Farklı yüzey işlemlerinin rezin simanların seramik materyaline olan bağlantı dayanımı üzerine etkisinin incelenmesi

Evaluation of the effect of different surface treatments on bond strength of the resin cements to the ceramic material

  1. Tez No: 293565
  2. Yazar: NURAN NOYAN ÖZYÖNEY
  3. Danışmanlar: PROF. DR. DİLEK TAĞTEKİN
  4. Tez Türü: Doktora
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2011
  8. Dil: Türkçe
  9. Üniversite: Marmara Üniversitesi
  10. Enstitü: Sağlık Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Diş Hastalıkları ve Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 159

Özet

Farklı Yüzey İşlemlerinin Rezin Simanların Seramik Materyaline Olan Bağlantı Dayanımı Üzerine Etkisinin İncelenmesiBu çalışmanın amacı, dört farklı yüzey işleminin rezin simanların IPS e.max ve IPS e.max CAD seramik materyaline olan bağlantı dayanımı üzerine etkisinin incelenmesidir. Çalışmada toplamda 240 adet olmak üzere, 2 farklı seramik numunesi (IPS e.max ve IPS e.max CAD) kullanıldı. Tüm seramik numuneleri yüzey işlemlerine göre (yüzey işlemi uygulanmayan, HF uygulanan, lazer uygulanan ve cojet uygulanan) 4 alt gruba ayrıldı. Yüzey pürüzlendirme işlemlerine göre 4 gruba ayrılan IPS e.max ve IPS e.max CAD seramik numuneleri, simantasyon için kullanılacak farklı rezin simanlara (Maxcem Elite, Biscem ve Bifix SE) göre 3 alt gruba ayrıldı. Tüm numunelere simantasyon işlemi öncesi Prosil silan (FGM, Joinville, SC, Brazil) uygulanarak, 60 saniye süre ile oda ısısında kurumaya bırakıldı. Seramik numunelerin rezin simanlar ile simantasyonu her bir rezin simanın kendine özgü üretici firma talimatlarına uyularak gerçekleştirildi. Simantasyon işlemini takiben, tüm örneklere 5±2 C°- 55±2 C° arasında, 30 saniyelik daldırma süresi ve kaplar arasında transfer zamanı 3 saniye olacak şekilde 10000 defa ısısal çevrim işlemi uygulandı. Kopma gerçekleşene kadar 0.5 mm/dk hızında Zwick Z010 (Zwick GmbH, Ulm, Germany) universal test cihazı kullanılarak, makaslama bağlanma kuvveti değerleri ölçüldü. Makaslama testi sonrası adeziv, koheziv ve miks kopma gösteren yüzeylerin analizi için Stereomikroskop kullanıldı. Makaslama bağlanma kuvveti değerleri arasındaki istatistiksel farklılıkların değerlendirilmesi için, Oneway Anova testi, Tukey HDS testi ve Student t test kullanıldı. Yüzey işlemlerine göre, en yüksek bağlanma kuvveti değerleri HF asit ile pürüzlendirilen gruplardan, en düşük bağlanma kuvveti değerleri yüzey işlemi uygulanmayan gruplardan elde edildi. Tüm gruplar arasında en yüksek makaslama bağlanma kuvveti değerleri HF asit ile pürüzlendirilip Maxcem Elite rezin siman ile yapıştırılan gruplardan elde edildi. Makaslama testi sonrasında elde edilen kopma yüzeylerinin stereomikroskop altında incelenmesi sonucu en fazla Tip I kopma (adeziv kopma), en az Tip II kopma (koheziv kopma) görüldü.

