Bor katkılı portland çimentosu ile üretilen betonların mühendislik özellikleri ve yüksek sıcaklık etkisi

The engineering properties and high temperature effects of concrete produced with portland cement boron mixtured

  1. Tez No: 353465
  2. Yazar: HAVVA ECE PEHLİVANOĞLU
  3. Danışmanlar: DOÇ. DR. ŞEMSETTİN KILINÇARSLAN, DOÇ. DR. METİN DAVRAZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: İnşaat Mühendisliği, Civil Engineering
  6. Anahtar Kelimeler: Borik asit [B(OH)3], çimento hidratasyonu, mekanik özellikler, nötron soğurma kapasitesi, priz süresi, yüksek sıcaklık, Boric acid [B(OH)3], cement hydration, the high temperatures, the mechanical properties, the neutron absorption capacity, the setting time
  7. Yıl: 2014
  8. Dil: Türkçe
  9. Üniversite: Süleyman Demirel Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Yapı Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 183

Özet

Bu tez çalışmasında, B2O3 kaynağı olarak kullanılan B[OH]3 ile birlikte priz hızlandırıcı ve harç gözenek suyunun alkanitesini artırıcı kimyasal katkı maddeleri kullanımının çimento hidratasyonuna, priz süresine ve mekanik dayanımına etkisi araştırılmıştır. Elde edilen bulgular neticesinde en yüksek %B2O3 oranında ve bu oran için en uygun kimyasal katkı maddesi ile beton üretilmiştir. Üretilen bu beton haricinde biri Borlu Aktif Belit (BAB) çimentosu diğeri Portland CEM I çimentosu kullanılarak iki ayrı kontrol betonu da üretilmiştir. Üretilen üç ayrı tip beton üzerinde çeşitli taze ve sertleşmiş beton deneyleri uygulanarak elde edilen veriler birbirleriyle karşılaştırılmıştır. Sonuç olarak bor bileşiklerinin çimento hidratasyonu kontrolü amacıyla katkı maddesi olarak kullanılabileceği, hidratasyon reaksiyonundaki gecikmenin sodyum alüminat katkısı kullanımı ile denetlenebileceği belirlenmiştir. Ancak BAB betonu örneklerinin kontrol örneklerine göre daha fazla nötron soğurma kapasitesi sergilerken, BSA betonu örneklerinden beklenen yarar sağlanamamıştır. Bu durum, BSA betonunun ağırlıkça B2O3/c oranının BAB betonuna göre yaklaşık 3 kat daha düşük olmasına bağlanmıştır. Ayrıca elde edilen sonuçlar doğrultusunda, bor katkısının betonun yüksek sıcaklıklar altındaki dayanımına olumlu bir etkisi olmadığı belirlenmiştir.

Özet (Çeviri)

In this thesis, the using of B[OH]3 as source of B2O3 and the using of chemical additives as the setting accelerator and the alkalinity increaser of the mortar pore water to the cement hydration, for setting time and mechanical strength were investigated. As a result of the findings, the concrete was produced by the appropriate chemical additives for the highest ratio % B2O3. Also two different types (control) concrete was produced by using boron modified active belite cement (BAB) and portland cement as binding material. On produced concretes as three different types, various fresh and hardened concrete experiments were performed and the data obtained were compared with each other. As a result, boron compounds may be used as additives to control hydration of cement, the delay of the hydration reactions can be controlled by use of sodium aluminate contribution was determined. However concrete samples of BAB were showed more neutron absorption capacity than the control samples, the expected benefits from concrete samples of BSA has not been provided. This stuation was thought to be due to that BSA concrete has approximately 3 times lower B2O3 / cement ratio by weight compared to BAB concrete. Also according to the results obtained was determined that there is not a positive effect of boron additives in concrete strength under the high temperatures.

Benzer Tezler

  1. Mechanical properties of boron blended cement concretes

    Bor katkılı çimentolarla üretilen betonların mekanik özellikleri

    ALİ ŞEREF CENGİZ

    Yüksek Lisans

    İngilizce

    İngilizce

    2011

    İnşaat MühendisliğiGaziantep Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MEHMET GESOĞLU

  2. Bor katkılı çimentoların özelliklerinin incelenmesi

    Examination of the properties of boron blended cements

    CAN DURMUŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    İnşaat MühendisliğiDokuz Eylül Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. SELÇUK TÜRKEL

  3. Üçüncü bileşen şartlarında bor atık katkılı çimentonun özelliklerinin incelenmesi

    Investigating the properties of cement with boron wastes under the circumstance of third components

    MUSTAFA ERSİN AKBULUT

    Yüksek Lisans

    Türkçe

    Türkçe

    2009

    Seramik MühendisliğiAfyon Kocatepe Üniversitesi

    Seramik Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. TANER KAVAS

  4. Boraks ve borik asit üretiminde ortaya çıkan katı atıkların çimento sanayiinde değerlendirilmesi

    Evaluation of solid wastes that are formed during the borax and boric acid production in cement industry

    İFFET YAKAR ELBEYLİ

    Yüksek Lisans

    Türkçe

    Türkçe

    2000

    Kimya MühendisliğiYıldız Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. SABRİYE PİŞKİN

  5. Bor endüstrisi atıklarının değerlendirilmesi

    Başlık çevirisi yok

    RECEP BONCUKCUOĞLU

    Doktora

    Türkçe

    Türkçe

    1993

    Kimya MühendisliğiAtatürk Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. M. MUHTAR KOCAKERİM