Bakır üzerinde pirol ve N-metil pirolün kopolimeri ile çift kaplamalarının sentezi ve korozyon performanslarının araştırılması

Synthesis of copolymer of pyrrole with N-methyl pyrrole and their bilayers on copper and investigation of their corrosion performances

  1. Tez No: 266371
  2. Yazar: İREM ÇAKMAKCI
  3. Danışmanlar: PROF. DR. GÖZEN BEREKET
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya, Chemistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2010
  8. Dil: Türkçe
  9. Üniversite: Eskişehir Osmangazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 133

Özet

Bu çalışmada bakır yüzeyinde elektrokimyasal olarak sentezlenen poli(pirol) filmlerinin su alması, düşük kararlılığı gibi dezavantajları N-metil pirol ile kopolimeri sentezlenerek ve çift kaplamaları yapılarak aşılmaya çalışılmıştır.Bakır elektrotta okzalik asit ortamında farklı monomer oranlarında (Py:NMPy 8:2, 6:4, 5:5, 4:6, 2:8) dönüşümlü voltametri yöntemiyle elektrokimyasal olarak poli(pirol-ko-N-metil pirol) kopolimerleri sentezlenmiştir. Bakır üzerine polipirol/poliN-metil pirol çift kaplaması okzalik asit ortamında dönüşümlü voltametri yöntemiyle biriktirilmiştir.Poli(pirol-ko-N-metil pirol) kopolimerleri ve poli(pirol)/poli(N-metil pirol) çift kaplamaları CV, SEM, ATR-FTIR spektroskopisi yöntemleri ile karakterize edilmiştir. 0,1 M H2SO4 ve % 3,5 NaCl ortamında 8:2 (Py:NMPy) monomer oranında sentezlenen poli(pirol-ko-N-metil pirol)'ün en iyi korozyon performansı verdiği bulunmuştur. PPy-ko-PNMPy ve PPy/PNMPy filmlerinin 0,1 M H2SO4 ve % 3,5 NaCl ortamında zamana bağlı korozyon performansı açık devre potansiyeli-zaman, anodik polarizasyon eğrileri ve elektrokimyasal empedans spektroskopisi yöntemleri ile incelenmiştir. Kaplamaların EIS yöntemiyle performanslarının incelenmesinde Bode eğrilerinden yararlanılmıştır. Bunun için düşük ve yüksek frekanstaki faz açılarının değişimi ile Z-frekans eğrileri altındaki alanların karşılaştırılmasından yararlanılmıştır. Sonuçlar kaplamaların anodik polarizasyondan ve OCP-zaman eğrilerinden elde edilen performans değişimleri ile uyumlu olduğunu göstermiştir.

Özet (Çeviri)

In this study, it was tried to overcome disadvantages of electrochemical synthesized polypyrrole films on copper like water up taking and resulting low stability, via copolymerization of pyrrole and N-methyl pyrrole and preparing their bilayer films.Poly(pyrrole-co-N-methyl pyrrole) copolymer has been synthesized on copper electrode by electrochemical copolymerization different monomer ratio of (Py:NMPy 8:2, 6:4, 5:5, 4:6, 2:8) in aqueous oxalic acid solution by using cyclic voltammetry. The synthesis of PPy/PNMPy bilayer coating was achieved on copper in oxalic acid solution by using cyclic voltammetry technique.Copolymer and bilayer coatings were characterized by CV, SEM, ATR-FTIRspectroscopy. It was found that copolymer film which was synthesized at 8:2 (Py:NMPy) monomer ratio to have the best corrosion performance both in 0.1 M H2SO4 and 3.5% NaCl. Variation of corrosion performances of PPy-co-PNMPy and PPy/PNMPy in 0.1 M H2SO4 and 3.5% NaCl with time was investigated by using open circuit potential - time, anodic polarization curves and electrochemical impedance spectroscopy methods. Bode plots were used in evaluating corrosion performances of coatings with EIS measurements. For this purpose recording the change of phase angle both at low and high frequencies and comparing of area under the Z-frequency plots were used. Results shows that change of performances of these coatings to be the same with the results obtained from anodic polarization and OCP-time curves.

Benzer Tezler

  1. Characterization of pyrrole and thiophene containing polymers and their copolymers

    Pirol ve tiyofen içeren polimer ve kopolimerlerin karakterizasyonu

    GÜRSEL SÖNMEZ

    Doktora

    İngilizce

    İngilizce

    2002

    Kimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. ABDÜLKADİR SEZAİ SARAÇ

  2. N-substituye karbazollerin endüstriyel metallerin korozyonunu önlemedeki etkileri

    Corrosion inhibition effect of N-substituted carbazole on the corrosion of some industrial metals

    SADIK ÖZTÜRK

    Yüksek Lisans

    Türkçe

    Türkçe

    2001

    Kimyaİstanbul Teknik Üniversitesi

    PROF.DR. A. SEZAİ SARAÇ

    Y.DOÇ.DR. ESMA SEZER

  3. N-sübstitüe anilin ve N-sübstitüe pirollerin bakır üzerinde elektropolimerizasyonları ve antikorozif özelliklerinin araştırılması

    Electropolymerizations of N-substituted anilines and N-substituted pyrroles on copper and investigation of their anticorrosive properties

    BERRİN DURAN

    Doktora

    Türkçe

    Türkçe

    2010

    KimyaEskişehir Osmangazi Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. GÖZEN BEREKET

  4. Alkollerin alüminyum-silisyum alaşımları üzerine inhibitör etkisinin elektrokimyasal ve yüzey analiz yöntemleriyle incelenmesi

    Inhibition effect of alcohols on the aluminum-silicon alloys have been investigated by using electrochemical and surface analysis methods

    AYŞEGÜL TÜRK

    Yüksek Lisans

    Türkçe

    Türkçe

    2005

    KimyaAfyon Kocatepe Üniversitesi

    Kimya Ana Bilim Dalı

    Y.DOÇ.DR. AYSEL BÜYÜKSAĞİŞ

  5. Sıcak hava ve kızılötesi kurutma işleminin arı poleninin bazı fiziksel özellikleri ve uçucu bileşen profili üzerine etkisi

    Effect of hot air and infrared drying processes on some physical properties and volatile compound profile of bee pollen

    SEVİNÇ ÇİFTÇİ

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Gıda MühendisliğiOrdu Üniversitesi

    Gıda Mühendisliği Ana Bilim Dalı

    DOÇ. DR. BEKİR GÖKÇEN MAZI