Yapay dişler ile akrilik reçinelerin bağlanma dayanımına yüzey uygulamaları ve termosiklusun etkilerinin mikro gerilim test yöntemiyle incelenmesi
Microtensile bond strength of acrylic teeth to denture base resi̇ns: Effect of surface treatments and thermocycli̇ng
- Tez No: 361500
- Danışmanlar: PROF. DR. FATMA ÜNALAN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Akrilik reçineler, mikro gerilim bağlanma dayanımı, yapay dişler, termosiklus, yüzey uygulamaları, Dental bonding, Dental materyaller, Dental restorasyon, Dental stres analizi, Takma dişler, Acrylic resins, microtensile bond strength, denture teeth, thermocycling, surface treatment, Dental bonding, Dental materials, Dental restoration, Dental stress analysis, Dentures
- Yıl: 2014
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Yapay dişler ile protez kaidesinin bağlanması hareketli bölümlü ve tam protezlerin bütünlüğü için zorunludur. Akrilik yapay dişler ve protez kaide materyalinin bağlanmalarındaki başarısızlık önemli problem teşkil etmektedir. Bu çalışmanın amacı akrilik reçine tipinin, yapay dişin krete bakan yüzeyine yapılan uygulamaların ve termosiklusun, akrilik dişler ile protez kaidesi arasındaki mikro gerilim bağlanma dayanımına etkisini incelemektir. Yüksek çapraz bağlantılı 108 adet akrilik yapay dişin krete bakan yüzeyleri düzleştirildi ve yüzey uygulaması için kimyasallarla (aseton, bonding ajan, monomer, diklorometan, mum uçurucu) ıslatıldı. Isı ile, ışık ile ve kimyasal olarak polimerize olan reçineler üretici firma talimatları doğrultusunda hazırlandı ve yapay dişlerle birlikte polimerizasyonları sağlandı. Tüm örnekler kesilerek 1mm2lik çubuklar haline getirildi. Her gruptaki çubuk haline getirilmiş örneklerin yarısı 5 0C- 55 0C ve 10.000 devir termosiklusa maruz bırakıldı. Örneklere mikro gerilim bağlanma dayanımı cihazında 1mm/dk hızda kopma gerçekleşinceye kadar kuvvet uygulandı. Kopma anında okunan değerler MPa cinsinden hesaplandı. Verilerin istatistiksel analizi için Kruskal Wallis testi ve farklılığa neden olan grubun tespitinde Mann Whitney U testi kullanıldı sonuçlar % 95 güven aralığında değerlendirildi (p<0.05). Akrilik reçineler arasında, akrilik yapay dişler ile mikro gerilim bağlanma dayanımı bakımından anlamlı farklılık gözlendi. En yüksek bağlanma dayanımı akrilik reçinelerden ısı ile polimerize olan örneklerde, en düşük ise kimyasal olarak polimerize olan örneklerde saptandı. Aseton uygulamasının ışık ile ve kimyasal olarak polimerize olan örneklerde, bonding ajan uygulamasının ise ısı ile polimerize olan örneklerde en yüksek bağlanma dayanımını sağladığı saptandı. Termosiklus uygulamasının ısı ile ışık ile ve kimyasal olarak polimerize olan örneklerin bağlanma dayanımında anlamlı fark yaratmadığı gözlendi.
Özet (Çeviri)
The connection between artificial teeth and denture base is essential for the integrity of dentures. Failure of the bond between acrylic resin teeth and denture base material remains a considerable problem. This study evaluated the effect of acrylic resin type (heat-polymerized, light-polymerized and autopolymerized), ridge lap surface treatment and thermocycling on the microtensile bond strength of acrylic teeth. The ridge laps of 108 identical highly cross-linked acrylic teeth (Integral) were ground and pre-treated using different conditioning liquids (acetone, bonding agent, monomer, dichloromethane, wax solvent). Heat- polymerized (Paladent20), light- polymerized (Eclipse) and autopolymerized (PaladentRR) resins were prepared as recommended by the manufacturer and applied on the acrylic denture teeth. Each tooth-acrylic resin set was serially sectioned to obtain rectangular bar specimens with mean cross-sectional area of 1mm2. Half of the bars in each group were thermocycled (10,000 cycles between 5oC and 55oC). The microtensile bond strength tests were performed in universal testing machine at 1 mm/min speed until failure. Statistical analyses performed with Kruskal Wallis and Mann Whitney U tests (p<0.05). There were significant differences in the bond strengths between acrylic resins to denture tooth. The highest bond strength values were obtained using the heat-polymerized denture base material, whereas the lowest values were found with the autopolymerized resin. Acetone application provided highest bond strengths in light- and autopolymerized groups. However, in heat-polymerized specimens, the highest bond strength achieved by bonding agent group. Thermocycling had no significant effect on the bond strength of denture teeth to heat-, light- and autopolymerized acrylic resins.
Benzer Tezler
- 3B yazıcı teknolojisi ile üretilen protezlerde kaide plağı ve yapay diş bağlantısının incelenmesi
Evaluation of the bond strength between the artificial teeth and denture base produced with the 3D printer
MERVE CANSIZOĞLU
Doktora
Türkçe
2024
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. HAYRUNNİSA CANAN BURAL ALAN
- Farklı içerik ve tasarımda üretilen post sistemlerinin itme dayanımlarının karşılaştırılması
Comparison of the push - out bond strength of postsystems produced in different content and design
AYŞE KARABAŞ
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş Hekimliğiİnönü ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. GÜLER YILDIRIM AVCU
DR. ÖĞR. ÜYESİ NUMAN TATAR
- Fiberle desteklenmiş bir kompozit rezinin farklı dentin nitelikleri ve preparasyon yöntemlerindeki bağlanma dayanımının geleneksel ve bulk-fill kompozitlerle karşılaştırılması
Bond strength comparison of a fiber reinforced composite resin with traditional and bulk-fill composite resins under different dentin conditions and preparation techniques
MERVE AĞACCIOĞLU
Diş Hekimliği Uzmanlık
Türkçe
2017
Diş HekimliğiGaziosmanpaşa ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. EMİNE ŞİRİN KARAARSLAN
- Cam fiber ile güçlendirilmiş akrilik resinlerin hareketli protezlerdeki yapay diş ve metal iskeletlere olan bağlantı kuvvetinin incelenmesi
An investigation of the bond strength of glass-fiber reinforced acrylic resin to artificial teeth and metal framework of the removable dentures
TUĞÇE BALOĞLU
Doktora
Türkçe
2010
Diş HekimliğiErciyes ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. BÜLENT KESİM
- Farklı protez temizleme solüsyonlarının farklı tekniklerle üretilen akrilik kaide materyalleri ile yapay dişlerin bağlantısına etkisi
The effect of different cleaning solutions on the bonding strength of artificial teeth with acrylic base produced with different techniques
ELİF ÇELİK
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiOrdu ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. DOĞU ÖMÜR DEDE