Porselen laminat venerlerin mineye, dentine ve mine-dentin kompleksine adezyonunda farklı rezin simanların kullanılmasının makaslama bağlanma dayanıklılığı üzerine etkisi

Shear bond strength of porcelain laminate veneers to enamel, dentin and enamel-dentin complex bonded with different resin cements

  1. Tez No: 281282
  2. Yazar: ELİF ÖZTÜRK
  3. Danışmanlar: PROF. DR. ŞÜKRAN BOLAY
  4. Tez Türü: Doktora
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2011
  8. Dil: Türkçe
  9. Üniversite: Hacettepe Üniversitesi
  10. Enstitü: Sağlık Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Diş Hastalıkları ve Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 146

Özet

Bu in vitro çalışmanın amacı, üç farklı rezin siman kullanarak porselen laminat venerlerin mine, dentin ve mine-dentin kompleksi olmak üzere üç farklı yüzeye makaslama bağlanma dayanıklılığının değerlendirilmesidir. Çalışmada 135 adet çekilmiş, çürüksüz insan üst santral dişi kullanılmış ve dişler rastgele 9 gruba ayrılmıştır (n=15). Dişler, akrilik kalıplara gömülmüş ve bağlanma yüzeyleri; mine (M), dentin (D) ve mine-dentin kompleksini (M-D) içermek üzere üç farklı seviyede prepare edilmiştir. İki mm kalınlığında ve 4 mm çapındaki porselen diskleri (IPS e.max Press/Ivoclar Vivadent) üretici firmanın önerileri doğrultusunda hazırlanmıştır. Porselen diskleri diş yüzeylerine; ikisi ışıkla [RelyX Veneer (RV); Variolink Veneer (VV)] biri hem kimyasal hem ışıkla [Variolink II (V II)] polimerize olan üç farklı rezin simanın, üretici firmalarının önerileri doğrultusunda uygulanması ile adeziv olarak simante edilmiştir. Tüm örnekler, 5000 döngülük termal siklus işlemine tabi tutulmuştur. Örneklerde, kırılma meydana gelinceye kadar, 0.5 mm/dk hızda çalışan üniversal bir test makinesi (MCE 2000ST, Quicktest Prüfpartner GmbH) ile makaslama bağlanma dayanıklılık testi gerçekleştirilmiştir. Elde edilen veriler istatistiksel olarak analiz edilmiştir. En düşük bağlanma dayanıklılık değerini RV-D grubu (5.42±6.6 MPa) göstermiştir. RV-D grubu ile V II-D (13.78±8.8 MPa) ve VV-D (13.84±6.2 MPa) grupları arasında istatistiksel olarak anlamlı bir farklılık yoktur (p>0.05). En yüksek bağlanma dayanıklılık değerini VV-M grubu (24.76±8.8 MPa) göstermiştir. VV-M grubu; RV-D, VV-D ve V II-D gruplarından istatistiksel olarak anlamlı derecede farklıdır (p

Özet (Çeviri)

The aim of this in vitro study was to evaluate shear bond strength of porcelain laminate veneers to three different surfaces by means of enamel, dentin and enamel-dentin complex using three different resin cements. Onehundredthirtyfive extracted, noncarious human maxillary central incisor teeth were used and the teeth were randomly divided into 9 groups (n=15). The teeth were embedded in acrylic molds and prepared with three different levels for bonding surfaces of enamel (E), dentin (D) and enamel-dentin complex (E-D). Porcelain discs (IPS e.max Press/Ivoclar Vivadent) of 2 mm in thickness and 4 mm in diameter were prepared according to the manufacturer?s instructions. Porcelain discs were luted to the tooth surfaces by using two light-cured [RelyX Veneer (RV); Variolink Veneer (VV)] and a dual-cured [Variolink II (V II)] resin cements according to the manufacturers? instructions. All the samples were thermal cycled for 5000 cycles. Shear bond strength test was performed in a universal testing machine (MCE 2000ST, Quicktest Prüfpartner GmbH) at 0.5 mm/min until bonding failure. The datas were statistically analyzed. Group RV-D exhibited the lowest bond strength value (5.42±6.6 MPa). There was statistically no difference between RV-D, V II-D (13.78±8.8 MPa) and VV-D (13.84±6.2 MPa) groups (p>0.05). Group VV-M exhibited the highest bond strength value (24.76±8.8 MPa). Group VV-M was statistically different from the groups RV-D, VV-D and V II-D (p

Benzer Tezler

  1. Farklı tekniklerle hazırlanmış porselen laminate veneer kronların ve yapıştırma sistemlerinin fiziksel olarak değerlendirilmesi

    A Physical evaluation of porcelain laminate veneer crowns and their bonding systems prepared with various techniques

    MEHMET ALİ KILIÇARSLAN

    Doktora

    Türkçe

    Türkçe

    1997

    Diş HekimliğiAnkara Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. ALİ ZAİMOĞLU

  2. Laminate veneerlerde kompozit reçinelerin kenar sızıntısının incelenmesi

    Evaluation of microleakage of composite resin bonded veneers

    AKKUŞ GONCAGÜL

    Yüksek Lisans

    Türkçe

    Türkçe

    2005

    Diş Hekimliğiİstanbul Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF.DR. HALUK KESKİN

  3. Farklı tam seramik sistemleri ile üretilen ve farklı rezin simanlarla yapıştırılan laminate veneer restorasyonların mineye bağlanma direncinin karşılaştırılmalı olarak incelenmesi

    Comparison of bond strengths of different porcelain laminate veneer materials luted on enamel surfaces with different resin cements

    ÖZGÜR ÖZTÜRK

    Doktora

    Türkçe

    Türkçe

    2012

    Diş HekimliğiGATA

    Diş Hekimliği Bölümü

    DOÇ. DR. O. CUMHUR SİPAHİ

  4. Porselen lamina venerler ile kompozit resin arasındaki tutunmada hidroflorik asit solüsyonu, silan bağlantı ajanı ve tükürüğün etkisi

    Başlık çevirisi yok

    NURCAN UYGUN (DURMAZ)

    Doktora

    Türkçe

    Türkçe

    1993

    Diş Hekimliğiİstanbul Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF.DR. ERMAN BÜLENT TUNCER

  5. Farklı sertleşme mekanizmasına sahip yapıştırma simanlarının porselen lamina venerlerin klinik performansına etkisi

    Effect of luting agents different polymerization mechanisms on the clinical performance of porcelain laminate veneers

    BİLAL YAŞA

    Doktora

    Türkçe

    Türkçe

    2011

    Diş HekimliğiEge Üniversitesi

    Diş Hastalıkları ve Tedavisi Ana Bilim Dalı

    PROF. DR. MURAT TÜRKÜN