalga boyu olan UVC deki verimin yüksek olmasına rağmen, UVA'da elde edilen verimin reaksiyon süresi sonunda (120dk) benzer verimi verdiği gözlemlenmiştir.Fe+3 ve Fe+2 beydellit minerallerinin yeniden kullanımında verimin düştüğü gözlenmiştir.Yapılan toplam organik karbon (TOC) ölçümlerinde ise Fe+2 beydellit kullanıldığında mineralizasyon veriminin UVA için %55.7, UVC için ise %94.2 olarak belirlenmiştir.

Özet (Çeviri)

In this study, color removal efficiency of Reactive-Mono Azo dye solution was investigated by heterogeneous photo Fenton oxidation using beydellit as a catalyst modified by iron (III), iron (II) ions.Using two different types of UVA lamps and also UVC lamps, color removal efficiency of Fe+3 and Fe+2 ions modified beidellite was performed and efficiencies were compared against homogenous photo Fenton process.By selecting the dye concentration 50 mg/L, the catalyst loading 1 g/L, hydrogen peroxide (H2O2) concentration 15 mmol, temperature 35oC and the solution pH as 5.2; it was found that Fe+2 modified beydellite has given better results against Fe+3 modified beidellite for color removal efficiency and Fe+2 modified beidellite has also given as good color removal efficiency as the homogenous processes.It was also seen that the both UVA type of lamps has given almost the same efficiency. Although UVC lamp type has performed better efficiency, UVA lamp type had the same effect at the end of reaction period (120 min).It was observed that color removal efficiency was dropped when the re-use of same Fe+3 and Fe+2 modified beidellite catalysts.Finally after (TOC) analysis, the mineralization efficiencies were 55.7% for UVA and 94.2% for UVC lamp types when Fe+2 modified beidellite catalysts were used.

Benzer Tezler

  1. Demir III (Fe+3), demir II (Fe+2), bakır II (Cu+2), seryum IV (Ce+4) iyonları ve bu iyonların karışımı ile modifiye edilmiş zeolit minerali varlığında azo boya çözeltisinin heterojen foto oksidasyonu

    Heterogeneous photo fenton oxidation of an azo dye solution by using zeolite as a catalyst modifed by iron (III), iron (II), copper (II), cerium (IV) ions and bimetals (Fe+3?Ce+4, Fe+3?Cu+2)

    DERYA EKİZOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    2008

    Kimya MühendisliğiGebze Yüksek Teknoloji Enstitüsü

    Çevre Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. H. CENGİZ YATMAZ

  2. Developing Fluorescent Sensors for the Bioimaging of Chelatable Iron(III) Ions

    Şelatlanabilir Demir(III) İyonlarının Biyogörüntülenmesi için Floresan Sensörlerin Geliştirmesi

    ZİYA AYDIN

    Doktora

    İngilizce

    İngilizce

    2015

    KimyaUniversity of Massachusetts Amherst

    Kimya Ana Bilim Dalı

    PROF. DR. MAOLIN GUO

  3. Aspartam içeren havalandırılmış çözeltide l-askorbik asidin bakır(II) ve demir(III) katalizli oksidasyon kinetiğinin incelenmesi

    Kinetic study of copper(II)- and iron(III) catalyzed oxidation of l-ascorbic acid in aspartame containing aerated solution

    BİLGE YILDOĞAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2006

    KimyaYıldız Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. İNCİ SÖNMEZĞLU

  4. Kırmızı çamurun değerlendirilmesi

    Utilization of red mud

    YUNUS ÇENGELOĞLU

    Doktora

    Türkçe

    Türkçe

    1991

    Kimya MühendisliğiSelçuk Üniversitesi

    Kimya Ana Bilim Dalı

    PROF.DR. RAMAZAN MİRZAOĞLU