Özet (Çeviri)

Evaluation of the Effect of Different Surface Treatments on Bond Strength of the Resin Cements to the Ceramic MaterialThe aim of this study was to determine the effect of four different surface treatments on bond strength of resin cements to IPS e.max and IPS e.max CAD ceramic materials. Two different ceramics (IPS e.max and IPS e.max CAD) were used for each test group yielding a total number of 240 specimens. According to surface treatments (no treatment, HF acid treatment, laser treatment, Cojet treatment); all ceramic specimens were divided into 4 groups. IPS e.max and IPS e.max CAD ceramics which were divided into 4 groups according to surface treatments, were divided into 3 subgroups according to different resin cements (Maxcem Elite, Biscem ve Bifix SE) used for cementation. Before cementation procedure, Prosil silane (FGM, Joinville, SC, Brazil) was applied to all specimens and dried for 60 sec. at room temperature. Cementation with resin cements performed following its own manufacturer?s instructions. Following the cementation procedure, all specimens subjected to 10000 cycles of thermocycling at 5±2 C°- 55±2 C° (dwelling time: 30 sec, transfer time: 3 sec). Bond strength was measured by means of a shear test, using Zwick Z010 (Zwick GmbH, Ulm, Germany) universal testing machine with 0.5 mm/min. speed until failure. A stereo microscope was used to analyse the surfaces for adhesive, cohesive and mixed failure percentages. To determine the statistical significance of the differences between the mean shear bond strength values, Oneway Anova, Tukey HDS and Student t test were used. According to surface treatments, while the highest bond strength was obtained from the groups treated with HF acid, the lowest bond strength was obtained from the groups without surface treatment. Between all groups, the highest bond strength was obtained with the groups treated with HF acid and luted with Maxcem Elite self adhesive resin cement. After shear bond strength test, under the Stereomicroscope the most prevalent type of failure was seen as Type I (adhesive failure) and the least prevalent type of failure was seen as Type II (cohesive failure).

Benzer Tezler

  1. Zirkonya seramik ve zirkonya ile güçlendirilmiş lityum disilikat cam seramiklere uygulanan farklı yüzey işlemlerinin, rezin simanların bağlanma dayanımı üzerine etkisi

    The effect of different surface treatments applied to zirconia ceramic and zirconia reinforced lithium dissilicate glass ceramics on the bonding strength of resin cements

    ÖZGE GÜRGENLİ

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2023

    Diş HekimliğiSivas Cumhuriyet Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. HAKAN DEMİR

  2. Farklı yüzey işlemlerinin zirkonya ile rezin siman arasındaki bağlantı kuvveti üzerine etkisi

    The effect of different surface treatments on the bond strength between zirconia and resin luting cement

    GÖKHAN ÇİÇEKCİ

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2020

    Diş HekimliğiAnkara Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. LALE KARAAĞAÇLIOĞLU

  3. Parçalı lamina venerlerde yorulma sonrası renk stabilitesinin değerlendirilmesi

    Evaluation of color stability of sectional laminate veneers after aging procedures

    BAHAR ELTER

    Doktora

    Türkçe

    Türkçe

    2015

    Diş HekimliğiEge Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. ATİLLA İSMAİL KESERCİOĞLU

  4. Farklı yüzey işlemleri uygulanan zirkonya seramik ile adeziv reçine siman bağlantısının in vitro olarak değerlendirilmesi

    Effect of different surface treatment methods on bond strength of zirconia and resin cement

    MERVE SONGÜL GÜDÜK

    Doktora

    Türkçe

    Türkçe

    2014

    Diş Hekimliğiİstanbul Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. BEGÜM AKKAYAN KESMEZACAR

  5. Fiber lazer sistemi ve farklı yüzey pürüzlendirme yöntemleri uygulanarak yüzeyi pürüzlendirilen zirkonya materyali ile dentin arasındaki bağlantı kuvvetinin in-vitro olarak değerlendirilmesi

    The evaluating in-vitro bond strength of zirconia surface that was roughed with fiber laser and different surface treatments techniques to dentin

    SERVER ÜNAL

    Doktora

    Türkçe

    Türkçe

    2013

    Diş HekimliğiDicle Üniversitesi

    Diş Hekimliği Bölümü

    PROF. DR. REMZİ NİĞİZ