Effect of additives on dielectric properties of Bi1.5Zn0.92Nb1.5O6.92 pyrochlore

Katkıların piroklor yapılı Bi1.5Zn0.92Nb1.5O6.92 seramiklerinin dielektrik özelliklerine etkileri

  1. Tez No: 275936
  2. Yazar: NİSA BAKIR
  3. Danışmanlar: DOÇ. DR. AYHAN MERGEN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2010
  8. Dil: İngilizce
  9. Üniversite: Marmara Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 97

Özet

Bi1.5Zn0.92Nb1.5O6.92 formülüne sahip piroklor bileşikleri yüksek ve ayarlanabilen dielektrik sabiti, düşük dielektik kayıp, sıfıra yakın sıcaklık katsayısı gibi teknolojik olarak faydalı dielektrik özelliklere sahip olup, mikrodalga dielektrik malzeme olarak özellikle kablosuz haberleşmede ve çok katlı seramik kapasitörlerde kullanım alanına sahiptir.Bu proje çalışmasında, oksitlerin karışımı yöntemi kullanılarak Y, Dy, Gd, Eu, Ho, Yb, La ve Cu ilaveleriyle tek fazlı yapıya sahip katkılı Bi1.5Zn0.92Nb1.5O6.92 (BZN) piroklor bileşikleri üretilmiş ve dielektrik özellikleri detaylı bir şekilde incelenmiştir. Her bir katkının BZN bünyesindeki çözünürlük sınırı XRD ve SEM kullanılarak hassas bir şekilde saptanmıştır. Nadir toprak elementlerin katkısıyla çözünürlük sınırlarının üzerinde BZN yapısında genelde ZnO fazının yanında MNbO4 (M=katkılandırılan nadir toprak elementi) ikincil fazı oluşmaktadır ve katkı miktarıyla ikincil fazların miktarı artmıştır. Minimum %97 relatif yoğunluğa sahip olacak şekilde üretilen katkılı BZN seramiklerinin dielektrik özelliklerinin ölçümü farklı dielektrik katsayılarına ve düşük dielektrik kayıplarına sahip seramiklerin üretildiğini göstermiştir. Genel olarak katkılı BZN seramiklerin dielektrik sabiti 1kHz-2MHz aralığında frekansdan bağımsız hareket etmekte ancak 20-200°C aralığında sıcaklık dielektrik sabitini önemli derecede etkilemektedir. Dielektrik kayıplar frekansla genelde düşmekte ancak özellikle belirli bir frekansın üzerinde (~250 kHz) sıcaklıktan az etkilenmektedir. Katkılı BZN seramiklerin dielektrik sabiti sıcaklık katsayısı katkı oranıyla oldukça değişkenlik göstermekte ancak bazı katkılı BZN seramiklerinde katkı oranı arttıkça sıcaklık katsayısı sıfıra yaklaşmaktadır.

Özet (Çeviri)

The pyrochlore compound with a formulation of Bi1.5Zn0.92Nb1.5O6.92, has important technological dielectric properties, like high and tuneable dielectric constant, low dielectric loss, close to zero values of temperature coefficient, can be used as microwave dielectric material in wireless communication sector and in multilayer ceramic capasitors.In this study, single phase Y, Dy, Gd, Eu, Ho, Yb, La and Cu doped Bi1.5Zn0.92Nb1.5O6.92 (BZN) pyrochlore compounds were produced by mixed oxide technique and their dielectric properties were examined in detail. The solubility limit of each additive was determined by XRD and SEM. Generally ZnO and MNbO4 (M=doped rare earth element) phases formed as second phases above the solubility limit in the BZN using rare earth elements and their content increased with dopant amount. Dielectric measurements of doped BZN ceramics having min 97% of relative density indicated that ceramics with various dielectric constants and low dielectric losses were produced. Dielectric constant of doped BZN ceramics was not a function of frequency between 1kHz-2MHz but the temperature had a significant effect on the dielectric constant between 20-200°C. Dielectric losses decreased generally with frequency but the temperature did not affect the dielectric losses especially above ~250 kHz. Temperature coefficient of dielectric constant of doped BZN ceramics varied significantly with dopant content and it approached to zero with higher amount of dopant for some additives.

Benzer Tezler

  1. Production and characterisation of Bi1.5Zn0.92Nb1.5O6.92 pyrochlore ceramics with precious metal oxide additives

    Değerli metal oksit katkılı Bi1.5Zn0.92Nb1.5O6.92 piroklor seramiklerinin üretimi ve karakterizasyonu

    OĞUZ ÖZYOLDAŞ

    Yüksek Lisans

    İngilizce

    İngilizce

    2010

    Metalurji MühendisliğiMarmara Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. AYHAN MERGEN

  2. Katkı malzemelerinin polyester yalıtkanlardaki elektriksel ve mekanik özelliklere etkileri

    Effects of additives on electrical and mechanical properties of polyester insulators

    SEREN ÇELİK

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Elektrik ve Elektronik Mühendisliğiİstanbul Üniversitesi-Cerrahpaşa

    Elektrik-Elektronik Mühendisliği Ana Bilim Dalı

    DOÇ. DR. CENGİZ POLAT UZUNOĞLU

    PROF. DR. MUKDEN UĞUR

  3. E63 kodlu NiPc+C61 katkılı nematik sıvı kristalin elektriksel ve manyetik özelliklerinin incelenmesi

    Investigation of electric and magnetic properties of NiPc and C-61 doped E63 nematic liquid crystal

    ÖMER YILMAZ

    Doktora

    Türkçe

    Türkçe

    2016

    Fizik ve Fizik MühendisliğiYıldız Teknik Üniversitesi

    Fizik Ana Bilim Dalı

    DOÇ. DR. ZEYNEP GÜVEN ÖZDEMİR

  4. Katı hal reaksiyonu ile kordiyerit oluşumuna TiO2, Fe2O3 ve Cr2O3 katkılarının etkisi

    The effect of TiO2, Fe2O3, Cr2O3 additives on formation of cordierite via solid state reaction

    MUZAFFER ŞAMİL ÇINAR

    Yüksek Lisans

    Türkçe

    Türkçe

    2013

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ERDEM DEMİRKESEN

  5. Katı hal reaksiyonuyla kordiyerit sentezine çeşitli katkıların selektif etkisi ve oluşan kordiyeritin termal genleşme davranışının incelenmesi

    The effect of some additives on the synthesis of cordierite via solid state reaction and on the thermal expansion behavior of cordierite

    DEMET AYDOĞMUŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ERDEM DEMİRKESEN