Analysis of magnesium addition, hydrogen porosity and T6 heat treatment effects on mechanical and microstructural properties of pressure die cast 7075 aluminum alloy

Basınçlı döküm yöntemiyle üretilmiş 7075 alüminyum alaşımının mekanik ve mikroyapısal özelliklerine magnezyum artışının, hidrojen porozitesinin ve T6 ısıl işleminin etkilerinin analizi

  1. Tez No: 318826
  2. Yazar: ECE ALAT
  3. Danışmanlar: PROF. DR. ALİ KALKANLI
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2012
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 125

Özet

Alüminyum alaşımları, düşük yoğunluğun yanı sıra sahip olduğu işlenebilirlik gibi özellikleri nedeniyle büyük önem arz eder. 7075 alüminyum alaşımı Al-Zn-Mg-Cu grubunda yer alan bir dövme alaşımıdır. Bu elementlerin alaşıma katılmış olmaları, 7075 alüminyum alaşımına diğer tüm alüminyum alaşımlarından daha yüksek mukavemet ve etkin bir çökelti sertleştirilebilme özelliği kazandırmıştır.Öte yandan, alüminyum alaşımlarının uygulamalarda yaygın olarak kullanılmasına engel teşkil eden bazı hususlar mevcuttur. Alüminyum alaşımlarında en sık karşılaşılan problemlerden bir tanesi, hidrojen poroziteleridir. Buna ek olarak, 7075 alaşımındaki bir durum da yeterinde akışkan olmamaktır. Magnezyum artışının bu eksikliği telafi edeceği düşünülmektedir. Buna göre, bu çalışmada, hidrojen porozitesi ve fazladan magnzeyum içeren basınçlı kalıp döküm yöntemi ile üretilmiş, 7075 alüminyum alaşım numuneleri incelenmiştir. Amacımız, hidrojen miktarı ile hidrojen porozitesi arasındaki ilişkiyi ve hidrojen porozitesi, magnezyum artışı ve T6 ısıl işlem uygulamasının basınçlı kalıp döküm yöntemi ile üretilmiş 7075 alüminyum alaşımının çekme ve bükülme dayancı özellikleri üzerine etkilerini belirlemektir.7075 alüminyum alaşım hurdaları bir basınçlı döküm firmasından temin edilmiştir. Gerekli spektral incelemelein ardından, basınçlı döküm prosesi iki aşamada gerçekleştirilmiştir. Birinci aşamada, magnezyum konsantrasyonu artırılmış 7075 alüminyum alaşımı dökülmüştür, ikinci aşamada ise herhangi bir alaşım değişikliği yapılmamış 7075 alaşımının dökümü gerçekleştirilmiştir. Bu dökümler yapılırken, her bir döküm öncesi hidrojen miktarı ölçümü gerçekleştirilmiştir. Son bir operasyon olarak da belli numunelere T6 ısıl işlemi uygulanmıştır.

Özet (Çeviri)

Aluminum alloys are having more attention due to their high specific stiffness and processing advantages. 7075 aluminum alloy is a wrought composition aluminum alloy in the Al-Zn-Mg-Cu series. Due to the significant addition of these alloying elements, 7075 has higher strength compared to all other aluminum alloys and effective precipitation hardenability characteristic.On the other hand, aluminum alloys have some drawbacks, which hinder the widespread application of them. One of the most commonly encountered defects in aluminum alloys is the hydrogen porosity. Additionally, in case of 7075, another problem is the lack of fluidity. Magnesium addition is thought to be effective in compensating this deficiency. Accordingly, in this study, die cast 7075 aluminum alloy samples with hydrogen porosity and additional magnesium content were investigated. Our aim was to determine the relationship between hydrogen content and hydrogen porosity, and the effects of hydrogen porosity, additional magnesium and T6 heat treatment on ultimate tensile and flexural strength properties of pressure die cast 7075 aluminum alloy.7075 aluminum alloy returns were supplied from a local pressure die casting company. After spectral analysis, pressure die casting was conducted at two stages. In the first stage, 7075 aluminum alloy with an increase in magnesium concentration was melted and secondly 7075 aluminum alloy was cast directly without any alloying addition. While making those castings, hydrogen content was measured continuously before each casting operation. As a final operation T6 heat treatment is carried out for certain samples. Finally, in order to accomplish our aim, mechanical and microstructural examination tests were conducted.

Benzer Tezler

  1. Quantitative analysis of carbon nanotube suspensions, synthesis of inorganic nanostructured materials and their characterization

    Karbon nanotüp süspansıyonlarının kantitatif analizi, inorganik nanoyapılı malzemelerin üretimi ve karakterizasyonu

    ALİ CAN ZAMAN

    Doktora

    İngilizce

    İngilizce

    2015

    KimyaYıldız Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. CENGİZ KAYA

    PROF. DR. FİGEN KAYA

  2. 5754 alüminyum alaşımının kaynak davranışının incelenmesi

    The analysis of 5754 aluminum alloy?s welding behaviour

    SAVAŞ AKINCI

    Yüksek Lisans

    Türkçe

    Türkçe

    2008

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. YILMAZ TAPTIK

  3. Bakır-bor alaşımlarının üretimi ve ısıl sistemi

    Production and heat treatment of copper-boron microalloys

    TUNCAY YETER

    Yüksek Lisans

    Türkçe

    Türkçe

    1994

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    PROF.DR. ADNAN TEKİN

  4. Güneş enerjisi destekli termokimyasal ve hibrit çevrimlerde hidrojen üretiminin enerji, ekserji ve eksergoekonomik analizi

    Energy, exergy and exergoeconomic analyses of hydrogen production in solar based thermochemical and hybrid cycles

    FATİH YILMAZ

    Doktora

    Türkçe

    Türkçe

    2017

    EnerjiSüleyman Demirel Üniversitesi

    Enerji Sistemleri Mühendisliği Ana Bilim Dalı

    PROF. DR. REŞAT SELBAŞ

  5. Synthesis, characterization, functionalization and tunable catalytic properties of bimetallic metal organic frameworks for glycerol oxidation

    Gliserol oksidasyonu için bimetalik metal organik ağ yapıların sentezlenmesi, karakterizasyonu, katalik özelliklerinin modifikasyonu ve işlevsellendirilmesi

    HÜLYA AÇAR KILIÇ

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Kimya MühendisliğiEge Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    DOÇ. DR. EMİNE SERT