Al-Si alaşımına eser miktarda ilave edilen elementlerin sıma prosesine etkisi
The influence of trace amounts of elements additions to Al-Si alloys of SIMA processing
- Tez No: 337085
- Danışmanlar: DOÇ. DR. NURŞEN SAKLAKOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: SIMA prosesi, ETIAL180 alaşımı, Al-Si alaşımları, XRD, SEM, SIMA process, ETIAL 180 alloy, Al-Si alloys, XRD, SEM
- Yıl: 2013
- Dil: Türkçe
- Üniversite: Celal Bayar Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Ana Bilim Dalı
- Bilim Dalı: Konstrüksiyon ve İmalat Bilim Dalı
- Sayfa Sayısı: 87
Özet
Bilindiği üzere yarı katı şekillendirmede dendritik tane yapısı akışkanlığa büyük direnç oluşturduğundan bu tür şekillendirmelerde küresel tane yapısının önemi büyüktür. Tane yapısının dendritik yapıdan küresel yapıya dönüştürme işlemlerinden bir tanesi de deformasyon ve yeniden kristalleşme metodu olarak bilinen SIMA (Stres Induced Melt Activated) prosesidir. Bu çalışmada alüminyum ve alaşımlarının özellikleri hakkında bilgiler verildi. ETIAL 180 alaşımı ve SIMA prosesi tanıtıldı. Bu alaşıma eser miktarda Mg ve SN ilave edilerek gravite döküm yöntemiyle numuneler elde edildi. Numunelerin mikroyapıları ve sertlikleri incelendikten sonra aynı numuneler SIMA prosesine tabi tutularak mikroyapı ve sertlik değerleri incelenip değerlendirildi. Numunelerin SEM ve XRD analizleri yapıldı ve karşılaştırıldı. ETIAL 180 alüminyum alaşımına ilave edilen eser miktarlardaki Mg ve Sn elementlerinin SIMA yönteminde küresellik ve tane boyutunda bir farklılığa yol açmadı görülmüştür. SIMA yöntemiyle kırılan dendritik yapının küreselliği mükemmelle yakın olduğu görülmüştür. Sn ilavesiyle sertlik değerlerinde önemli bir değişme görülmemiş olup Mg ilavesiyle sertlik değerlerinde %20?ye yakın bir artış tespit edilmiştir. SIMA prosesi sonucunda yarı katı şekillendirme yapılmadığı için SIMA prosesli numunelerin sertlik değerlerinde azalma görülmüştür. Sn ve Mg ilavesinin Çin yazısı şeklindeki intermetaliklerin oluşumunu tetiklediği ve Mg ilavesi ile Mg2Si bileşiğinin oluştuğu tespit edilmiştr. SIMA yöntemi ile de bu Çin yazısı intermetaliklerin kabalaştığı, çatladığı ve kırılarak matriks yapıya dağıldığı tespit edilmiştir.
Özet (Çeviri)
As it known, since dendritic grain structure is generates a great resistance for solid forming, spherical grain structure has a great importance for in this type forming. One of the procedures of transforming the grain structure from dendritic form to spherical form is SIMA (Stress Induced Melt Activated) process which is also known as recrystallization method. In this study, information about the characteristics of aluminum and its alloys were presented. The ETIAL 180 alloy and SIMA process was introduced. By adding trace amount of Mg and SN via gravity casting method, samples were obtained. After examining the microstructures and hardness of the samples, the microstructure and hardness values of these samples were analyzed by subjecting them to SIMA process. The SEM and WRD analyzes of the samples were performed and the results were compared. It was observed that the Mg and SN elements trace amount of which were added to ETIAL 180 aluminum alloy has no effect on sphericity and grain size with SIMA method. It was observed that the sphericity of the dendritic structure which was cracked by using the SIMA method was close to perfection. It was detected that the addition of Mg element had increased the hardness value by 20% while addition of Sn element had no significant effect on hardness value. Since semi-solid forming was not performed following the SIMA process, a decrease was observed in the hardness value of SIMA processed samples. It was observed that the insertion of Mg and Sn elements trigged the formation of the Chinese script shaped intermetallic, and formation of Mg2Si compound occurred with addition of Mg element. It was observes that these Chinese script shaped intermetallic coarsened, cracked and split to matrix structures by breaking with use of SIMA method.
Benzer Tezler
- Protein-enerji malnurisyonunda hematolojik parametrelerdeki değişiklikler
Changes of hematological parameters in protein-energy malnutrition
MURAT ÖZKALE
Tıpta Uzmanlık
Türkçe
2003
HematolojiSağlık BakanlığıÇocuk Sağlığı ve Hastalıkları Ana Bilim Dalı
DOÇ. DR. TANSU SİPAHİ
- Alüminyum silisyum alaşımlarında bor ile tane inceltme
Grain refinement of aluminium silicon alloys with boron
UĞUR AYBARS ESER
Yüksek Lisans
Türkçe
2019
Metalurji MühendisliğiYıldız Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. MUSTAFA ÇİĞDEM
- Al-Si alaşımının mekanik özelliklerine magnezyum elementinin etkileri
The effects of the magnesium element on the mechanical properties of the Al-Si alloy
HALİL EREN
Yüksek Lisans
Türkçe
2017
Metalurji MühendisliğiKarabük ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ALİ GÜNGÖR
- Ötektik alüminyum-silisyum alaşımının mikroyapı ve mekanik özelliklerine titanyum-bor ilavesinin etkisi
The effect of titanium-boron addition on microstructure and mechanical properti̇es of aluminum-silicon alloy
ALMİLA BAHADIR
Yüksek Lisans
Türkçe
2021
Metalurji MühendisliğiKarabük ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ALİ GÜNGÖR
- Yaşlanabilir alüminyum alaşımlarının aşınma davranışları
Başlık çevirisi yok
YAVUZ SUN
Yüksek Lisans
Türkçe
1998
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU