Farklı yöntemlerle şekillendirilmiş CaO/MgO katkılı stabilize edilmiş ZrO2 esaslı seramiklerin fiziksel ve elektriksel özelliklerinin incelenmesi
An investigation on physical and electrical properties of CaO/MgO-stabilized zirconia ceramics formed with different methods
- Tez No: 252202
- Danışmanlar: PROF. DR. A. OKAN ADDEMİR
- Tez Türü: Doktora
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2008
- Dil: Türkçe
- Üniversite: İstanbul Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 150
Özet
Bu çalışmada, Kalsiya(CaO) ve Magnezya(MgO) ile stabilize edilmiş farklı karışımlardaki Zirkonya tozları çalışılmıştır. Toz karışımları (Ca(OH)2, Mg(OH)2 ve ZrO2 ) aseton ortamında yitriya (Y2O3) ile satabilize edilmiş zirkonya bilyeler kullanılarak değirmende hazırlanmıştır. Slip döküm, basınçsız sıcak şekillendirme, kuru presleme ve soğuk izostatik presleme yöntemleriyle şekillendirilmiştir. Daha sonra şekillendirilen numuneler 1300?1700 0C de 1?5 saat süreyle elektrikli fırınlarda normal atmosferde sinterlenmiştir. Sinterlenmiş bazı numuneler 1420 0C de 4 saat yaşlandırılmıştır. Sinterlenmiş numunelerin yoğunluk ve poroziteleri Archimedes metodu ile ölçülmüştür. Sinterlenmiş numunelerin mikroyapısal karakterizasyonu ve analizi taramalı elektron mikroskobu (SEM) ve EDS kullanılarak yapılmıştır. Faz analizleri XRD ile Co K? radyasyonu kullanılarak yapılmıştır. Seramiklerin termal davranışlarının katrakterizasyonunda DTA ve DSC kullanılmıştır. Numunelerin doğru akım elektrik iletkenliğinin ölçünümde platin telli dört nokta ölçüm metodu kullanılmıştır. Ca-ZrO2 ve Mg-ZrO2 seramikler katı hal reaksiyon sentezlenmesiyle hazırlanmış ve elektriksel, fiziksel ve termal özellikleri analiz edilmiştir. t- ZrO2 ve c- ZrO2 fazlarının miktarlarında artan CaO ilavesi, sinterleme sıcaklığı ve sinterleme zamanı ile artış olduğu görülmüştür.
Özet (Çeviri)
In present study, Calcia and Magnesia stabilized fine Zirconia powders in various ratios were studied. Powder mixtures (Ca(OH)2, Mg(OH)2 and ZrO2 ) were prepared in acetone and milled as wet with YSZ (yitria stabilized zirconia) balls. The slip casting, pressureless hot moulding, dry pressing and cold isostatic pressing techniques have been selected for forming of the partial stabilized zirconia with MgO and CaO. After completing this forming process, green ceramics were fired at 1300-1700 0C for 1-5 hours in an electric-heated furnace and then cooled quickly. Some of the fired ceramics were aged in the same furnace for 4 hours at 1420 0C. The density and porosity of sintered samples were measured by Archimedes principle. The microstructural characterization of the sintered samples was carried out using scanning electron microscopy. The morphological parameters of the various phases were characterized by using a semiautomatic image analyzer, EDS and the formed phases were analyzed by X-ray powder diffractometer using Co K? radiation. The thermal behavior of the ceramics was characterized by differential thermal analyzer DTA and DSC. The direct current (d.c.) electrical conductivity of each sample was measured in air using the four - probe method with platinum wire. Ca-ZrO2 and Mg-ZrO2 ceramics have been prepared by solid state reaction synthesis and the beneficial effects on the electrical, physical and thermal properties have been analyzed. t- ZrO2 and c- ZrO2 phase value increased with the addition of Calcia (CaO) and fired temperature and time.
Benzer Tezler
- Iğdır ve çevresindeki yöresel killer, yapısal özellikleri ve seramik kullanım alanları
Local clays of Iğdır and its surroundings, structural properties and usage areas in ceramics
ELÇİN TELLİ ATEŞ
Sanatta Yeterlik
Türkçe
2023
Güzel SanatlarMimar Sinan Güzel Sanatlar ÜniversitesiSeramik ve Cam Ana Sanat Dalı
PROF. NEZİHE LERZAN ÖZER
- Silisyum karbür esaslı ileri teknoloji seramiklerin dökümü, sinterlenmesi ve karakterizasyonu
Slip casting, sintering and characteristics of silicon carbide based high technology ceramics
YUSUF ALPER AKINALP
Yüksek Lisans
Türkçe
2019
Metalurji MühendisliğiSivas Cumhuriyet ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. LEVENT CENK KUMRUOĞLU
- Farklı yöntemlerle üretilmiş döner sistem niti eğelerin vertikal kırık oluşturma düzeylerinin karşılaştırılması
Vertical root fructure resistance of teeth instrumented with differentially manufactured niti rotary files
FATMA FURUNCUOĞLU
Doktora
Türkçe
2015
Diş HekimliğiOndokuz Mayıs ÜniversitesiEndodonti Ana Bilim Dalı
YRD. DOÇ. DR. ELİF KALYONCUOĞLU
- Yüksek karbonlu toz metal çeliklerin mikroyapı ve darbe tokluğu özelliklerine küreselleştirme ısıl işlemleri etkilerinin araştırılması
Investigating the effect of spheroidization heat treatments on the microstructure and impact toughness properties of high carbon powder metal steels
ONUR ALTUNTAŞ
Yüksek Lisans
Türkçe
2013
Metalurji MühendisliğiGazi ÜniversitesiMetal Eğitimi Ana Bilim Dalı
DOÇ. DR. AHMET GÜRAL
- Julia Kristeva ve Judith Butler bağlamında 'özne': Failliğin inşası
'the subject' in the context of Julia Kristeva and Judith Butler: The construction of agency
DERYA ŞENGÜN ÖZEN