Influence of different thickness on the flexural strength of zirconia ceramics
Influence of different thickness on the flexural strength of zirconia ceramics
- Tez No: 298710
- Danışmanlar: PROF. DR. ENDER KAZAZOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental materyaller, Dental porselen, Dental restorasyon, Diş hastalıkları, Zirkonyum, Zirkonyum oksit, Dental materials, Dental porcelain, Dental restoration, Tooth diseases, Zirconium, Zirconium oxide
- Yıl: 2011
- Dil: İngilizce
- Üniversite: Yeditepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Özet yok.
Özet (Çeviri)
The aim of this project was to evaluate and compare the different thickness of zirkonzahn ceramics and its mechanical properties of ceramics, which have generated interest in restorative dentistry because of their high strength and high resistance to fracture.Three different thickness and 10 samples of zirkonzahn ceramic were selected for this study (15x0.3mm), (15x0.5mm), (15 x0.7mm) Three control discs of the green stage Zirconia block were cut with saw (leitz 1600) and sintered in zirkonzahn sintering oven start at 20- 1500 ?C. All discs were polished with diamond paste. The cycle of all processes take 8 hrs and this procedure were provided by (zirkonzahn Furnace). The surface of the Zirconia specimens were ground with 600, 800, 1200 (Silver carbide abrasives) under water cooling and then with 120 ?m Al2O3 particles are blasted to 0.5 MPa pressure from a distance of 10 mm, 15 seconds.The evaluation data were performed by NCSS (Number Crunchers statistical system) 2007&PASS 2008 Statistical Software (Utah, USA) program. The evaluation of operating data, comparisons between groups one-way analysis of variance (one way ANOVA) test and Tukey HDS test was used for the determination of the group that lead to differences. Pearson correlation analysis was used for assessing the relationships between parameters p <0.05 level were evaluated.The mean biaxial flexural strengths of ten discs are presented in all groups. The highest mean biaxial flexural strength found at 0.7mm than at 0.5 mm and lowest value was found at 0.3mm. A cording to our results; increasing the core thickness of Zirconia from 0.3 to 0.5mm flexural strength was increased 7%. But core thickness did not differ between 0.5mm and 0.7mm, Which revealed no significant difference between the fracture strength values of the test groups (P>.05).In this study the Increasing the core thickness from 0.3 to 0.5 has shown 7% increase at the flexural strength and the Increasing the core thickness from 0.5 to 0.7 mm has shown no differences at the flexural strength. Result of this in-vitro study shows that increasing the thickness of zirconia from 0.3 mm to 0.5 or 0.7 mm it does not appear to be significant effect on flexural strength.
Benzer Tezler
- Farklı yaşlandırma yöntemlerinin monolitik zirkonyanın mekanik dayanımına ve faz dönüşümüne etkisi
The effect of different aging methods on the mechanical strength and phase transformation of monolithic zirconia
HALİTCAN YÜKSEL
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. İSA YÖNDEM
- İki farklı multilayer zirkonyum oksit restorasyon materyalinin fiziksel ve mekanik özelliklerinin karşılaştırılması
A comparative study on the physical and mechanical properties of two different multilayer zirconia based dental restorative materials
FURKAN ÇETİNTÜRK
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiSüleyman Demirel ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. HAKKI CENKER KÜÇÜKEŞMEN
- Yüksek translusent zirkonya blokların boyama ve cila işlemleri sonrası optik, mekanik, fiziksel ve mikroyapısal açıdan incelenmesi
Evaluation of optic, mechanical, physical and microstructural properties of high-translucent zirconia blocks after staining and polishing procedures
BESTE BURCU UZ
Doktora
Türkçe
2025
Diş HekimliğiSağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. BİKE ALTAN ÇINAR
- Yüzey uygulamaları ve yapay yaşlandırma işleminin Y-TZP dental seramiklerinin biaksiyel bükme dayanımı ve faz değişimi üzerine etkilerinin in-vitro olarak incelenmesi
Influence of surface treatments and accelerated aging on flexural strength and phase transformation of bilayered Y-TZP ceramics
EVRİM ÖZER BULTAN
Doktora
Türkçe
2013
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. DENİZ ŞEN
- Silisyum kaplamasının farklı titanyum seramiklerinde titanyum seramik bağına etkisi
Effect of silicon coating on titanium-ceramic bonding of different titanium ceramics
IŞIL ÖZCAN
Doktora
Türkçe
2003
Diş HekimliğiÇukurova ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. HAKAN UYSAL